Electrochemical element and all-solid-state lithium ion secondary battery

一种电化学元件、全固体的技术，应用在二次电池、锂蓄电池、电气元件等方向，能够解决输出小等问题

Active Publication Date: 2019-04-02
TDK CORPARATION
View PDF11 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] Electrochemical elements using solid electrolytes have a problem of lower output than electrochemical elements using electrolyte solutions

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Electrochemical element and all-solid-state lithium ion secondary battery
  • Electrochemical element and all-solid-state lithium ion secondary battery
  • Electrochemical element and all-solid-state lithium ion secondary battery

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0102] Example 1 is different from Comparative Example 1 in that the fired laminate was left in a constant temperature and humidity chamber at a temperature of 25° C. and a humidity of 50% for 12 hours before forming terminal electrodes. Other conditions are the same as in Comparative Example 1.

Embodiment 2

[0104] In Example 2, the fired laminate was first placed in a constant temperature and humidity chamber at a temperature of 25° C. and a humidity of 90% for 30 minutes, and then placed in a constant temperature and humidity chamber at a temperature of 25° C. and a humidity of 50% for 1 hour. Week. Then, it is different from Comparative Example 1 in that terminal electrodes are formed on the laminate taken out from the high-temperature, high-humidity tank. Other conditions are the same as in Comparative Example 1.

Embodiment 3

[0106] In Example 3, the fired laminate was first placed in a constant temperature and humidity chamber at a temperature of 25°C and a humidity of 90% for 2 hours, and then placed in a constant temperature and humidity chamber at a temperature of 25°C and a humidity of 50% for 1 week. . Then, it is different from Comparative Example 1 in that terminal electrodes are formed on the laminate taken out from the high-temperature, high-humidity tank. Other conditions are the same as in Comparative Example 1.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
relative densityaaaaaaaaaa
Login to View More

Abstract

An electrochemical element according to one embodiment of the present invention is provided with a laminate that comprises a positive electrode, a negative electrode and a solid electrolyte sandwichedbetween the positive electrode and the negative electrode. The laminate contains moisture; and the moisture content in the laminate is 0.001% by mass or more but less than 0.3% by mass relative to the laminate.

Description

technical field [0001] The invention relates to an electrochemical element and an all-solid lithium ion secondary battery. [0002] This application claims priority based on Japanese Patent Application No. 2016-153709 filed in Japan on August 4, 2016, the content of which is incorporated herein. Background technique [0003] Electrolytes as media for ion movement are used in various applications such as batteries, capacitors, and capacitors. As the electrolyte, there are an electrolytic solution using a liquid and a solid electrolyte using a solid. Liquid electrolyte has problems such as leakage. For example, when a liquid leak occurs in a lithium ion secondary battery, it can cause a fire. Therefore, electrochemical devices using solid electrolytes that do not have to worry about problems such as liquid leakage have attracted attention. [0004] An electrochemical element using a solid electrolyte has a problem of lower output than an electrochemical element using an el...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01M10/0562H01B1/06H01M10/052
CPCH01B1/06H01M10/052H01M10/0562H01M10/0585H01M10/0525H01M2300/0068H01M50/489H01M2300/0094H01M4/13H01M10/0566H01G11/56
Inventor 大石昌弘小宅久司佐藤洋高柳宽子矶道岳步
Owner TDK CORPARATION
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com