A potassium sodium niobate-based lead-free piezoelectric ceramic and its manufacturing process and application
A potassium-sodium niobate-based, lead-free piezoelectric technology, applied in the manufacture/assembly of piezoelectric/electrostrictive devices, piezoelectric/electrostrictive/magnetostrictive devices, circuits, etc., can solve the problem of harming human health and the ecological environment, unsatisfactory sound effects, etc., to reduce damage to human health and the environment, good sound effects, and low driving voltage
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0034] A kind of potassium niobate base lead-free piezoelectric ceramics, chemical composition is: 0.85 (K 0.5 Na 0.45 Li 0.05 )NbO 3 +0.15(Bi 0.5 Ag 0.5 )TiO 3 , its manufacturing process includes the following steps:
[0035] (1) Dehydration of raw materials: put potassium carbonate, sodium carbonate, niobium pentoxide, lithium carbonate, bismuth trioxide, titanium dioxide and silver oxide into a petri dish, place in an oven, keep warm at 150°C for 6 hours, and remove raw materials moisture in
[0036] (2) Mixing: Proportioning raw materials according to the chemical composition, dispersing in absolute ethanol, mixing by ball milling, the ball milling speed is 600rpm, and the ball milling time is 24h, after mixing evenly, dry, pulverize and sieve to make dry powder;
[0037] (3) Pre-calcination: put the dry powder in a box furnace and continuously heat up to 950°C, keep it warm for 12 hours, cool down to room temperature, crush and sieve to obtain pre-calcined powder;...
PUM
Property | Measurement | Unit |
---|---|---|
piezoelectric charge coefficient | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com