Deplating solution and deplating technology for removing glass NCVM film layer
A technology for stripping solution and glass, applied in the field of stripping solution and stripping process, can solve the problems affecting product appearance quality, product yield instability, photosensitive ink damage, etc., to achieve good appearance, guarantee gloss effect, product quality Yield stable effect
Active Publication Date: 2019-03-01
LENS TECH CHANGSHA
View PDF7 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Traditionally, a strong alkaline stripping solution is used to remove the NCVM film layer, but using this type of stripping solution for stripping is easy to cause damage to the photosensitive ink af
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Example Embodiment
[0117] Example 1
[0118] A deplating solution for removing glass NCVM film layer, which is composed of the following components by mass percentage: sodium carbonate 15%, potassium sodium tartrate 10%, penetrant JFC 3%, and the rest is water.
Example Embodiment
[0119] Example 2
[0120] A deplating solution for removing glass NCVM film layer, which is composed of the following components by mass percentage: sodium carbonate 25%, potassium sodium tartrate 5%, penetrant JFC 1%, and the rest is water.
Example Embodiment
[0121] Example 3
[0122] A deplating solution for removing glass NCVM film layer, which is composed of the following components by mass percentage: sodium carbonate 20%, potassium sodium tartrate 8%, penetrant JFC 2%, and the rest is water.
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more PUM
Login to view more Abstract
The invention discloses a deplating solution and a deplating technology for removing a glass NCVM film layer, and relates to the technical field of glass deplating. The deplating solution comprises the following components by mass percentage: 10-30% of soluble carbonate, 5-15% of a complexing agent, 1-5% of penetrant and the balance of water. In the deplating technology, the deplating solution isused for deplating the NCVM film layer of a glass product. By adopting the deplating solution and the deplating technology provided by the invention, the technical problems that a strong alkaline deplating solution used for the removal of the NCVM film layer easily causes damage to photosensitive ink after exposure and development and the product yield is low in a traditional technology are alleviated. The deplating solution provided by the invention mainly uses the soluble carbonate as a main deplating agent, and by cooperating with the complexing agent and the penetrant, not only can the NCVM film layer be cleanly removed with a good deplating effect, but also no damage is caused to the photosensitive ink after exposure and development, and the glass product after being deplated with thedeplating solution has a good appearance and a high yield.
Description
technical field [0001] The invention relates to the technical field of glass deplating, in particular to a deplating solution and a deplating process for stripping glass NCVM film layers. Background technique [0002] With the progress of society, 2D, 2.5D or 3D glass has been applied to various electronic products and has become a fashion. Compared with traditional plastic and metal mobile phone battery covers, 2D, 2.5D or 3D glass is thinner, transparent and clean , anti-fingerprint, anti-glare, scratch resistance and weather resistance. At present, the deplating process has been well used on glass as a new type of operation method. This process can not only obtain beautiful and precise patterns, but also the patterns have no concave-convex feeling and fine texture. [0003] NCVM (Non-Conductive Vacuum Metalize, vacuum non-conductive electroplating) is a non-conductive vacuum metallization coating process. NCVM uses special metals. This process not only makes the coated f...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more Application Information
Patent Timeline
Login to view more IPC IPC(8): C03C23/00
CPCC03C23/0075
Inventor 饶桥兵蔡杰勇
Owner LENS TECH CHANGSHA
Who we serve
- R&D Engineer
- R&D Manager
- IP Professional
Why Eureka
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Social media
Try Eureka
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap