A kind of integrated automobile window lifter guide rail production material and its preparation method and application

A technology of automotive glass and lifter, which is applied in the direction of textiles and papermaking, papermaking, non-woven fabrics, etc., to achieve the effect of increasing the contact area, reducing the contact distance, and improving the effect of impregnation

Active Publication Date: 2020-08-28
WUHU MOTIONTEC AUTOMOTIVE
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The technical problem to be solved by the present invention: Aiming at the technical problems existing in the preparation of long glass fiber reinforced polypropylene (LGF-PP) pellets and the subsequent injection molding process in the current LFT-G process, the present invention provides an integrated automotive window regulator Guide rail manufacturing material and preparation method thereof solve the above problems

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of integrated automobile window lifter guide rail production material and its preparation method and application
  • A kind of integrated automobile window lifter guide rail production material and its preparation method and application
  • A kind of integrated automobile window lifter guide rail production material and its preparation method and application

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0026] Embodiment 1: prepare long glass fiber reinforced polypropylene (LGF-PP) material as follows:

[0027] 1. Preparation of raw materials

[0028] Long glass fiber (LGF40) specific gravity 1.22g / cm 3 , monofilament diameter 10μm, pure polypropylene fiber specific gravity 0.92g / cm 3 , single filament diameter 11μm, the weight of the pure polypropylene filter is 180g / m 2 The pure polypropylene filter mesh is 50 mesh, and the surface of the long glass fiber has been treated with 10% silane coupling agent kh550 to improve the compatibility between the long glass fiber and the polypropylene substrate.

[0029] 2. Preparation of materials for the guide rail of the integrated automobile window lifter:

[0030] (1) The long glass fiber and pure polypropylene fiber after fiber spreading are respectively cut into 80mm fiber segments, and the long glass fiber and pure polypropylene fiber are weighed according to the long glass fiber content of 60wt%, and placed on the comb after m...

Embodiment 2

[0036] Embodiment 2: prepare long glass fiber reinforced polypropylene (LGF-PP) material as follows:

[0037] 1. Preparation of raw materials

[0038] Long glass fiber specific gravity (LGF20) 1.18g / cm 3 , monofilament diameter 11μm, pure polypropylene fiber specific gravity 0.90g / cm 3 , single filament diameter 11μm, the weight of the pure polypropylene filter is 227g / m 2 The pure polypropylene filter mesh is 100 mesh, and the surface of the long glass fiber has been treated with 10% silane coupling agent kh550 to improve the compatibility between the long glass fiber and the polypropylene substrate.

[0039] 2. Preparation of materials for the guide rail of the integrated automobile window lifter:

[0040] (1) The long glass fiber and pure polypropylene fiber after fiber spreading are respectively cut into 120mm fiber segments, and the long glass fiber and pure polypropylene fiber are weighed according to the long glass fiber content of 80wt%, and placed on the comb needl...

Embodiment 3

[0046] Embodiment 3: prepare long glass fiber reinforced polypropylene (LGF-PP) material as follows:

[0047] 1. Preparation of raw materials

[0048] Long glass fiber (LGF40) specific gravity 1.22g / cm 3 , monofilament diameter 8μm, pure polypropylene fiber specific gravity 0.92g / cm 3 , single filament diameter 11μm, the weight of the pure polypropylene filter is 200g / m 2 The pure polypropylene filter mesh is 70 mesh, and the surface of the long glass fiber has been treated with 10% silane coupling agent kh550 to improve the compatibility between the long glass fiber and the polypropylene substrate.

[0049] 2. Preparation of materials for the guide rail of the integrated automobile window lifter:

[0050] (1) The long glass fiber and pure polypropylene fiber after fiber spreading are respectively cut into 100mm fiber segments, and the long glass fiber and pure polypropylene fiber are weighed according to the long glass fiber content of 70wt%, and placed on the comb needle ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Basis weightaaaaaaaaaa
Basis weightaaaaaaaaaa
diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses an integrated manufacturing material for an automotive glass lifter guide rail and a manufacturing method of the material. The material is prepared from 40-55 wt% of long glass fibers and the balance pure polypropylene. The integrated manufacturing material for the automotive glass lifter guide rail is in a columnar particle shape, the interiors of columnar particles are of Swiss-roll-shaped lamination structures, the lamination structures are formed by alternately rolling mixing blanketing layers and pure polypropylene layers, and the mixing blanketing layers are formed in the mode that after the long glass fibers and pure polypropylene fibers are mixed, wet-method deposition is conducted. The prepared particle material can quickly form a stable three-dimensional space structure in the injection molding process and is not easily influenced by the rotation speed of a screw of an injection molding machine, the long glass fibers are not easily broken, the mechanical property of a finished product is obviously improved, through the mixing blanketing layers and the lamination structures, the difficulty of an impregnation technology can be lowered, and the impregnation effect is improved. Through a needling technology, the stability of the mixing blanketing layers in the processing process can be obviously improved.

Description

technical field [0001] The invention relates to the field of long glass fiber reinforced polypropylene materials, in particular to a material for making guide rails of an integrated automobile glass lifter and a preparation method thereof. Background technique [0002] At present, automobile parts have been prepared with a large number of different lightweight materials, and thermoplastic composite materials such as PP plastics have become the main body of lightweight materials. Long glass fiber reinforced thermoplastic composite materials are easy to process and shape, high in strength and small in weight. The advantages of wear resistance and low cost are becoming the key areas of automobile lightweight research. [0003] There are four main types of long glass fiber reinforced thermoplastic composite (LFT) molding processes, namely LFT-D, LFT-E, LFT-G, LFT-S, LFT-D full name long / continuous glass fiber reinforced hybrid direct molding Process, this process uses a special...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): D04H1/4218D04H1/4291D04H1/46D04H1/498D21F13/00
CPCD04H1/4218D04H1/4291D04H1/46D04H1/498D21F13/00
Inventor 周玉成许成刚吴鹏飞王康江辉
Owner WUHU MOTIONTEC AUTOMOTIVE
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap