A thermoplastic resin and a joining method technology, which are applied in the fields of joining and joining devices for fiber-reinforced thermoplastic resin parts, and can solve the problems of high temperature and poor appearance.

Inactive Publication Date: 2019-05-17
TOYOTA JIDOSHA KK
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] However, in a fiber-reinforced thermoplastic resin part, when the heating temperature is increased to sufficiently heat the part to be joined, the temperature of the surface away from the joint surface is also increased due to heat transfer by the reinforcing fibers.
Here, in the method of performing natural cooling after heating the part to be joined, the temperature of a part of the surface of the part to be joined may exceed the melting temperature to cause surface swelling, etc., which may cause appearance defects.
[0005] That is, in the case of heating and joining a plurality of fiber-reinforced thermoplastic resin parts by the heating unit, compared with the method of only using natural cooling for cooling after heating, the joint part of the joining target part is guaranteed to be more efficient. There is room for improvement in the aspect of suppressing the appearance defect of the joint target part while reducing the shear strength

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Fiber-reinforced thermoplastic resin member welding method and welding device
  • Fiber-reinforced thermoplastic resin member welding method and welding device
  • Fiber-reinforced thermoplastic resin member welding method and welding device

Examples

Experimental program
Comparison scheme
Effect test

no. 1 approach

[0044] An example of the method for joining fiber-reinforced thermoplastic resin parts and the device for joining fiber-reinforced thermoplastic resin parts according to the first embodiment will be described.

[0045] the whole frame

[0046] exist figure 1 In , a bonding device 20 for bonding the resin component 12 and the resin component 14 is shown. The resin member 12 and the resin member 14 are examples of a plurality of fiber-reinforced thermoplastic resin members. The joining device 20 is an example of a joining device for fiber-reinforced thermoplastic resin components. In addition, as an example, the resin member 12 and the resin member 14 are set to be members having the same shape, size, and composition. Therefore, the resin member 12 will be described, and the description of the resin member 14 will be omitted.

[0047] As an example, the resin member 12 is set as a plate material formed into a rectangular shape when viewed from above. In the following descri...

no. 2 approach

[0099] Next, an example of a method for joining fiber-reinforced thermoplastic resin components and a device for joining fiber-reinforced thermoplastic resin components according to the second embodiment will be described. In addition, about components and locations that are basically the same as those in the first embodiment described above, the same reference numerals as those in the first embodiment will be assigned and descriptions thereof will be omitted.

[0100] exist Figure 6 In , the engagement device 80 of the second embodiment is shown. The joining device 80 is an example of a joining device for fiber-reinforced thermoplastic resin components. Furthermore, as an example, the joining device 80 has a heating part 30 , a pressurizing part 90 , a support roller 82 , and a cooling part 50 . The pressurizing part 90 is an example of a pressurizing part. In addition, in the bonding apparatus 80, the mounting table 22 and the moving part 60 are not provided (refer to f...

no. 3 approach

[0110] Next, an example of a method for joining fiber-reinforced thermoplastic resin parts and an apparatus for joining fiber-reinforced thermoplastic resin parts according to the third embodiment will be described. In addition, about the components and parts which are basically the same as those in the above-mentioned first and second embodiments, the same symbols as those in the first and second embodiments are given, and description thereof will be omitted.

[0111] exist Figure 7 In , the joining device 100 of the third embodiment is shown. The joining device 100 is an example of a joining device for fiber-reinforced thermoplastic resin components. In addition, as an example, the joining device 100 is configured such that, in the joining device 20 of the first embodiment (refer to figure 1 ), instead of the cooling unit 50 (see figure 1 ) and a cooling unit 110 is provided. In addition, in Figure 7 In, the storage part 34 and the power supply 38 are omitted (refer t...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

A fiber-reinforced thermoplastic resin member welding method includes: heating, by a heating unit, a welding target portion in which plural fiber-reinforced thermoplastic resin members layered on topof each other, each of the plural fiber-reinforced thermoplastic resin members including thermoplastic resin as a main composition, and the thermoplastic resin including reinforcing fibers; applying pressure, by a pressure applying unit, to the welding target portion; and cooling, by a cooling unit, at least a surface of the welding target portion at the same time as when the welding target portion is being heated by the heating unit or after the welding target portion has been heated by the heating unit.

Description

technical field [0001] The present disclosure relates to a joining method and joining device of fiber-reinforced thermoplastic resin components. Background technique [0002] In Japanese Unexamined Patent Application Publication No. 2004-160675, a welding method is disclosed in which, when a part made of thermoplastic resin is welded on a product body made of thermoplastic resin, the Welding is carried out with the thermoplastic resin film of the area between the welding parts interposed. [0003] In the case of heating and joining a portion to be joined in which a part of a plurality of fiber-reinforced thermoplastic resin members are laminated by a heating unit, it is necessary to sufficiently heat the portion to be joined in order to ensure the shear strength of the joined portion to be joined. to melt it. [0004] However, in a fiber-reinforced thermoplastic resin component, when the heating temperature is increased in order to sufficiently heat the part to be joined, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): B29C65/32
CPCB29C65/364B29C65/3668B29C66/1122B29C66/43B29C66/836B29C66/8362B29C65/3684B29C66/72141B29C65/8215B29C65/8253B29C66/0342B29C66/342B29C66/349B29C66/81465B29C66/81811B29C66/91411B29C66/91951B29C66/7212B29C66/73921B29C66/71B29K2077/00B29K2023/12B29K2081/04B29K2067/003B29K2067/006B29K2069/00B29K2033/12B29K2055/02B29K2063/00B29K2307/04B29K2305/00B29K2305/12B29C65/3424B29C65/222B29C65/242
Inventor 岩野吉宏
Owner TOYOTA JIDOSHA KK
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap