Preparation method of recycled asphalt mixture

A technology of asphalt mixture and recycled asphalt, which is applied in the direction of sustainable waste treatment, solid waste management, climate sustainability, etc., can solve the problems of unfavorable asphalt precipitation, RAP aging, and reduce the performance of recycled asphalt mixture, so as to avoid secondary Secondary aging, short heating time, energy saving effect

Active Publication Date: 2021-11-23
YANGZHOU UNIV
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

In this radiation heating method, the heat transfer process is from the outside of the RAP to its inside (from the surface to the inside), which is not conducive to the precipitation of old asphalt adsorbed by the recycled material; and the heating time is as long as 2-4 hours, resulting in RAP Further aging reduces the performance of the corresponding recycled asphalt mixture,

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of recycled asphalt mixture
  • Preparation method of recycled asphalt mixture
  • Preparation method of recycled asphalt mixture

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0014] A method for preparing recycled asphalt mixture, comprising the following steps:

[0015] Step 1. Heat the new aggregate, asphalt, and mineral powder to 160-165°C by means of thermal radiation heating;

[0016] Step 2. Use microwave heating to heat the recycled asphalt mixture to 150-155°C;

[0017] Step 3. Dry-mix the recycled asphalt mixture for 90s first, then add the heated new aggregate, asphalt, mineral powder and microwave-heated recycled asphalt mixture in sequence, and mix for 90s for each material added.

[0018] Step 4. Microwave the final mixed recycled asphalt mixture again, using microwave for 30s, intermittent for 30s, controlling the temperature at 150-155°C, and microwave heating for 6-8 cycles.

[0019] In a further embodiment, the mass percentage of ferric iron tetroxide in the recycled asphalt mixture in step 2 is greater than 3%.

[0020] In a further embodiment, the recycled asphalt mixture in step 2 is all kinds of old asphalt pavement binders t...

Embodiment 1

[0025] Such as figure 1 , 2 As shown, different dosages (30%, 40%, 50%) of regenerated asphalt mixture specimens were prepared by traditional heating and the present invention for comparative study.

[0026] The composition and mass ratio of AC-13 recycled asphalt mixture (30% RAP) are: 65 parts of new aggregate, 30 parts of recycled asphalt mixture, 5 parts of mineral powder, and 4.78 parts of asphalt

[0027] The composition and mass ratio of AC-13 recycled asphalt mixture (40% RAP) synthetic mineral materials are: 55 parts of new aggregate, 40 parts of recycled asphalt mixture, 5 parts of mineral powder, and 4.42 parts of asphalt

[0028] The composition and mass ratio of AC-13 recycled asphalt mixture (50% RAP) synthetic mineral materials are: 45 parts of new aggregate, 50 parts of recycled asphalt mixture, 5 parts of mineral powder, and 4.29 parts of asphalt

[0029] All the above ratios can meet the design requirements of the ratio in "Technical Specifications for Cons...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
penetrationaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for preparing regenerated asphalt mixture, which adopts a thermal radiation heating method to heat new aggregate, asphalt, mineral powder and other components to 160-165°C; heat recycled asphalt mixture to 150-155°C ; Mix the heated new aggregate, asphalt, mineral powder, and microwave-heated asphalt mixture reclaimed material; microwave the recycled asphalt mixture after mixing, using microwave 30s, intermittent 30s, and the temperature is controlled at 150‑155 ° C, microwave heating for 6‑8 cycles, and the performance-enhanced recycled asphalt mixture was obtained. The invention uses microwaves to heat the RAP, has short heating time, saves a lot of energy, and can greatly improve the performance of the recycled asphalt mixture.

Description

technical field [0001] The invention belongs to road engineering technology, in particular to a method for preparing recycled asphalt mixture. Background technique [0002] At present, the recycling of RAP (waste and old asphalt mixture) is mainly applied to the surface layer of low-traffic roads and the cushion or subbase of high-grade roads with a certain amount of blending ratio. However, the aggregates recovered from the upper layer of asphalt are basically high-quality aggregates. The reason why they cannot be used in large quantities in the surface layer is that after mixing RAP, the old and new asphalt in the asphalt mixture cannot be fully integrated, resulting in the crack resistance of the asphalt pavement. , fatigue life and other related properties will have different degrees of decline. [0003] In the current RAP thermal regeneration process, the temperature of the mixture is raised to the temperature required for mixing and paving mainly through heat radiatio...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C04B26/26C04B40/00C04B18/16
CPCC04B26/26C04B40/0082C04B2111/0075C04B18/16C04B14/00C04B18/141Y02W30/91
Inventor 李波张晨吴正光张永健
Owner YANGZHOU UNIV