Transparent conductive film structure with optical characteristic regulation

A technology of transparent conductive film, optical properties, applied in the direction of conductive layer on insulating carrier, etc.

Inactive Publication Date: 2019-10-08
INTERFACE TECH CHENGDU CO LTD +2
View PDF4 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] It can be seen that there are still many deficiencies in the above-mentioned customary items, which are not a good designer and need to be improved urgently.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Transparent conductive film structure with optical characteristic regulation
  • Transparent conductive film structure with optical characteristic regulation
  • Transparent conductive film structure with optical characteristic regulation

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0019] The present invention relates to a "transparent conductive film structure with adjustable optical properties", please refer to image 3 As shown, the transparent conductive film structure with adjustable optical properties of the present invention mainly includes: a substrate 10 , a nano conductive material 20 and a nano particle 30 .

[0020] Wherein, the nano conductive material 20 is evenly distributed on the substrate 10 by coating.

[0021] The particle size of the nanoparticles 30 is between 1nm and 20nm, the nanoparticles 30 are evenly distributed on the substrate 10 by coating, and the space ratio occupied by the nanoparticles 30 on the substrate 10 is 1% to 20nm. 25%.

[0022] With the composition of the above components, the nano conductive material 20 and the nano particles 30 are evenly mixed on the substrate 10 to form a conductive film 1 with an adjustable refractive index.

[0023] In this way, by adding appropriate nanoparticles on the conductive layer...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a transparent conductive film structure with optical characteristic regulation. The transparent conductive film structure comprises a substrate, a nano conductive material andnanoparticles. The nano conductive material is uniformly coated on the substrate. The particle size of the nanoparticles is within 1-20nm. The nanoparticles are uniformly coated on the substrate andthe space ratio of the nanoparticles on the substrate is 1%-25%. Therefore, a conductive film with the adjustable refractive index is formed by uniformly mixing the nano conductive material and the nanoparticles on the substrate.

Description

technical field [0001] The present invention is a transparent conductive film structure with optical properties control, especially a structure on a transparent conductive film, adding appropriate nano particles in the conductive layer to change the equivalent refractive index of the conductive layer. Background technique [0002] Press, in recent years, 3C products generally have a touch function, and the touch function makes the distance between electronic products and users closer. For touch products, if they are paired with display products, the touch film will have higher requirements on optical performance. Therefore, how to reduce the reflectivity of the touch film and improve the transmittance will be an important technical focus. [0003] see figure 1 , 2 As shown, the general light is irradiated on the film layer, and the effect of light can be divided into three parts: penetration, reflection and absorption, such as figure 1 shown. The absorption rate (A) of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): H01B5/14
CPCH01B5/14
Inventor 范佳铭张景翔
Owner INTERFACE TECH CHENGDU CO LTD