A kind of method for preparing calcium ferrite from titanium gypsum tailings

A technology of titanium gypsum and calcium ferrite, applied in chemical instruments and methods, iron compounds, improvement of process efficiency, etc., can solve the problems of high moisture content, difficult drying, and low added value, etc.

Active Publication Date: 2021-11-05
SOUTHWEAT UNIV OF SCI & TECH
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] Since titanium gypsum contains iron hydroxide, it has high moisture content, is not easy to dry, and has low added value.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of method for preparing calcium ferrite from titanium gypsum tailings
  • A kind of method for preparing calcium ferrite from titanium gypsum tailings

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0028] The present invention will be described in further detail below in conjunction with specific examples.

[0029] (1) Add carbonate to the titanium white wastewater, filter after the reaction, add surfactant to the filtrate, add calcium source for neutralization to obtain titanium gypsum slurry, and physically separate to obtain titanium gypsum tailings. The formulations of raw carbonate, surfactant and calcium source are shown in Table 1.

[0030] Table 1

[0031]

[0032] (2) After the titanogypsum tailings are aged, add binder, catalyst, sintering aid and reducing agent, mix evenly, form balls, reduce and roast to obtain calcium ferrite. The raw material formula is shown in Table 2.

[0033] Table 2

[0034]

[0035] It can be concluded from Examples 1 to 16 that the content of harmful elements in the obtained calcium ferrite meets the quality requirements of steelmaking raw materials, and can be used as a slagging agent for steelmaking.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

This patent discloses a method for preparing calcium ferrite from titanium gypsum tailings. Add carbonate to titanium white wastewater, filter after the reaction, add surfactant to the filtrate, add calcium source for neutralization to obtain titanium gypsum slurry body, physical separation to obtain titanogypsum tailings; after aging, the titanogypsum tailings are added with binder, catalyst, sintering aid and reducing agent, mixed evenly, formed into balls, reduced and roasted to obtain calcium ferrite. Compared with the existing technical solutions, the method has the characteristics of low production cost, high production efficiency and good product quality.

Description

technical field [0001] The invention relates to the field of resource utilization of industrial waste residues, in particular to high-quality utilization of titanium gypsum. In addition, this patent also relates to the treatment of industrial wastewater, specifically to the treatment of iron-containing sulfuric acid wastewater. Background technique [0002] According to the present invention, my country is a country with large titanium resources in the world, and the mineral type is mainly ilmenite. According to the data released by the United States Geological Survey (USGS) in 2015, my country's ilmenite reserves are 200 million tons, accounting for 28% of the global reserves, ranking first in the world . There are 45 primary ilmenite deposits in China, mainly distributed in Panxi, Sichuan and Chengde, Hebei. According to the joint statistics of Titanium, Zirconium and Hafnium Branch of China Nonferrous Metals Industry Association and Panzhihua Iron and Steel Titanium Indu...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01G49/00C21C7/076
CPCC01G49/00C21C7/076Y02P10/20
Inventor 谭宏斌马小玲董发勤李玉香王进明邓秋林王进王军霞李芳贺小春
Owner SOUTHWEAT UNIV OF SCI & TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com