Packaging box adhesive and preparation method thereof

A technology for adhesives and packaging boxes, applied in the direction of adhesive types, rosin adhesives, adhesives, etc., can solve the problems of unguaranteed product quality of packaging boxes, weak adhesive cohesion, compression resistance, Problems such as poor moisture resistance and high temperature resistance, to achieve strong adhesion, enhanced high temperature resistance and adhesion performance, and good adhesion performance

Inactive Publication Date: 2019-03-26
贵州众旺包装有限公司
View PDF2 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, this kind of adhesive has weak cohesive force, poor pressure resistance, moisture resistance a

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Example Embodiment

[0014] Example 1 of the present invention.

[0015] A packaging box adhesive, by weight, consists of 30-50 parts of epoxy resin, 30-50 parts of maleic acid resin, 30-50 parts of 2-imidazolidinone, 30-50 parts of ethylene-acetic acid copolymer, 10-20 parts of butyl rubber, 20-40 parts of epoxy soybean oil, 15-30 parts of castor oil hydrogenation mixture, 10-20 parts of cooked tung oil, 8-12 parts of tripropargyl trimellitate, water-soluble poly 8-12 parts of ethylene vinyl alcohol wax, 8-12 parts of isopropanol, 8-12 parts of silicone resin, 0.8-1.2 parts of antioxidant, 1-3 parts of tackifier and 2-20 parts of deionized water .

[0016] The packaging box adhesive is composed of 40 parts of epoxy resin, 40 parts of maleic acid resin, 40 parts of 2-imidazolidinone, 40 parts of ethylene-acetic acid copolymer, 15 parts of butyl rubber, and ring 30 parts of oxygenated soybean oil, 22 parts of castor oil hydrogenation mixture, 15 parts of cooked tung oil, 10 parts of tripropargyl trime...

Example Embodiment

[0023] Example 2 of the present invention.

[0024] A packaging box adhesive, by weight, composed of 30 parts epoxy resin, 30 parts maleic acid resin, 30 parts 2-imidazolidinone, 30 parts ethylene-acetic acid copolymer, 10 parts butyl rubber, epoxy resin 20 parts of soybean oil, 15 parts of castor oil hydrogenation mixture, 10 parts of cooked tung oil, 8 parts of tripropargyl trimellitate, 8 parts of water-soluble polyvinyl alcohol wax, 8 parts of isopropanol, 8 parts of silicone resin It is composed of 0.8 parts of antioxidant, 1 part of tackifier and 2 parts of deionized water.

[0025] The preparation method of the packaging box adhesive includes the following steps:

[0026] (1) Add epoxy resin, maleic acid resin, 2-imidazolidinone, tripropargyl trimellitate, and silicone resin into the reactor, stir and react at 120-150℃ for 0.9-1.3h, and cool to 80-90℃, add meta-ethylene-acetic acid copolymer dropwise, continue to stir and react for 0.5-0.6h to obtain modified epoxy resin;

[...

Example Embodiment

[0031] Example 3 of the present invention.

[0032] A packaging box adhesive, based on weight, composed of 50 parts of epoxy resin, 50 parts of maleic acid resin, 50 parts of 2-imidazolidinone, 50 parts of ethylene-acetic acid copolymer, 20 parts of butyl rubber, and epoxy 40 parts of soybean oil, 30 parts of castor oil hydrogenation mixture, 20 parts of cooked tung oil, 12 parts of tripropargyl trimellitate, 12 parts of water-soluble polyvinyl alcohol wax, 12 parts of isopropanol, 12 parts of silicone resin It consists of 1.2 parts of antioxidant, 3 parts of tackifier and 20 parts of deionized water.

[0033] The preparation method of the packaging box adhesive includes the following steps:

[0034] (1) Add epoxy resin, maleic acid resin, 2-imidazolidinone, tripropargyl trimellitate, and silicone resin into the reactor, stir and react at 120-150℃ for 0.9-1.3h, and cool to 80-90℃, add meta-ethylene-acetic acid copolymer dropwise, continue to stir and react for 0.5-0.6h to obtain mo...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a packaging box adhesive. The packaging box adhesive contains the following components in parts by weight: 30-50 parts of epoxy resin, 30-50 parts of maleic resin, 30-50 partsof 2-imidazolidone, 30-50 parts of an ethylene-acetate copolymer, 10-20 parts of butyl rubber, 20-40 parts of epoxidized soybean oil, 15-30 parts of a castor oil hydrogenated mixture, 10-20 parts of boiled wood oil, 8-12 parts of tripropargyl trimellitate, 8-12 parts of a water-soluble polyethylene acetylene alcohol wax, 8-12 parts of isopropanol, 8-12 parts of silicon resin, 0.8-1.2 parts of an antioxidant, 1-3 parts of a tackifier and 2-20 parts of deionized water. By utilizing the epoxy resin, the high temperature resistance and adhesion property of the adhesive can be improved, meanwhile,the prepared adhesive is non-toxic and harmless, and a water-glue separation phenomenon is unlikely to occur; and the preparation method is simple, low in process condition and stable in product quality, a paper board obtained through adhesion is high in compressive resistance and strong in puncture resistance, and the quality of a product packaging box can be guaranteed. The packaging box adhesive has the characteristics of strong adhesion force, compressive resistance, moisture resistance and high temperature resistance.

Description

technical field [0001] The invention relates to a packaging box adhesive and a preparation method thereof, belonging to the technical field of carton preparation. Background technique [0002] Among all kinds of packaging for industrial products, packing boxes have become the mainstream of the packaging industry, because they are light in weight, foldable, low in cost, environmentally friendly, easy to change in specifications, can be printed with high quality, and can be used as renewable materials after recycling. Resources, therefore, are used more and more widely. Adhesive is an essential material for packaging box enterprises, and it is mainly used in the compounding process of face paper or cardboard. At present, starch glue is mainly used for the bonding of cardboard. However, this type of adhesive has weak cohesive force, poor compression resistance, moisture resistance and high temperature resistance, so the quality of the produced packaging box products cannot be...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C09J163/00C09J193/04C09J123/08C09J123/22
CPCC08L2201/08C08L2205/035C09J123/0853C09J123/22C09J163/00C09J193/04C08L93/04C08L23/0853C08L23/22C08L63/00
Inventor 王智峰
Owner 贵州众旺包装有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products