Production process of polyester filament interwoven multifunctional bedding fabric
A polyester filament and production process technology, which is applied in the field of polyester fabrics, can solve the problems of difficult coloring of polyester fabrics, inconvenient fading of polyester fabrics, and inability to form patterns on fabric weaving threads, so as to achieve the effect of improving the difficulty of coloring.
Inactive Publication Date: 2019-05-17
新昌县丙辰储能科技有限公司
View PDF9 Cites 2 Cited by
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
[0003] The purpose of the present invention is to provide a production process for polyester filament interwoven multifunctional bedding fabrics, which solves the problem of mixing PBT or PET particles with dyes in the traditional process steps, and then coloring the particles to make master batches. Polyester filaments and fine polyester filaments are co-extruded on the wire drawing machine to achieve the coloring of the fabric weaving thread. Although this method can improve the defect that the polyester fabric is not easy to color and make the fabric weaving thread overall colored, it cannot achieve the fabric color. The weaving thread is colored according to a specific pattern, so that the fabric weaving thread itself cannot form a specific pattern, and because the PBT or PET particles are combined with thick polyester filaments and fine polyester filaments through the co-extrusion of the wire drawing machine, thus Problems that make polyester fabrics extremely inconvenient when they are recycled and need to be faded
Method used
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View moreImage
Smart Image Click on the blue labels to locate them in the text.
Smart ImageViewing Examples
Examples
Experimental program
Comparison scheme
Effect test
Embodiment Construction
[0025] The following will clearly and completely describe the technical solutions in the embodiments of the present invention with reference to the accompanying drawings in the embodiments of the present invention. Obviously, the described embodiments are only some, not all, embodiments of the present invention. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without creative efforts fall within the protection scope of the present invention.
[0026] Such as Figure 1-2 Shown is the production process of polyester filament interwoven multifunctional bedding fabric. The bedding fabric is made of coarse polyester filament, fine polyester filament and PBT blended filament. The bedding fabric is prepared by the following steps :
[0027] Raw material selection, coloring, drying, weaving, co-extrusion, weaving and finishing;
[0028] The selection of raw materials includes the selection of 1100D high-streng...
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More PUM
Login to View More Abstract
The invention discloses a production process of a polyester filament interwoven multifunctional bedding fabric. The bedding fabric is made of raw materials of coarse count polyester filaments, fine count polyester filaments and PBT blended filaments by the following steps: raw material selection, coloring, drying, weaving, coextrusion, weaving and finishing. The production technology solves the problems that in the traditional process steps, PBT or PET particles are mixed with dye, master batches are prepared from the particles by coloring, the master batches, the coarse count polyester filaments and the fine count polyester filaments are coextruded on a drawing machine to realize coloring of fabric threads, the defect that polyester fabrics are not easily colored can be overcome, but thefabric threads cannot form specific patterns as coloring of the fabric threads cannot be performed according to specific lines, and the problem that polyester fabric are quite inconvenient to recoverand fade since the PBT or PET particles are combined with the coarse count polyester filaments and the fine count polyester filaments by coextrusion of the drawing machine is solved.
Description
technical field [0001] The invention relates to the field of polyester fabrics, in particular to a production process of polyester filament interwoven multifunctional bedding fabrics. Background technique [0002] Polyester fabric is a kind of chemical fiber clothing fabric widely used in daily life. Its biggest advantage is that it has good wrinkle resistance and shape retention, so it is suitable for outerwear, various bags, bedding fabrics and tents. Polyester filament needs to go through a series of processing steps in the production of bedding fabrics. In the traditional process steps, PBT or PET particles are mixed with dyes, and the particles are colored to make masterbatches. , Fine polyester filaments are co-extruded on the wire drawing machine to realize the coloring of the fabric weaving thread. Although this method can improve the defect that the polyester fabric is not easy to color and make the fabric weaving thread overall colored, it cannot achieve the color...
Claims
the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More Application Information
Patent Timeline
Login to View More Patent Type & Authority Applications(China)
IPC IPC(8): D02G3/34D03D15/00D03D15/283D03D15/47D03D15/54D03D15/573D03D15/58
Inventor 不公告发明人
Owner 新昌县丙辰储能科技有限公司