High-weather-resistance high-environmental-friendliness flame-retardant polycarbonate alloy material based on transesterification control, and preparation method thereof
A technology of flame-retardant polycarbonate and alloy materials, which is applied in the field of polymer materials, can solve problems such as the difficulty in effectively controlling transesterification reactions, the reduction of mechanical performance indicators of alloy materials, and the evaluation and testing of long-term weather resistance of materials that are not involved. The effects of excellent UV resistance, good rigidity and impact resistance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0042] Example 1
[0043] Weigh the virgin PC resin, virgin PBT resin, multi-block copolymer toughener, and weather resistance stabilizer according to the data of Example 1 shown in Table 1, and mix them evenly to obtain mixed raw material A, which is weighed according to the stated weight percentage Take recycled PET resin, organic phosphorus flame retardant, and transesterification reaction control agent to obtain mixed raw material B.
[0044] After the above-mentioned mixed raw materials A and B are fully dried, the mixed raw material A is placed in the main feeding bin of a twin-screw extruder that is tightly meshed and rotating in the same direction, and is added to the barrel of the extruder through the main feeding screw ; Place the mixed raw material B in the lateral feeding bin, and add it to the extruder barrel by the lateral feeding screw. The diameter of the screw extruder is 36mm, the length-to-diameter ratio L / D is 44, and the temperature of each zone of the main ba...
Example Embodiment
[0047] Example 2
[0048] Weigh the virgin PC resin, virgin PBT resin, multi-block copolymer toughener, and weather resistance stabilizer according to the data of Example 2 shown in Table 1, and mix them evenly to obtain mixed raw material A, which is weighed according to the stated weight percentage Take recycled PET resin, organic phosphorus flame retardant, and transesterification reaction control agent to obtain mixed raw material B.
[0049] After the above-mentioned mixed raw materials A and B are fully dried, the mixed raw material A is placed in the main feeding bin of a twin-screw extruder that is tightly meshed and rotating in the same direction, and is added to the barrel of the extruder through the main feeding screw ; Place the mixed raw material B in the lateral feeding bin, and add it to the extruder barrel by the lateral feeding screw. The diameter of the screw extruder is 36mm, the length-to-diameter ratio L / D is 44, and the temperature of each zone of the main ba...
Example Embodiment
[0050] Example 3
[0051] Weigh the virgin PC resin, virgin PBT resin, multi-block copolymer toughener, and weather resistance stabilizer according to the data of Example 3 shown in Table 1, and mix them evenly to obtain mixed raw material A, which is weighed according to the stated weight percentage Take recycled PET resin, organic phosphorus flame retardant, and transesterification reaction control agent to obtain mixed raw material B.
[0052] After the above-mentioned mixed raw materials A and B are fully dried, the mixed raw material A is placed in the main feeding bin of a twin-screw extruder that is tightly meshed and rotating in the same direction, and is added to the barrel of the extruder through the main feeding screw ; Place the mixed raw material B in the lateral feeding bin, and add it to the extruder barrel by the lateral feeding screw. The diameter of the screw extruder is 36mm, the length-to-diameter ratio L / D is 44, and the temperature of each zone of the main ba...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap