Stamp rubber material capable of being used for capacitor printing and preparation method thereof

A rubber and seal technology, applied in the field of rubber stamp rubber and its preparation, can solve the problems of thermal instability, poor dimensional stability of rubber, adhesion, wear resistance and corrosion resistance, etc., to achieve adhesion Strong, good mechanical strength, excellent dimensional stability effect

Active Publication Date: 2019-05-31
AGRI PRODS PROCESSING RES INST CHINESE ACAD OF TROPICAL AGRI SCI
View PDF8 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, when the existing rubber materials for stamps are used on products such as capacitors or resistors, they are prone to thermal instability due to excessive local temperature during the use of electrical appliances, such as poor dimensional stability of the rubber material, poor adhesion, and wear resistance. , corrosion resistance, etc. need to be improved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Stamp rubber material capable of being used for capacitor printing and preparation method thereof
  • Stamp rubber material capable of being used for capacitor printing and preparation method thereof
  • Stamp rubber material capable of being used for capacitor printing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0042] Preferably, the preparation method of described modified nanometer calcium carbonate comprises the steps:

[0043] 10 parts by weight of nano-calcium carbonate and 1 to 2 parts by weight of functionalized hyperbranched polyethylene are added to a high-speed mixer, stirred and mixed for 45 minutes at 70°C, then heated to 210°C, and (0.5 to 1.5 parts by weight part) polyphosphoric acid solution of vinyl silsesquioxane (CAS: 69655-76-1, purchased from Suzhou Sisuo New Material Co., Ltd.) and 0.004 to 0.008 parts by weight of initiator were added to the above mixing system, and the heat preservation reaction After 3 to 5 hours, the system is cooled to room temperature, poured into acetone solution, washed, filtered, and dried.

[0044] Preferably, the functionalized hyperbranched polyethylene is maleic anhydride graft modified hyperbranched polyethylene.

[0045] Preferably, the graft ratio of the maleic anhydride graft modified hyperbranched polyethylene is 5-12%.

[004...

Embodiment 1

[0083] Embodiment 1 provides a kind of stamp glue, and its preparation raw material, by weight, comprises the following components:

[0084]

[0085] The nitrile rubber is the product of N-726 (the acrylonitrile content is 27% and the Mooney viscosity (ML100 ℃ 1+4) is 60) for the trade mark of Sai Kede Rubber and Plastics Group Company; the epoxidized natural rubber is made of tropical Provided by the Rubber Research Institute of the Academy of Sciences, the degree of cyclization is 5%; the filler is composed of 30 parts by weight of white carbon black and 10 parts by weight of calcium carbonate, and the white carbon black is precipitated white carbon black, purchased from Jinan Jinri and Chemical Co., Ltd., the nano-calcium carbonate is purchased from Beijing Deke Daojin Technology Co., Ltd., and its average particle diameter is 20nm; the active agent is made up of 1 weight part of stearic acid and 10 weight parts of zinc oxide; The anti-aging agent is composed of anti-agi...

Embodiment 2

[0091] Embodiment 2 provides a kind of stamp glue, and its preparation raw material, by weight, comprises the following components:

[0092] Nitrile rubber 70

[0093] Epoxidized Natural Rubber 50

[0094] Filler 50

[0095] active agent 25

[0096] Antiager 5

[0097] Accelerator 8

[0098] Vulcanizing agent 5

[0099] Pigment 3.

[0100] The nitrile rubber is the product of N-608 (the acrylonitrile content is 33% and the Mooney viscosity (ML100° C. 1+4) is 80) of Sai Kede Rubber and Plastic Group Company; Provided by the Rubber Research Institute of the Academy of Sciences, the degree of cyclization is 60%; the filler is composed of 50 parts by weight of white carbon black and 30 parts by weight of calcium carbonate, and the white carbon black is precipitated white carbon black, purchased from Jinan Jinri and Chemical Co., Ltd., the nano-calcium carbonate is purchased from Beijing Deke Daojin Technology Co., Ltd., and its average particle diameter is 20nm; the active ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
The average particle sizeaaaaaaaaaa
Grafting rateaaaaaaaaaa
Login to View More

Abstract

The invention relates to the field of design rubber materials, in particular to a stamp rubber material capable of being used for capacitor printing and a preparation method thereof. The stamp rubbermaterial is prepared by, by weight, 50-70 parts of nitrile-butadiene rubber, 30-50 parts of epoxidized natural rubber, 30-50 parts of filler, 10-25 parts of activating agent, 1-5 parts of anti-aging agent, 3-8 parts of accelerant, 2-5 parts of vulcanizing agent and 1-3 parts of pigment.

Description

technical field [0001] The invention relates to the field of rubber materials, in particular to a rubber stamp material which can be used for printing on capacitors and a preparation method thereof. Background technique [0002] Today's 21st century has entered the electronic age, the output of electronic products has also increased rapidly, and the industry competition has become increasingly fierce. For manufacturers, the headache is that there will be a logo on the surface of each electronic component product, and the logo needs to be stamped on it. On the one hand, the manufacturer maintains production costs, and on the other hand, it must ensure efficiency. The first thing that comes to mind is the inkjet printer, because the inkjet printer has a wide range of uses, but the use of the inkjet printer faces high cost investment, followed by high maintenance costs. Therefore, stamp rubber came into being, which is not only low cost, zero maintenance cost, but also high ef...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): C08L9/02C08L15/00C08K13/02C08K5/09C08K3/22C08K3/36C08K3/26
Inventor 曾宗强余和平王启方
Owner AGRI PRODS PROCESSING RES INST CHINESE ACAD OF TROPICAL AGRI SCI
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com