Aqueous ultrathin expansion-type fireproof coating for steel structure and preparation method thereof

A kind of technology of fireproof coating and expansion type, applied in the direction of fireproof coating, epoxy resin coating, coating, etc., can solve the problems of non-uniform foaming of carbonized layer, smoke safety problem, poor adhesion of steel substrate, etc., to achieve emulsion Comprehensive performance improvement, improved fire performance, and the effect of reducing methanol

Active Publication Date: 2014-11-05
沈阳泰丰化工有限公司
View PDF4 Cites 45 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] At present, most water-based steel structure fireproof coatings have many shortcomings, such as non-uniform foaming of the carbonized layer formed during combustion, poor strength, and adhesion to the steel substrate. Poor focus, there are smoke safety problems, poor weather resistance and other shortcomings

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Aqueous ultrathin expansion-type fireproof coating for steel structure and preparation method thereof
  • Aqueous ultrathin expansion-type fireproof coating for steel structure and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0043] Prepare steel structure fireproof coating of the present invention according to the composition and mass percentage listed below:

[0044] Modified water-based epoxy emulsion 20

[0045] Hardener 3

[0046] Silicone acrylic emulsion 8

[0047] Ammonium polyphosphate 13

[0048] Melamine 7

[0049] Pentaerythritol 9

[0050] Modified aluminum hydroxide 4

[0051] Modified Zinc Oxide 2

[0052] Zinc borate 3

[0053] Titanium dioxide 3

[0054] Wollastonite powder 3

[0055] Expanded vermiculite 2

[0056] Various additives 5

[0057] water 18

[0058] The preparation process of the fireproof coating of the present invention is as follows: Weigh the required amount of each component, add water, some additives, ammonium polyphosphate, melamine, pentaerythritol, modified aluminum hydroxide, modified zinc oxide, Zinc borate, titanium dioxide, wollastonite powder and expanded vermiculite are stirred at a speed of 1000r / min for 30 mi...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thermal decomposition temperatureaaaaaaaaaa
thermal decomposition temperatureaaaaaaaaaa
degree of polymerizationaaaaaaaaaa
Login to view more

Abstract

The invention discloses an aqueous ultrathin expansion-type fireproof coating for a steel structure and a preparation method thereof, and belongs to the technical field of fireproof coatings. The aqueous ultrathin expansion-type fireproof coating comprises, by mass, 10-35 parts of a modified aqueous epoxy emulsion, 1-8 parts of a curing agent, 5-15 parts of a styrene-acrylic emulsion or a silicone-acrylic emulsion, 10-20 parts of ammonium polyphosphate, 6-12 parts of melamine, 8-16 parts of pentaerythritol, 5-15 parts of a fire retardant, 5-15 parts of a pigment and a filling material, 2-8 parts of an assistant and 15-35 parts of water. The aqueous ultrathin expansion-type fireproof coating has the characteristics of low raw material cost, simple preparation process and environmental friendliness.

Description

technical field [0001] The invention belongs to the technical field of fireproof coatings, in particular to a water-based ultra-thin intumescent fireproof coating for steel structures and a preparation method thereof. Background technique [0002] As a type of building, steel structure is widely used for its advantages of light weight, high strength, good plasticity, and short construction period, especially in long-span structures and high-rise buildings. However, steel structures have poor fire resistance. When the temperature reaches 600°C, the steel structure will lose almost all its strength. Once a fire occurs, the steel structure will lose its bearing capacity, which will seriously endanger people's lives and property safety. Therefore, it is necessary to protect the steel structure from fire. The method widely used at present is to coat the surface of the steel structure with a steel structure fireproof coating. [0003] Fire retardant coatings for steel structures ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D163/02C09D125/14C09D133/04C09D7/12C09D5/18C09C3/12
Inventor 张千峰叶云飞张振海马骏
Owner 沈阳泰丰化工有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap