Tungsten carbide hard face abrasion-resistant bearing and preparation method thereof

A wear-resistant bearing, tungsten carbide technology, applied in metal processing equipment, transportation and packaging, coating, etc., can solve the problems of wear failure, high friction coefficient, etc., to change the surface friction coefficient, control friction and wear performance, improve friction and wear performance effect

Inactive Publication Date: 2019-03-15
SEED TECH CORP LTD
View PDF11 Cites 6 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, the above-mentioned existing tungsten carbide hard-faced wear-resistant bearings have the following problems: the coefficient of friction is still high, resulting in severe wear and tear failure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Tungsten carbide hard face abrasion-resistant bearing and preparation method thereof
  • Tungsten carbide hard face abrasion-resistant bearing and preparation method thereof
  • Tungsten carbide hard face abrasion-resistant bearing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0036] The present application also provides a preparation method of the tungsten carbide hard-faced wear-resistant bearing, comprising the following steps:

[0037] Mix 20% to 55% of pure nickel powder or nickel-based alloy powder, 2.5% to 15% of self-lubricating component powder, and 30% to 77.5% of tungsten carbide particles according to volume percentage to obtain a mixed powder; the self-lubricating The component is a composite material of nickel-coated molybdenum disulfide or a composite material of nickel-coated graphite;

[0038] The mixed powder is molded on the cemented carbide to obtain a tungsten carbide hard surface wear-resistant bearing.

[0039] According to the present invention, pure nickel powder or nickel-based alloy powder, self-lubricating component powder and tungsten carbide particles are mixed according to the volume percentage; among the above-mentioned components, the particle size of self-lubricating component powder is 30-180 μm, and in specific im...

Embodiment 1

[0044] Ni-(4-20)Cr-(1-10)Si-( 0.5-5) B nickel-based alloy powder and spherical cast tungsten carbide with a particle diameter of 100-150 μm and a volume fraction of 40% are mixed to obtain a mixed powder. The above-mentioned mixed powder is surfacing welded on the cemented carbide through PTA to obtain a tungsten carbide hard-faced wear-resistant bearing. The hard-faced wear-resistant layer obtained by mixing the powder according to this ratio is defined as HF-01.

Embodiment 2

[0046] Ni-(4-20)Cr-(1-10)Si-( 0.5-5) B nickel-based alloy powder and spherical cast tungsten carbide with a particle diameter of 100-150 μm and a volume fraction of 40% are mixed to obtain a mixed powder. The above mixed powder is surfacing welded on the cemented carbide through PTA to obtain a tungsten carbide hard-faced wear-resistant bearing. The hard-faced wear-resistant layer obtained by mixing the powder according to this ratio is defined as HF-02.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
thicknessaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention provides a tungsten carbide hard face abrasion-resistant bearing. The tungsten carbide hard face abrasion-resistant bearing is composed of a hard alloy and a coating distributed on the periphery of the hard alloy; the coating is prepared from the following components, by volume percentage, 20%-55% of pure nickel or a nickel-based alloy, 2.5%-15% of a self-lubricating component, and 30%-77.5% of tungsten carbide particles; and the self-lubricating component is a nickel-coated molybdenum disulfide composite material or a nickel-coated graphite composite material. The invention further provides a preparation method of the tungsten carbide hard face abrasion-resistant bearing. According to the provided tungsten carbide hard face abrasion-resistant bearing, due to the existence ofthe lubricating component (such as graphite) in the coating, the friction coefficient of the surface of the hard face is lowered, and the abrasion performance can be effectively improved; and the lubricating component such as graphite is in three-dimensional uniform distribution, and can uninterruptedly occur on the new formed surface under the condition of initial surface abrasion, and thereforea self-lubricating effect is achieved.

Description

technical field [0001] The invention relates to the technical field of bearing materials, in particular to a tungsten carbide hard surface wear-resistant bearing and a preparation method thereof. Background technique [0002] Tungsten carbide hard faced anti-friction bearings are high performance bearings widely used in industry. The high hardness and wear resistance of tungsten carbide make the bearings containing tungsten carbide on the surface particularly prominent in high-load oil and gas drilling. [0003] At present, tungsten carbide hard-faced wear-resistant bearings are generally inlaid cemented carbide blocks and composite materials (such as figure 1 ). The tungsten carbide hard-faced wear-resistant bearing in the figure includes cemented carbide block, cast tungsten carbide particles and nickel-based alloy adhesive; among them, the selection of nickel-based alloy adhesive is due to the high strength of nickel and nickel alloy, and steel The affinity of the matr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B22F7/08B22F1/02B22F3/105C22C19/05C22C29/08
CPCC22C19/057C22C29/067C22C29/08B22F3/105B22F7/08B22F1/105B22F1/17
Inventor 徐跃华
Owner SEED TECH CORP LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap