Scale inhibition particle as well as preparation method and application thereof

A technology of scale inhibition and granules, applied in the field of its preparation and scale inhibition granules, can solve the problems of unmentioned slow release performance, and achieve the effect of wide application range, cost reduction and performance improvement.

Pending Publication Date: 2020-06-05
BEYCLEAN ENVIRONMENTAL PROTECTION TECH
View PDF10 Cites 7 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The anti-scaling carbon membrane prepared by this invention has good anti

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Scale inhibition particle as well as preparation method and application thereof
  • Scale inhibition particle as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0093] In this embodiment, a kind of antiscaling granule is provided, the preparation raw material percentage by weight of described antiscaling granule is 42% antiscaling powder, 34% adsorption material and 24% binding agent; Wherein antiscaling powder is organic Antiscaling powder, the binder is a combination of starch and polyethylene, the mass ratio of starch and polyethylene is 1:3, the adsorption material is carbon powder, and the mesh number of carbon powder is 1000 mesh.

[0094] The organic antiscaling powder includes the antiscaling material treated with surfactant hydrophobic, and the antiscaling material includes an antiscaling agent and a mesoporous material carrying the antiscaling agent; wherein the antiscaling agent is polyaspartic acid and poly The combination of acrylic acid; the mass ratio of polyaspartic acid and polyacrylic acid is 1.5:1; the mesoporous material is pure silicon MCM-41; the mesh number of pure silicon MCM-41 is 500 mesh; the scale inhibitor ...

Embodiment 2

[0103] In this embodiment, a kind of antiscaling granule is provided, the preparation raw material percentage by weight of described antiscaling granule is 50% antiscaling powder, 30% adsorption material and 20% binding agent; wherein antiscaling powder is organic Antiscaling powder, the binder is a combination of polyvinyl alcohol and polypropylene, the mass ratio of polyvinyl alcohol and polypropylene is 1:1, the adsorption material is diatomite, and the mesh number of diatomite is 500 mesh.

[0104] The antiscaling powder includes the antiscaling material treated with surfactant hydrophobic, and the antiscaling material includes the antiscaling agent and the mesoporous material loaded on the antiscaling agent; wherein the antiscaling agent is polyaspartic acid and polyacrylic acid The combination; the mass ratio of polyaspartic acid and polyacrylic acid is 1:1; the mesoporous material is diatomite; the mesh number of diatomite is 200 orders; the mass ratio of scale inhibitor...

Embodiment 3

[0113] In this embodiment, a kind of antiscaling granule is provided, the preparation raw material percentage by weight of described antiscaling granule is 35% antiscaling powder, 30% adsorption material and 35% binding agent; Wherein antiscaling powder is organic Antiscaling powder, the binder is a combination of starch and polyethylene, the mass ratio of starch and polyethylene is 1:10, the adsorption material is montmorillonite, and the mesh number of montmorillonite is 1200 mesh.

[0114] The antiscaling powder includes the antiscaling material treated with surfactant hydrophobic, and the antiscaling material includes the antiscaling agent and the mesoporous material loaded on the antiscaling agent; wherein the antiscaling agent is polyaspartic acid and polyacrylic acid The combination; the mass ratio of polyaspartic acid and polyacrylic acid is 3:1; the mesoporous material is activated carbon; the mesh number of activated carbon is 1000 mesh; The agent is stearic acid.

...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Meshaaaaaaaaaa
Meshaaaaaaaaaa
Meshaaaaaaaaaa
Login to view more

Abstract

The invention provides a scale inhibition particle as well as a preparation method and application thereof, the scale inhibition particle comprises scale inhibition powder, an adsorption material anda binder, and the binder is a combination of a water-soluble binder and a cured binder; the scale inhibition particle prepared by the invention has the advantages of strong descaling capability, longscale inhibition life, good water resistance, excellent water purification function, good slow release effect, controllable release rate, long action, simple preparation process and low cost, are usedfor water quality scale inhibition treatment, and are especially suitable for scale inhibition treatment of household water.

Description

technical field [0001] The invention relates to the field of water treatment chemicals, and relates to antiscaling particles, a preparation method and application thereof. Background technique [0002] With the large population increase, the pollution caused by the industrialization process, and the accelerated cycle of water use, a large amount of groundwater has to be over-exploited, making the hardness of tap water higher and higher. According to the survey, the water hardness in northern China has reached 500ppm, and the hardness of water is high. Boiled water tastes poor and often causes scaling on the bottom of the pot. Long-term drinking of high-hardness water can easily cause gastrointestinal disorders, kidney stones and other diseases. At present, the methods of descaling of drinking water in the market are mainly physical and chemical methods: physical methods mainly use physical methods such as magnetic field and electric field to soften water quality, but the phy...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C02F5/08C02F5/10
CPCC02F5/08C02F5/086C02F5/105
Inventor 陈柔羲李延涛秦黎明梁立兵陈红
Owner BEYCLEAN ENVIRONMENTAL PROTECTION TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap