A super wear-resistant pvg flame retardant conveyor belt cover rubber

A conveyor belt, ultra-wear-resistant technology, applied in the field of conveyor belts, can solve the problems of short service life, high wear index, and high operating cost of conveyor belts, and achieve the effects of low cost, large transport volume, and low price

Active Publication Date: 2022-02-22
BAODING HUAYUE RUBBER BELTS
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Although they are 120-150mm larger than conventional conveyor belts 3 The Shao Boer wear index has been reduced to a certain extent, but the wear index is still high, the service life of the conveyor belt is still short, and the operating cost is high
[0004] At the same time, because most of the materials are inflammable, the fire scene becomes a source of smoke, poisonous gas and heat energy
This not only brings great fire hazards to people's safety and quality of life and property, but also greatly limits the application in special fields with high fire protection requirements (such as public places, commercial places, entertainment, educational places and other crowded places furniture) Material)

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A super wear-resistant pvg flame retardant conveyor belt cover rubber
  • A super wear-resistant pvg flame retardant conveyor belt cover rubber

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A super wear-resistant PVG flame-retardant conveyor belt cover rubber, which is composed of the following components by weight: 95 parts of SG-3 resin, 15 parts of dioctyl phthalate, tris (2-chloroethyl) phosphate 20 parts, 2 parts of tribasic lead sulfate, 4 parts of dibasic lead phosphite, 13 parts of triaryl phosphate, 5 parts of tetrapropylene titanate, 3 parts of antimony trioxide, 5213 parts of chlorinated paraffin, water 3 parts of zinc borate, 1 part of silane coupling agent, 1 part of dicumyl peroxide.

[0028] The preparation method of the super wear-resistant PVG flame-retardant conveyor belt cover glue comprises the following steps:

[0029] (1) Put SG-3 type resin, dioctyl phthalate, and tetrapropylene titanate into the internal mixer for 2 minutes, the speed is 40r / min, and then add tris (2-chloroethyl) phosphate , tribasic lead sulfate, dibasic lead phosphite, triaryl phosphate, antimony trioxide, chlorinated paraffin-52, zinc borate water, mixing for 5 ...

Embodiment 2

[0033]A super wear-resistant PVG flame-retardant conveyor belt cover rubber, which is composed of the following components by weight: 98 parts of SG-3 resin, 18 parts of dioctyl phthalate, tris (2-chloroethyl) phosphate 23 parts, 2 parts of tribasic lead sulfate, 4 parts of dibasic lead phosphite, 14 parts of triaryl phosphate, 6 parts of tetrapropylene titanate, 4 parts of antimony trioxide, 5214 parts of chlorinated paraffin, water 3 parts of zinc borate, 1 part of silane coupling agent, 1 part of dicumyl peroxide.

[0034] The preparation method of the super wear-resistant PVG flame-retardant conveyor belt cover glue comprises the following steps:

[0035] (1) Put SG-3 resin, dioctyl phthalate, and tetrapropylene titanate into the internal mixer for 3 minutes, the speed is 42r / min, and then add tris (2-chloroethyl) phosphate , tribasic lead sulfate, dibasic lead phosphite, triaryl phosphate, antimony trioxide, chlorinated paraffin-52, zinc borate water, mixing for 6 minute...

Embodiment 3

[0039] A super wear-resistant PVG flame-retardant conveyor belt cover rubber, which is composed of the following components by weight: 100 parts of SG-3 type resin, 20 parts of dioctyl phthalate, tris (2-chloroethyl) phosphate 25 parts, 3 parts of tribasic lead sulfate, 5 parts of dibasic lead phosphite, 15 parts of triaryl phosphate, 7 parts of tetrapropylene titanate, 5 parts of antimony trioxide, 5215 parts of chlorinated paraffin, water 3.5 parts of zinc borate, 2 parts of silane coupling agent, and 2 parts of dicumyl peroxide.

[0040] The preparation method of the super wear-resistant PVG flame-retardant conveyor belt cover glue comprises the following steps:

[0041] (1) Put SG-3 type resin, dioctyl phthalate, and tetrapropylene titanate into the internal mixer for 3 minutes, the speed is 43r / min, and then add tris (2-chloroethyl) phosphate , tribasic lead sulfate, dibasic lead phosphite, triaryl phosphate, antimony trioxide, chlorinated paraffin-52, zinc borate in wat...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a super wear-resistant PVG flame-retardant conveyor belt cover rubber, which belongs to the field of conveyor belts and consists of the following components in parts by weight: 95-105 parts of SG-3 type resin, 15-15 parts of dioctyl phthalate 25 parts, 20-30 parts of tris(2-chloroethyl) phosphate, 2-4 parts of tribasic lead sulfate, 4-6 parts of dibasic lead phosphite, 13-18 parts of triaryl phosphate, titanic acid 5-9 parts of tetrapropenyl ester, 3-7 parts of antimony trioxide, 13-17 parts of chlorinated paraffin-52, 3-4 parts of zinc borate water, 1-3 parts of silane coupling agent, dicumyl peroxide 1 to 3 servings. The super wear-resistant PVG flame-retardant conveyor belt cover glue provided by the present invention has the characteristics of high strength, large transportation volume, and balanced transportation. At the same time, the product has good flame retardancy, antistatic, impact resistance, wear resistance, corrosion resistance, High strength, excellent safety performance and other characteristics, as well as lower cost and lower price compared with other flame-retardant conveyor belts.

Description

technical field [0001] The invention relates to the technical field of conveyor belts, in particular to a super wear-resistant PVG flame-retardant conveyor belt cover glue. Background technique [0002] Conveyor belts are an indispensable tool in material transportation industries such as mines, power plants, coal, and docks, and their continuity and high efficiency play a huge role. At the same time, due to the increase in the current conveying volume, the large transport capacity and long transport distance of the steel wire rope conveyor belt are also gradually significant. But at the same time, the conveyor belt is affected by the material during operation, and the long-term contact and friction with the conveyor roller and the material will cause the conveyor belt covering rubber to be non-wearable and easy to fall off, resulting in frequent maintenance and short life. Therefore, the operating cost is higher, and the scrapped conveyor belt cannot be reused. Prolonging...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C08L27/06C08L91/06C08K13/02C08K5/12C08K5/521C08K3/30C08K5/523C08K3/22C08K3/32C08K3/38B65G15/32
Inventor 李昭钦
Owner BAODING HUAYUE RUBBER BELTS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products