Intumescent fireproof coating and preparation method thereof

Abstract

The disclosure provides an intumescent fireproof coating, comprising: polyorganosiloxane emulsion, base resin emulsion, carbonizing agent, flame retardant foaming agent, nitrogen-containing foaming agent, pre-foaming agent, expansion agent, Defoamer, wetting and dispersing agent, film-forming aid and filler, and in the fireproof coating, the mass percentage of polyorganosiloxane emulsion is 3% to 10%; the mass percentage of base resin emulsion is 10% to 17% ; The mass percentage of the carbonizing agent is 11% to 18%; the mass percentage of the flame retardant foaming agent is 20% to 30%; the mass percentage of the nitrogen-containing foaming agent is 10% to 20%; The percentage is 0.3% to 0.6%; the mass percentage of expansion agent is not more than 5%; the mass percentage of defoamer is 0.2% to 0.4%; the mass percentage of wetting and dispersing agent is 0.5% to 1.5%; The percentage is 0.1% to 0.5%; the mass percentage of filler is 10% to 25%. According to the present disclosure, it is possible to provide a fire-resistant paint capable of extending the fire-resistant time and improving the fire-proof performance.

Description

technical field [0001] The present disclosure particularly relates to an intumescent fireproof coating and a preparation method thereof. Background technique [0002] In the construction industry, by coating the surface of flammable materials in buildings with fire-resistant coatings, the fire resistance of flammable materials can be effectively improved and the spread of flames can be slowed down. This type of fire retardant coating is sometimes also called flame retardant coating. In particular, the mechanical strength and mechanical properties of commonly used building materials such as steel will decrease with the increase of temperature, and they will easily lose their supporting ability, resulting in the collapse of the building. Therefore, fire protection for such materials can effectively prevent such materials from rapidly heating up in a fire and reduce their strength, and avoid the loss of supporting capacity and cause the building to collapse. [0003] Proposed...

AI Technical Summary

Problems solved by technology

[0004] However, although the fireproof coatings disclosed in the above-mentioned patent documents have improved the fireproof performance of steel structures, when a fire actually breaks out, the foam carbonized layer formed when such fireproof coatings burn has uneven foaming and is not compatible with the steel base. The shortcomings such as poor adhesion of the material lead to a short fire-resistant time and poor fire-proof performance of the fire-resistant coating.

Images