Environment-friendly composite flocculus and preparation method thereof

An environmentally friendly, wadding technology, which is applied in the fields of fiber chemical characteristics, non-woven fabrics, textiles and papermaking, etc., can solve the problems that ordinary wadding cannot meet the requirements of home, and cannot be warmed and adjusted.

Inactive Publication Date: 2020-01-10
海门市同泰工艺品有限公司
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] The existing flakes are used as winter clothing fillings, which can only play a role in heat insulation and warmth, but cannot adjust the temperature, let alone intelligently adjust the temperature and humidity simultaneously, and do not have the effects of antibacterial, anti-mite, and flame retardant. , and poor skin affinity
Ordinary flakes can no longer meet people's growing living and home requirements

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Environment-friendly composite flocculus and preparation method thereof
  • Environment-friendly composite flocculus and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] An environment-friendly composite wadding is formed by mixing temperature-regulating fibers and bamboo pulp fibers, and the mixing ratio of the temperature-regulating fibers and bamboo pulp fibers is 20%:80%.

[0022] A kind of preparation method of environment-friendly composite wadding, complete the preparation method of environment-friendly composite wadding through the steps of preparation of bamboo pulp fiber, preparation of fiber net, thermal bonding process and post-treatment process, concrete steps are as follows:

[0023] (1) Preparation of bamboo pulp fiber: Mix the pulverized bamboo pulp and ionic liquid evenly, dissolve at a temperature of 55°C for 14 hours to form a uniform and stable spinning solution with a total solid content of 5%, and then pass through the wet spinning method Carry out spinning, plastic stretching, washing, oiling, and drying to complete the preparation of bamboo pulp fibers; the ionic liquid is composed of anions and cations, the catio...

Embodiment 2

[0028] An environment-friendly composite wadding is formed by mixing temperature-regulating fibers and bamboo pulp fibers, and the mixing ratio of the temperature-regulating fibers and bamboo pulp fibers is 50%:50%.

[0029] A kind of preparation method of environment-friendly composite wadding, complete the preparation method of environment-friendly composite wadding through the steps of preparation of bamboo pulp fiber, preparation of fiber net, thermal bonding process and post-treatment process, concrete steps are as follows:

[0030] (1) Preparation of bamboo pulp fiber: Mix the pulverized bamboo pulp and ionic liquid evenly, dissolve at 120°C for 22 hours to form a uniform and stable spinning solution with a total solid content of 15%, and then pass through the wet spinning method Carry out spinning, plastic stretching, washing, oiling, and drying to complete the preparation of bamboo pulp fibers; the ionic liquid is composed of anions and cations, the cations are alkyl qu...

Embodiment 3

[0035] An environment-friendly composite wadding is formed by mixing temperature-regulating fibers and bamboo pulp fibers, and the mixing ratio of the temperature-regulating fibers and bamboo pulp fibers is 35%:65%.

[0036] A kind of preparation method of environment-friendly composite wadding, complete the preparation method of environment-friendly composite wadding through the steps of preparation of bamboo pulp fiber, preparation of fiber net, thermal bonding process and post-treatment process, concrete steps are as follows:

[0037] (1) Preparation of bamboo pulp fiber: Mix the pulverized bamboo pulp and ionic liquid evenly, dissolve at 85°C for 18 hours to form a uniform and stable spinning solution with a total solid content of 10%, and then pass through the wet spinning method Carry out spinning, plastic stretching, washing, oiling, and drying to complete the preparation of bamboo pulp fibers; the ionic liquid is composed of anions and cations, the cations are alkyl qua...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Needling densityaaaaaaaaaa
Login to View More

Abstract

The invention discloses an environment-friendly composite flocculus and a preparation method thereof. The environment-friendly composite flocculus is formed by mixing temperature adjusting fibers withbamboo pulp fibers, wherein the mixing ratio of the temperature adjusting fibers to the bamboo pulp fibers is (20-50%): (50-80%), preparation of the environment-friendly composite flocculus is finished through the steps of preparation of the bamboo pulp fibers, preparation of fiber webs, a thermal bonding process and a post-treatment process; the temperature adjusting fibers and the bamboo pulp fibers are mixed to prepare the composite flocculus, effects of the temperature adjusting fibers and the bamboo pulp fibers are achieved, the prepared flocculus has effects of inhibiting bacteria, preventing mites, ventilating and dehumidifying, and is environment-friendly, the temperature-adjusting fibers can effectively adjust the temperature and the humidity, and the temperature is controlled tobe 28-35 DEG C.

Description

technical field [0001] The invention relates to the technical field of flakes, in particular to an environment-friendly composite flake and a preparation method thereof. Background technique [0002] Flock is a filling material widely used in the world and at home. It is a kind of flaky and loose filling material. It has been widely used especially in the textile field and has entered thousands of households. Compared with the traditional glued cotton batting, the non-glued cotton batting reduces the use of adhesives (especially aldehyde adhesives) in the manufacturing process, increases the bulkiness, and improves the problem of poor warmth retention. [0003] As one of the non-woven fabrics, non-adhesive cotton batting is a high-grade material for quilts, clothing, plush toy padding, warmth retention, sound absorption, and filter materials. It has good air permeability, good warmth retention, light weight, and resilience. Strong, anti-aging, washable, no mildew and so on....

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
IPC IPC(8): D04H1/425D04H1/485D04H1/4382D01F2/00
CPCD01F2/00D04H1/425D04H1/4382D04H1/485
Inventor 邱桐
Owner 海门市同泰工艺品有限公司