Moon white glaze Ru porcelain and preparation method thereof

A technology of Ruci and Yuebai, which is applied in the field of ceramics, can solve problems such as inexorable toxicity and human hazards, and achieve the effect of increasing market share, excellent porcelain quality, and moderate thermal insulation

Active Publication Date: 2019-06-25
王晟鸣
View PDF9 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The sintering temperature of Ru porcelain is generally between 1180°C and 1235°C, so the toxicity in chromium oxide cannot be ruled out, and it is very harmful to the human body as a practical device.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Moon white glaze Ru porcelain and preparation method thereof
  • Moon white glaze Ru porcelain and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A moon white glazed Ru porcelain, comprising a body and glaze, the body is composed of the following components in parts by mass: 20-35 parts of Fengxue soil, 30-65 parts of kaolin clay, 20-55 parts of Tanggou soil parts, 10~20 parts of black wool soil, 0.5~2 parts of white feldspar, 1~2.5 parts of sandstone; the glaze is composed of the following components by mass: 50~65 parts of white feldspar, 50~65 parts of red feldspar 10-20 parts of calcite, 10-20 parts of calcite, 5-10 parts of black stone, 5-12 parts of agate, 0.5-1.2 parts of sheep bone ashes, and 3-10 parts of wollastonite.

[0030] A kind of preparation method of moon white glaze Ru porcelain, comprises the following steps:

[0031] Step 1. Calculate according to the above-mentioned mass parts, take 20-35 parts of Fengxue soil, 30-65 parts of kaolin clay, 20-55 parts of Tanggou soil, 10-20 parts of black wool soil, 0.5-2 parts of white feldspar, sand Mix 1-2.5 parts of stone evenly to obtain mixture A, put ...

Embodiment 2

[0054] A moon white glazed Ru porcelain, comprising a green body and a glaze, the green body is composed of the following components in parts by mass: 28 parts of Fengxue soil, 32 parts of kaolin clay, 24 parts of Tanggou soil, 13.5 parts of black wool soil 1.2 parts of white feldspar, 1.3 parts of sandstone; the glaze is composed of the following components by mass: 55 parts of white feldspar, 12 parts of red feldspar, 15 parts of calcite, 6 parts of black stone, agate 6 parts, 1 part of sheep bone ashes, 5 parts of wollastonite.

[0055] A kind of preparation method of moon white glaze Ru porcelain, comprises the following steps:

[0056] Step 1. Select high-quality wind-hole soil, kaolin, Tanggou soil, and black hairy soil raw materials. After selection, bleaching, and crushing, mix with feldspar and sandstone according to 28 parts of wind-hole soil, 32 parts of kaolin, 24 parts of Tanggou soil, Mix 13.5 parts of black hairy soil, 1.2 parts of white feldspar, and 1.3 parts...

Embodiment 3

[0074] A kind of moon white glazed Ru porcelain, including a body and a glaze, the body is composed of the following components in parts by mass: 20 parts of Fengxue soil, 30 parts of kaolin clay, 37 parts of Tanggou soil, 11 parts of black wool soil parts, 0.5 parts of white feldspar, 1.5 parts of sandstone; the glaze is composed of the following components in mass parts: 50 parts of white feldspar, 10 parts of red feldspar, 20 parts of calcite, 10 parts of black stone, agate 5 parts, sheep ashes 0.6 parts, wollastonite 4.4 parts.

[0075] A kind of preparation method of moon white glaze Ru porcelain, comprises the following steps:

[0076] Step 1. Select high-quality wind-hole soil, kaolin, Tanggou soil, and black hairy soil. After selection, bleaching, and crushing, the raw materials are mixed with feldspar and sandstone according to 20 parts of wind-hole soil, 30 parts of kaolin, 37 parts of Tanggou soil, Mix 11 parts of black hairy soil, 0.5 parts of white feldspar, and ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
melting pointaaaaaaaaaa
boiling pointaaaaaaaaaa
Login to View More

Abstract

The invention provides a moon white glaze Ru porcelain and a preparation method thereof. The moon white glaze Ru porcelain comprises a green body and a glaze, and the green body comprises, by mass, 20-35 parts of Fengxue soil, 30-65 parts of kaolin, 20-55 parts of Tanggou soil, 10-20 parts of black raw soil, 0.5-2 parts of white feldspar and 1-2.5 parts of sandstones; and the glaze comprises, by mass, 50-65 parts of white feldspar, 10-20 parts of red feldspar, 10-20 parts of calcite, 5-10 parts of black stones, 5-12 parts of agate, 0.5-1.2 parts of sheep bone ash and 3-10 parts of wollastonite. The preparation method comprises the following steps: preparing the green body, preparing the glaze, and coating the prepared green body with the prepared glaze. The porcelain formed by calcining the green body and the glaze has the advantages of excellent porcelain quality, dense body surface, delicate and elegant property, delicate shape, moist color and strong surface impression. The glaze layer is smooth regardless of the thickness of the body, and the porcelain has the characteristics of air ventilation, non-permeability, good taste-keeping function, moderate heat preservation, and goodreflection of the color, smell and taste of food materials.

Description

technical field [0001] The invention relates to the technical field of ceramics, in particular to a moon white glazed porcelain and a preparation method thereof. Background technique [0002] Ru porcelain belongs to high-end works of art and collections. With the vigorous development of the cultural industry and the improvement of people's living standards, Ru porcelain has gradually developed from traditional antique products and handicrafts to daily-use porcelain, especially the tableware made of Ru porcelain. Tea sets are very popular among people. People's demand for Ru porcelain is becoming more and more diversified, and at the same time, the requirements for its quality are also getting higher and higher. [0003] The main characteristics of Ru porcelain moon white glaze are: the glaze color is white and blue, the glaze layer is even and thick, the glaze surface is moist, and the jade texture is strong. But the moon white glaze in the prior art market mostly adopts c...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B33/16C04B33/13C04B33/04C03C8/00C04B33/34C04B33/24C04B41/86
Inventor 李晓涓王晟鸣郗奎奎
Owner 王晟鸣
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com