A low-cost preparation method of ultrafine-grained high-strength plastic rare earth magnesium alloy

A rare-earth magnesium and ultra-fine-grained technology, which is applied in the field of magnesium alloy processing, achieves the effects of simple operation, high density, and avoiding long processing cycles

Active Publication Date: 2021-01-05
SOUTHWEST UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0008] The technical problem to be solved by the present invention is to overcome the disadvantages of the production technology of ultra-fine-grained magnesium alloy in the above-mentioned background technology, and provide an ultra-fine-grained superplastic rare-earth magnesium alloy with small deformation, low damage, low cost and short production cycle Preparation

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A low-cost preparation method of ultrafine-grained high-strength plastic rare earth magnesium alloy
  • A low-cost preparation method of ultrafine-grained high-strength plastic rare earth magnesium alloy

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0021] In order to facilitate the understanding of the method of the present invention, ZK60-1.2Yb deformed magnesium alloy is used as an example material below, and the present invention will be further described in detail in combination with the description of the drawings and specific implementation examples.

[0022] When preparing ZK60-1.2Yb magnesium alloy, the following methods can be used specifically:

[0023] a. Alloy melting: in SF 6 +CO 2 Under the protection of gas, the magnesium alloy ingredients with the national standard of ZK60 are smelted according to the normal smelting process. After being fully dissolved, the Mg-Yb master alloy with a Yb content of 1.2% of the mass percentage of the final smelted alloy design is added at 770-780 ° C. Stand at 700-730°C for 10-20 minutes to remove slag, then pour out of the furnace and cool naturally to room temperature;

[0024] b. Solid solution treatment: keep warm for 48 hours in an environment filled with argon at 40...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
tensile strengthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses a low-cost preparation method of an ultrafine-grained high-strength plastic rare earth magnesium alloy. The low-cost preparation method comprises the steps of alloy smelting, solution treatment and isothermal extrusion, specifically, firstly a ZK60 magnesium alloy containing a rare earth element ytterbium (Yb) with a mass percentage of 0.8-1.5% is smelted according to the composition, then rapidly condensed into an ingot and then subjected to the solution treatment at 400 DEG C for 48 h, and finally the isothermal extrusion is performed at 330-350 DEG C with a strain rate of 0.1-1.0 s<-1> and an extrusion ratio of 10-30 to obtain an ultrafine-grained high-strength plastic magnesium alloy block with an average grain size of less than 1 [mu]m, the tensile strength ofmore than 400 MPa and the elongation of more than 15%. According to the low-cost preparation method of the ultrafine-grained high-strength plastic rare earth magnesium alloy, conventional low extrusion ratio deformation is utilized to obtain an ultrafine-grained structure which is difficult to obtain in a conventional magnesium alloy system, the addition amount of the rare earth element is combined to control the strength and plasticity of the alloy, and finally a magnesium alloy block material which is refined in structure and has high strength and plasticity is obtained. The cost is low, theprocess is short, the efficiency is high, and good industrial application prospects are achieved.

Description

technical field [0001] The invention belongs to the technical field of processing magnesium alloys, in particular to a simple processing method for producing ultra-fine-grained high-strength plastic rare-earth magnesium alloys, in particular to a low-cost preparation method for ultra-fine-grained high-strength plastic rare-earth magnesium alloys. Background technique [0002] Because magnesium alloy has the advantages of low density, specific stiffness, high specific strength, good damping performance, shock absorption performance, electromagnetic shielding performance and recyclability, magnesium alloy is widely used in automobiles, aerospace, weapons and other fields. However, the disadvantages of magnesium alloys such as low strength, poor corrosion resistance, and poor plasticity at room temperature also seriously restrict the development and application of magnesium alloys. [0003] Since the lattice structure of the matrix element magnesium is a close-packed hexagonal ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C1/03C22C23/04C22F1/06B21C23/00B21C29/00
Inventor 李路王雨张存才王涛李豪潘志远
Owner SOUTHWEST UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com