Plant granular aromatic bead and preparation method and application thereof
A technology of plant particles and fragrant beads, which is applied in the fields of application, food science, tobacco, etc., can solve the problems of easily damaged blades for cutting filter rods, loose combination with filter rod tow, and unfavorable smoking quality of cigarettes, so as to improve smoking Good quality, good fragrance-carrying performance, and high utilization rate
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0026] Example 1
[0027] Step 1: Weighing and mixing of raw materials: Weigh 3kg licorice powder, 2kg nano calcium carbonate, 3kg degummed hemp fiber powder, 1kg modified corn starch, 1kg water-soluble chitosan. Add the weighed raw materials into the cone mixer, turn on the mixer and mix for 60 minutes, and mix well to obtain a mixture;
[0028] Step 2: Wet material preparation: add the mixture to the stirred reactor, then add 6kg of hot water at 50°C with the quality of the mixture, and stir at 50°C for 2h;
[0029] Step 3: Particle molding: Use an extruder to extrude the wet material prepared in Step 3 into strip particles with a diameter of 4mm and a length of 4mm, and then transfer them to a circular granulator for rounding. The particle size is controlled within 2.5mm, get round particles;
[0030] Step 4: Drying: Dry the round particles obtained in Step 3, and control the moisture content of the dried particles at 2%;
[0031] Step 5: Grinding and sieving: Put the dry particles...
Example Embodiment
[0037] Example 2
[0038] Step 1: Weighing and mixing of raw materials: Weigh 4kg mint leaf powder, 1.5kg nano calcium carbonate, 2kg degummed hemp fiber powder, 1.5kg modified corn starch, 1kg water-soluble chitosan. Add the weighed raw materials into the cone mixer, turn on the mixer and mix for 60 minutes, and mix well to obtain a mixture;
[0039] Step 2: Wet material preparation: add the mixture to the stirred reactor, then add 8kg of hot water at 50°C with the quality of the mixture, and stir for 1.5h at 50°C;
[0040] Step 3: Particle forming: Use an extruder to extrude the wet material prepared in step 3 into strip particles with a diameter of 3mm and a length of 3mm, and then transfer them to a circular granulator for rounding. The particle size is controlled within 3.8mm, get round particles;
[0041] Step 4: Drying: Dry the round particles obtained in Step 3, and control the moisture content of the dried particles at 3%;
[0042] Step 5: Grinding and sieving: Put the dry pa...
Example Embodiment
[0048] Example 3
[0049] Step 1: Weighing and mixing of raw materials: Weigh 2kg licorice powder and 2kg angelica powder, 1kg nano calcium carbonate, 2.5kg degummed hemp fiber powder, 1.5kg corn modified starch, 1kg water-soluble chitosan. Add the weighed raw materials into the cone mixer, turn on the mixer and mix for 60 minutes, and mix well to obtain a mixture;
[0050] Step 2: Wet material preparation: add the mixture to the stirred reactor, then add 9kg of hot water at 50℃ with the mass of the mixture, and stir for 2.5h at 50℃;
[0051] Step 3: Particle molding: Use an extruder to extrude the wet material prepared in Step 3 into strip particles with a diameter of 4mm and a length of 4mm, and then transfer them to a circular granulator for rounding. The particle size is controlled within 2.5mm, get round particles;
[0052] Step 4: Drying: Dry the round particles obtained in Step 3, and control the moisture content of the dried particles at 3%;
[0053] Step 5: Grinding and sievi...
PUM
Property | Measurement | Unit |
---|---|---|
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Particle size | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap