Concrete interlocking block and production process thereof
A production process and technology of interlocking blocks, which are applied in the direction of manufacturing tools, paving surfaces paved with prefabricated blocks, supply devices, etc. The effect of high efficiency, convenient operation and high promotion value
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0022] The invention provides a concrete interlocking block, which is made of the following raw materials by weight:
[0023] Coarse aggregate 49, fine aggregate 22, cement 16 and appropriate amount of water.
[0024] Among them, the coarse aggregate is gravel, and the particle size of the coarse aggregate is not greater than 10mm, so as to avoid the exposed or sunken surface of the interlocking block; the fine aggregate is river sand, and the particle size of the fine aggregate is 2~5mm, so as to avoid The surface is honeycomb pitted surface, the cement is ordinary Portland cement P.O42.5, the cement strength is high, the amount of cement used is less under the same coarse aggregate and fine aggregate materials, and the coarse aggregate is oval crushed with smooth surface. Stone and fine aggregate are fine and well-matched river sand, which can reduce the amount of cement used and increase the compressive strength of the interlocking blocks.
[0025] see figure 1 , a concre...
Embodiment 2
[0033] The invention provides a concrete interlocking block, which is made of the following raw materials by weight:
[0034] Coarse aggregate 51, fine aggregate 25, cement 18 and appropriate amount of water.
[0035] Among them, the coarse aggregate is gravel, and the particle size of the coarse aggregate is not greater than 10mm, so as to avoid the exposed or sunken surface of the interlocking block; the fine aggregate is river sand, and the particle size of the fine aggregate is 2~5mm, so as to avoid The surface is honeycomb pitted surface, the cement is ordinary Portland cement P.O42.5, the cement strength is high, the amount of cement used is less under the same coarse aggregate and fine aggregate materials, and the coarse aggregate is oval crushed with smooth surface. Stone and fine aggregate are fine and well-matched river sand, which can reduce the amount of cement used and increase the compressive strength of the interlocking blocks.
[0036] see figure 1 , a concre...
Embodiment 3
[0044] The invention provides a concrete interlocking block, which is made of the following raw materials by weight:
[0045] Coarse aggregate 53, fine aggregate 28, cement 20 and appropriate amount of water.
[0046] Among them, the coarse aggregate is gravel, and the particle size of the coarse aggregate is not greater than 10mm, so as to avoid the exposed or sunken surface of the interlocking block; the fine aggregate is river sand, and the particle size of the fine aggregate is not greater than 2~5mm, to avoid interlocking The surface of the block is honeycomb pitted surface, the cement is ordinary Portland cement P.O42.5, the cement strength is high, the amount of cement used is less under the same coarse aggregate and fine aggregate materials, and the coarse aggregate is oval with smooth surface Crushed stone and fine aggregate are fine and well-matched river sand, which can reduce the amount of cement used and increase the compressive strength of the interlocking blocks...
PUM
| Property | Measurement | Unit |
|---|---|---|
| particle diameter | aaaaa | aaaaa |
| particle diameter | aaaaa | aaaaa |
| thickness | aaaaa | aaaaa |