A kind of one-dimensional metal oxide/carbide composite material and preparation method thereof

A composite material and oxide technology, applied in the field of inorganic nano functional material synthesis, can solve the problems of complex synthesis process, lack of catalysis, adsorption and electrochemical activity, high energy consumption, etc., and achieves simple preparation method and good active site. , the effect of low energy consumption

Active Publication Date: 2022-03-04
SUZHOU ADVANCED MATERIALS CO LTD
View PDF6 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the synthesis of carbides usually adopts a high-temperature thermal reduction method. The high-temperature environment used generally needs to reach above 1000°C, which consumes a lot of energy. The generated carbides are often block materials, which do not have good catalytic, adsorption and electrolytic chemical activity
However, although one-dimensional porous carbides with high activity can be obtained by using the template method, the synthesis process is very complicated.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of one-dimensional metal oxide/carbide composite material and preparation method thereof
  • A kind of one-dimensional metal oxide/carbide composite material and preparation method thereof
  • A kind of one-dimensional metal oxide/carbide composite material and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0045] A preparation method of a one-dimensional metal oxide / carbide composite material, comprising the steps of:

[0046] a. Preparation of one-dimensional strip metal-organic framework materials:

[0047] Take Ni(NO 3 ) 2 ·6H 2 Add O (1.2mM) into 6mL of water, then add 12mL of 4,4'-biphenyldicarboxylic acid (1.2mM) and sodium hydroxide (2.4mM) into the aqueous solution under stirring, stir well, and put it into the reaction kettle , treated at 170°C for 12 hours, centrifuged, washed, and dried to obtain a one-dimensional strip-shaped metal-organic framework material.

[0048] b. Preparation of one-dimensional metal oxide / carbide composites:

[0049] Put the one-dimensional strip metal-organic framework material prepared in step a into a porcelain cup, transfer it into a tube furnace, feed it with oxygen, raise the temperature to 400°C at a rate of 10°C / min, calcinate for 2 hours, and wait for cooling Finally, a fluffy black powder is obtained, which is a one-dimensional...

Embodiment 2

[0051] A preparation method of a one-dimensional metal oxide / carbide composite material, comprising the steps of:

[0052] a. Preparation of one-dimensional strip metal-organic framework materials:

[0053] Take Ni(NO 3 ) 2 ·6H 2 O(0.6mM), Co(NO 3 ) 2 ·6H 2 Add O (0.6mM) into 6mL of water, then add 12mL of 4,4'-biphenyl dicarboxylic acid (1.2mM) and sodium hydroxide (2.4mM) into the aqueous solution under stirring, stir well, and put it into the reaction kettle , treated at 170°C for 12 hours, centrifuged, washed, and dried to obtain a one-dimensional strip-shaped metal-organic framework material.

[0054] The SEM (scanning electron microscope) picture of the above-mentioned one-dimensional strip metal-organic framework material is shown in figure 1 ;Depend on figure 1 It can be seen that it is a nano-ribbon structure, the length is on the micrometer scale, the width and thickness are on the nanometer scale, the aspect ratio is ≥ 10, and there is a certain scale (50-...

Embodiment 3

[0060] A preparation method of a one-dimensional metal oxide / carbide composite material, comprising the steps of:

[0061] a. Preparation of one-dimensional strip metal-organic framework materials:

[0062] Take Ni(NO 3 ) 2 ·6H 2 O(0.3mM), Co(NO 3 ) 2 ·6H 2 Add O (0.9mM) into 6mL of water, then add 12mL of 4,4'-biphenyl dicarboxylic acid (2.4mM) and sodium hydroxide (2.4mM) into the aqueous solution under stirring, stir evenly, and put it into the reaction kettle , treated at 170°C for 8 hours, centrifuged, washed, and dried to obtain a one-dimensional strip-shaped metal-organic framework material.

[0063] b. Preparation of one-dimensional metal oxide / carbide composites:

[0064] Put the one-dimensional strip-shaped metal-organic framework material prepared in step a into a porcelain cup, transfer it into a tube furnace, pass in air, and heat it up to 500°C at a heating rate of 20°C / min for 1 hour and wait for cooling Finally, a one-dimensional metal oxide / carbide com...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The embodiments of the present invention involve the field of inorganic nano -functional material synthesis, and specifically involve a one -dimensional metal oxide / carbide composite material and its preparation methods.The one -dimensional metal oxide / carbide composite material provided by the present invention is made by the method including the following steps: the one -dimensional metal organic frame material is burned; the burning temperature is 200‑600 ° C; the one -dimensional metal metalOrganic framework materials include one -dimensional strip -shaped metal organic frame material.Low energy consumption, low raw material cost, easy to enlarge production.

Description

technical field [0001] The invention relates to the field of synthesis of inorganic nano functional materials, in particular to a one-dimensional metal oxide / carbide composite material and a preparation method thereof. Background technique [0002] Porous carbon materials have very important applications in the fields of electrocatalysis, batteries, capacitors, sensors, and gas adsorption due to their large specific surface area, good adsorption, and electrical conductivity. However, pure carbon materials lack active sites that can be directly used, so they are usually used as carrier materials and need to be combined with other active materials to achieve wider applications. In order to solve this problem, the commonly used method is to introduce active substances, mainly including noble metals, transition metal oxides, etc., and compound them with porous carbon materials by loading methods to improve their catalytic, adsorption and electrochemical activities. However, the...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01G11/26H01G11/30H01G11/86H01M4/36B01J27/22B01J35/10B01J37/08
CPCH01M4/362H01G11/30H01G11/26H01G11/86B01J27/22B01J35/0033B01J35/1004B01J37/086Y02E60/10
Inventor 张晓伟高鸿毅其他发明人请求不公开姓名
Owner SUZHOU ADVANCED MATERIALS CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com