Synthesis method and application of superabsorbent resin microspheres with antibacterial properties

A technology of super absorbent resin and synthesis method, which is used in absorbent pads, medical science, bandages, etc., can solve the problems of the maximum water absorption ratio and the water absorption rate and the water locking effect is difficult to balance and take into account, so as to avoid the rapid rise of the reaction temperature and the properties Uniform and efficient effect

Active Publication Date: 2019-09-24
HANGZHOU COCO HEALTHCARE PRODS +2
View PDF4 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] There are various types of polymer water-absorbent resins in the prior art, some of which have been successfully applied to the core of diapers, but they still have the following deficiencies: the maximum water absorption rate, water absorption rate, water-locking effect and avoiding the phenomenon of dough. Important elements are difficult to balance

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029] A method for synthesizing superabsorbent resin microspheres with antibacterial properties, the steps of the synthesis method are as follows:

[0030] Step S1: The magnetically ordered mesoporous carbon nanospheres are modified with hydrazine groups, and the conditions for the hydrazine group modification treatment are: add 1 g of magnetically ordered mesoporous carbon nanospheres to 80 ml of PBS buffer solution with pH 7.3, and add 10 mg of HBA , 10mg of EDC and 10mg of NHS, stirred and reacted for 6 hours in the dark, then magnetically separated, washed and dried. The particle size is 160-170nm, the average pore size is 4.2-4.4nm, and the magnetic Ms is greater than or equal to 9.0emu / g;

[0031] Step S2: Add a certain amount of magnetically ordered mesoporous carbon nanospheres and polymer dispersant after the treatment in step S1 to a certain amount of water, stir well, then vacuum and / or ultrasonic-assisted degassing treatment for 1 hour, add a certain amount Stir...

Embodiment 2

[0040] A method for synthesizing superabsorbent resin microspheres with antibacterial properties, the steps of the synthesis method are as follows:

[0041] Step S1: The magnetically ordered mesoporous carbon nanospheres are modified with hydrazine groups, and the conditions for the hydrazine group modification treatment are: 2 g of magnetically ordered mesoporous carbon nanospheres are added to 100 ml of PBS buffer solution with pH 7.5, and 20 mg of HBA is added. , 20mg of EDC and 20mg of NHS, stirred and reacted for 8 hours in the dark, then magnetically separated, washed and dried. The particle size is 170-180nm, the average pore size is 4.6-4.8nm, and its magnetic Ms is greater than or equal to 9.0emu / g;

[0042] Step S2: Add a certain amount of magnetically ordered mesoporous carbon nanospheres and polymer dispersant treated in step S1 to a certain amount of water, stir well, then vacuum and / or ultrasonic-assisted degassing treatment for 2 hours, add a certain amount St...

Embodiment 3

[0052] A method for synthesizing superabsorbent resin microspheres with antibacterial properties, the steps of the synthesis method are as follows:

[0053] Step S1: The magnetically ordered mesoporous carbon nanospheres are modified with hydrazine groups. The conditions for the hydrazine group modification treatment are: 1.5 g of magnetically ordered mesoporous carbon nanospheres are added to 90 ml of PBS buffer solution with pH 7.4, and 15 mg of HBA, 15mg of EDC and 15mg of NHS, stirred and reacted for 7 hours in the dark, then magnetically separated, washed and dried. The particle size is 170-180nm, the average pore size is 4.2-4.5nm, and the magnetic Ms is greater than or equal to 9.0 emu / g;

[0054] Step S2: Add a certain amount of magnetically ordered mesoporous carbon nanospheres and polymer dispersant treated in step S1 to a certain amount of water, stir well, then vacuum and / or ultrasonic-assisted degassing treatment for 1.5 hours, add a certain amount of Stir a larg...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
pore sizeaaaaaaaaaa
particle diameteraaaaaaaaaa
Login to view more

Abstract

The invention relates to a synthesis method and application of superabsorbent resin microspheres with antibacterial properties. The synthesis method comprises the following steps: (1) adding a certain amount of magnetic ordered mesoporous carbon nanospheres and a polymer dispersing agent to a certain amount of water, performing full and even stirring, then performing vacuum and/or ultrasonic-assisted degassing treatment for 1-2 h, adding a certain amount of acrylic acid, performing even stirring, and controlling the temperature at 35-45 DEG C; (2) adding a certain amount of sodium hydroxide to the system obtained in the step (1) while stirring, and controlling the temperature at 65-75 DEG C in the reaction process; (3) adding a certain amount of a composite crosslinking agent and an initiator, and controlling the temperature at 80-90 DEG C for a reaction for 2-3 hours so as to form a semi-finished product superabsorbent resin colloid, wherein the composite crosslinking agent is a mixture of NMBA and PEGDA; and (4) putting the superabsorbent resin colloid obtained in the step (3) in a certain amount of a solvent, performing rinsing for 1-3 times, adding a certain amount of a nano-silver antibacterial agent, performing drying until the moisture content at less than 3%, performing pulverization to a certain particle size, and performing magnetic separation so as to obtain the superabsorbent resin finished product.

Description

technical field [0001] The invention relates to a synthesis method and an application thereof of superabsorbent resin microspheres with antibacterial properties, and belongs to the technical field of polymer resin synthesis. Background technique [0002] Superabsorbent resin is widely used in daily life and medical and health fields because of its large water absorption multiple and high water retention rate. Superabsorbent polymers can be divided into three categories according to their raw material sources: starch-based, cellulose-based, and synthetic polymer-based. Starch raw materials have a wide range of sources, many types, and large yields. However, the reaction raw materials are very viscous when hydrolyzed, and the operation and control are very difficult. Natural cellulose has a wide range of sources, and there are many hydroxyl groups on its molecule that can be compatible with water. Furthermore, the fibrous substance has many capillaries and a large surface are...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08F220/06C08F222/38C08F222/20C08F2/44C08K9/04C08K7/24C08K9/12C08K3/08A61L15/24A61L15/18A61L15/42A61L15/44A61L15/60A61L15/46
CPCA61L15/18A61L15/24A61L15/425A61L15/44A61L15/46A61L15/60A61L2300/104A61L2300/404C08F2/44C08F220/06C08K3/08C08K7/24C08K9/04C08K9/12C08K2003/0806C08K2201/011C08L33/02
Inventor 唐伟金利伟王旭张春娥孔宋华陈锴周黎峰鲍益平裘向阳武晓莺
Owner HANGZHOU COCO HEALTHCARE PRODS
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology