Inlaying method for products having diameter or thickness less than 2mm

A product, thermal mounting technology, applied in the field of mounting, can solve problems such as sample deflection, inability to accurately test and analyze, failure analysis of samples and internal organizational structure morphology, etc., to achieve accurate analysis data and reduce costs

Active Publication Date: 2019-05-03
NANJING IRON & STEEL CO LTD
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The technical problem to be solved by the present invention is to solve the problem of inlaying a product with a diameter or thickness less than 2mm without a spring clamp, that is, the problem that the sample cannot be correctly analyzed for failure or the inspection and analysis of the surface and internal tissue structure; at the same time, it solves the problem of traditional In the process of inlaying small samples, the sample deflection often leads to the problem of inaccurate inspection and analysis, overcomes the shortcomings of the existing technology, and provides an inlay method suitable for products with a diameter or thickness less than 2mm. This inlay method is simple and easy to implement and low in cost. , high accuracy of inspection and analysis data

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Inlaying method for products having diameter or thickness less than 2mm
  • Inlaying method for products having diameter or thickness less than 2mm
  • Inlaying method for products having diameter or thickness less than 2mm

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030] This embodiment provides an inlay method suitable for products with a diameter or thickness less than 2mm, which specifically includes the following steps:

[0031] (1) Choose the mosaic method according to the product requirements, such as semiconductors, mild steel, etc., which will be damaged when heated, choose cold mosaic, general steel, etc. choose hot mosaic, and choose according to the needs of the product;

[0032] (2) Spread the prepared 0.85mm sample sheet and the 0.3mm diameter wire-drawn sample in a metallographic mounting machine with an inner mold of 30mm preheated for 5 minutes, and then put 7-10g of thermal mounting powder (the thermal mounting powder is phenolic The mixture of plastic powder, bakelite powder and electric jade powder, hot mosaic powder is already in good proportion when you buy it, and the hot mosaic powder with such ingredients in it is used) to form a 5mm high sample, close the lid, and apply pressure , 150 degrees heat preservation f...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Thicknessaaaaaaaaaa
Thicknessaaaaaaaaaa
Login to view more

Abstract

The invention discloses an inlaying method for products having the diameter or thickness less than 2mm. The method comprises the following steps that: step one, an inlaying method is selected based ona product need, wherein the inlaying method includes thermal inlaying and cold inlaying; step two, a sample having the diameter or thickness less than 2mm is laid in an inlaying machine for primary inlaying, wherein the inlaying depth reaches 4 to 8mm; step three, after the primary inlaying in the step two, the sample is cooled and a cutting machine is used for cutting the sample longitudinally into small samples with secondary inlaying; step four, carrying out secondary inlaying vertically on the small samples obtained after longitudinal cutting in the step three to ensure the product integrity; and step five, the samples after secondary inlaying are ground, polished and analyzed based on a preparation flow used by metallographic phase. According to the invention, a problem of inlaying of a product having the diameter or thickness less than 2mm by a fixture without a spring and a problem that detection and analysis can not be carried out accurately due to test sample deviation duringthe traditional small sample inlaying process are solved. The inlaying method is simple and is easy to implement; and the data checking and analysis accuracy is high.

Description

technical field [0001] The invention relates to a practical inlay method for preparing cold and hot inlay samples in the iron and steel manufacturing industry. Specifically, it is suitable for internal structure, decarburization layer, and surface of products with a diameter or thickness less than 2mm without the need for spring clamps. A mosaic method for the analysis of defects, failures, etc. Background technique [0002] In the iron and steel manufacturing industry, the diversity of product shapes is the characteristic of the industry. How to analyze the surface and internal organization of products of different shapes is a test. The research department analyzes product performance and promotes product production process improvement. One of the necessary items. Therefore, for a long time, the manufacturing industry has been accustomed to irregular shapes, wires and plates, small workpieces, surface treatment and coating, surface decarburization material preparation (grin...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): G01N1/28G01N1/32
Inventor 刘莉雍太平张华伟郝宇雄王超
Owner NANJING IRON & STEEL CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products