A composition, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition, and a preparation method thereof

A fracturing fluid thickener, temperature-resistant and salt-resistant technology, which is applied in the field of temperature-resistant and salt-resistant fracturing fluid thickener and its preparation, and in the field of preparation of temperature-resistant and salt-resistant fracturing fluid thickener compositions. There are few problems such as research, so as to achieve the effect of complete glue breaking, complete flowback and large tolerance

Active Publication Date: 2021-09-24
SHANDONG NUOER BIOLOGICAL TECH
View PDF13 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The currently used synthetic polymers mainly include polyacrylamide cross-linked jelly and hydrophobically associated polyacrylamide (HAPAM), and the latter has strong salt and shear resistance when used as a fracturing fluid thickener. The characteristics of complete gel breaking have attracted widespread attention, but there are few researches on products with high temperature resistance (>130°C) and high salt resistance.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A composition, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition, and a preparation method thereof
  • A composition, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition, and a preparation method thereof
  • A composition, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition, and a preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0039] The present invention also provides a preparation method of a temperature-resistant and salt-resistant fracturing fluid thickener, the preparation method comprising the following steps:

[0040] (1) Mix the composition provided by the present invention and 507 to 700 parts by weight of the second solvent (for example, it can be 507, 600 or 700 parts by weight), and adjust the pH of the mixing system to 6.5 to 6.8 (for example, it can be 6.5, 6.6, 6.7 or 6.8), then add 0.01 to 0.025 parts by weight of a molecular weight regulator (for example, 0.01, 0.02 or 0.025 parts by weight) to the mixed system, pass nitrogen to remove oxygen, and then add the initiator system to the mixed system 0.001~0.5 parts by weight (for example, it can be 0.001, 0.01, 0.1, 0.2, 0.4 or 0.5 parts by weight) at 10~12°C (for example, it can be 10°C, 11°C or 12°C) to initiate the polymerization reaction, and the reaction ends Finally, the temperature-resistant and salt-resistant fracturing fluid t...

Embodiment 1

[0046] Prepare shielding agent

[0047] The preparation raw materials include: 130 parts by weight of acrylic acid, 13 parts by weight of maleic anhydride, 13 parts by weight of 2-acrylamide-2-methylpropanesulfonic acid, 8 parts by weight of sodium methacrylate, 85 parts by weight of sodium hydroxide, and 751 parts by weight of ionized water, 0.5 parts by weight of sodium formate, 0.08 parts by weight of ammonium persulfate, and 0.04 parts by weight of sodium bisulfite.

[0048] The preparation method comprises the following steps:

[0049] Add acrylic acid, maleic anhydride, 2-acrylamide-2-methylpropanesulfonic acid, sodium methacrylsulfonate and deionized water into the reactor, after fully dissolving, adjust the pH value of the solution with sodium hydroxide, and adjust the pH The value is adjusted between 7.0-7.2, and sodium formate is added at the same time;

[0050] Deoxygenate with nitrogen for 60 minutes, add ammonium persulfate and sodium bisulfite in turn, and poly...

Embodiment 2

[0054] The preparation raw materials include: 215 parts by weight of acrylamide, 45 parts by weight of acrylic acid, 8 parts by weight of N,N-di-n-octyl acrylamide, 20 parts by weight of 2-acrylamide-2-methylpropanesulfonic acid, p-styrenesulfonic acid 40 parts by weight of sodium, 1.5 parts by weight of sodium lauryl sulfate, 15 parts by weight of shielding agent, 29 parts by weight of sodium hydroxide, 626.5 parts by weight of deionized water, 0.12 parts by weight of sodium formate, azobisisobutylamidine dihydrochloride 0.15 parts by weight, 0.02 parts by weight of potassium persulfate and 0.015 parts by weight of sodium bisulfite.

[0055] The preparation method comprises the following steps:

[0056] Add acrylamide, acrylic acid, N,N-di-n-octyl acrylamide, 2-acrylamide-2-methylpropanesulfonic acid, sodium p-styrenesulfonate, sodium lauryl sulfate, After the shielding agent and deionized water are fully dissolved, adjust the pH value of the solution with sodium hydroxide t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
viscosityaaaaaaaaaa
Login to view more

Abstract

The invention relates to a composition for preparing a temperature-resistant and salt-resistant fracturing fluid thickener, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition and a preparation method thereof. The composition comprises the following components: acrylamide, acrylic acid, hydrophobic monomer, 2-acrylamide-2-methylpropanesulfonic acid, rigid monomer, surfactant and screening agent. The temperature-resistant and salt-resistant fracturing fluid thickener provided by the present invention can achieve a good sand suspension effect without cross-linking with a cross-linking agent, and has better temperature-resistant and salt-resistant properties. After aging for 2 hours in simulated brine with a concentration of 50,000 mg / L, the viscosity retention rate of the fracturing fluid thickener is ≥80%. The fracturing fluid solution prepared by the present invention is completely broken, has no water insoluble residue, and has a thorough flowback. No damage to the formation, no pollution to the oil layer.

Description

technical field [0001] The invention relates to the technical field of oil field acidizing and fracturing, in particular to a composition for preparing a temperature-resistant and salt-resistant fracturing fluid thickener, a temperature-resistant and salt-resistant fracturing fluid thickener prepared by using the composition and its preparation method. Background technique [0002] The proportion of low-permeability oil and gas resources in my country is more than 50%, and low-permeability oil and gas resources have become the main exploration and development targets in China. Because low-permeability reservoirs are affected by factors such as large burial depth, high formation temperature (120°C-160°C), high salinity of formation water, strong diagenesis and compaction, etc., they usually have to undergo fracturing, acidizing, and acid fracturing. Effective development can only be achieved through measures to increase production. The high-temperature and salt-resistant fr...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C09K8/68C08F220/06C08F222/06C08F220/58C08F228/02C08F220/56C08F220/54C08F212/14
Inventor 荣敏杰孙建波许永升于庆华荣帅帅
Owner SHANDONG NUOER BIOLOGICAL TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap