Method for making high carbon chromium bearing steel

A technology of high carbon chromium bearing steel and molten steel, applied in the field of steel manufacturing

Active Publication Date: 2020-11-27
BAOSTEEL SPECIAL STEEL SHAOGUAN CO LTD
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Based on the above-mentioned deficiencies, the present application provides a method for producing high-carbon chromium bearing steel, to partially or completely improve, or even solve the problem of how to optimize the process for bearing steel with specific components and specific cross-sectional specifications, low-cost, high-efficiency The problem of refining carbide band structure

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for making high carbon chromium bearing steel
  • Method for making high carbon chromium bearing steel
  • Method for making high carbon chromium bearing steel

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0065] The composition of high carbon chromium bearing steel is as follows. C (carbon): 1.01%; Si (silicon): 0.24%; Mn (manganese): 0.35%; P (phosphorus): 0.012%; S (sulfur): 0.002%; Cu (copper): 0.02%; Ni( Nickel): 0.04%; Cr (chromium): 1.48%; Ti (titanium): 0.0013%; O (oxygen): 0.0006%, and the balance is iron and unavoidable impurities.

[0066] Its production method is as follows:

[0067] 1. Continuous casting process.

[0068] Adopt constant temperature (1474°C-1478°C) and constant casting speed control, the superheat of molten steel is controlled at 20 to 24°C, the casting speed is constant at 0.85m / min, and the mold electromagnetic stirring (M-EMS) parameter is controlled at 300A / 2.5Hz. The terminal stirring electromagnetic stirring (F-EMS) parameter is 400A / 5.0Hz, and the specific water volume is 0.24L / Kg.

[0069] At the same time, the end soft reduction process is adopted, and the total reduction amount of the solidification end soft reduction is set to 14 mm acc...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to a method for manufacturing high carbon chromium bearing steel, and belongs to the field of steel manufacturing. The method comprises the following steps that electromagnetic stirring at the head end and electromagnetic stirring at the tail end are separately carried out in the process of molten steel crystallization, the total amount of reduction in the soft reduction zoneis controlled at the tail end of molten steel solidification, then, a slab is heated in a heating furnace, the temperature of the core and surface of the slab is homogenized, so that a segregation structure in the slab is effectively diffused, and the slab is subjected to be rolled directly after being discharged from the furnace. In the example, the condensation process of the molten steel, theheating process of the slab in the heating furnace and the rolling process can be selectively adjusted, so that the cold working performance and hot working performance of the obtained steel are improved and the fatigue life of the bearing is also prolonged.

Description

technical field [0001] The present application relates to the field of steel manufacturing, in particular, to a method for producing high-carbon chromium bearing steel. Background technique [0002] The slab of high-carbon chromium bearing steel will undergo crystallization segregation when it is cooled and solidified, and it will extend along the rolling direction to form carbide-rich bands during hot rolling deformation. These carbide-rich bands are called carbide bands. The presence of carbide bands will directly affect the cold and hot workability of steel, thereby reducing the fatigue life of bearings. [0003] For the problem of carbide strips, at present, the occurrence of the above problems is mainly suppressed by high-temperature diffusion treatment of the billet. Specifically, the carbide band shape is improved by prolonging the holding time of the high temperature section. This method can improve the banding quality, but it cannot stably control the carbide ban...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C38/02C22C38/04C22C38/42C22C38/50B22D11/115B22D11/16C21D7/13
CPCB22D11/115B22D11/16C21D7/13C22C38/002C22C38/02C22C38/04C22C38/42C22C38/50
Inventor 胡昭锋邓湘斌刘年富冯杰斌黄铸铭张正波钟凡叶德新
Owner BAOSTEEL SPECIAL STEEL SHAOGUAN CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com