A processing method for nickel-titanium shape memory alloy high-strength wire

A nickel-titanium alloy, memory alloy technology, applied in metal processing equipment, manufacturing tools, metal extrusion and other directions, can solve the problems of low single-mode production efficiency, poor comprehensive performance, poor toughness, etc.

Active Publication Date: 2021-10-29
西安华创新材料有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The object of the present invention is to overcome above-mentioned deficiencies in the prior art, provide a kind of nickel-titanium shape memory alloy high-strength wire material processing method, overcome 1 in the prior art: the processing method of hot drawing of fixed mold is nickel-titanium alloy under high temperature The surface of the wire material is seriously polluted, and repeated heating causes poor overall performance, low strength, and poor toughness; 2: The processing method of fixed die cold drawing has serious work hardening of nickel-titanium alloy materials. In order to prevent wire breakage, repeated heating and annealing is required. The secondary production efficiency is low, and the residual strain is large; 3: The existing technology does not have the technical inspiration of combining the two processing methods and the specific operation method.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A processing method for nickel-titanium shape memory alloy high-strength wire
  • A processing method for nickel-titanium shape memory alloy high-strength wire
  • A processing method for nickel-titanium shape memory alloy high-strength wire

Examples

Experimental program
Comparison scheme
Effect test

specific Embodiment approach

[0032] It should be noted that the structures, proportions, sizes, etc. shown in this specification are only used to cooperate with the content disclosed in the specification for the understanding and reading of those familiar with this technology, and are not used to limit the conditions for the implementation of the present invention , any modification of structure, change of proportional relationship or adjustment of size shall still fall within the scope covered by the technical content disclosed in the present invention without affecting the effect and purpose of the present invention. .

[0033] At the same time, terms such as "upper", "lower", "left", "right", "middle" and "one" quoted in this specification are only for the convenience of description and are not used to limit this specification. The practicable scope of the invention and the change or adjustment of its relative relationship shall also be regarded as the practicable scope of the present invention without...

Embodiment 1

[0035] The invention discloses a method for processing nickel-titanium shape memory alloy high-strength wire, which comprises the following steps:

[0036] Step 1) Thick nickel-titanium alloy wire is obtained by peeling the nickel-titanium alloy wire billet;

[0037] Step 2) hot-drawing the nickel-titanium alloy thick wire in step 1) to obtain the nickel-titanium alloy medium thick wire;

[0038] Step 3) performing high-temperature annealing and water quenching on the thick wire in the nickel-titanium alloy in step 2);

[0039] Step 4) performing cold drawing and on-line annealing treatment on the nickel-titanium alloy medium-thick wire after high-temperature annealing and water quenching in step 3), to obtain the nickel-titanium alloy thin wire;

[0040] Step 5) performing on-line aging treatment and peeling treatment on the nickel-titanium alloy fine wire in step 4), to obtain high-strength nickel-titanium shape memory alloy wire.

Embodiment 2

[0042] The invention discloses a method for processing nickel-titanium shape memory alloy high-strength wire, which comprises the following steps:

[0043]Step 1) Thick nickel-titanium alloy wire is obtained by peeling the nickel-titanium alloy wire billet;

[0044] Step 2) hot-drawing the nickel-titanium alloy thick wire in step 1) to obtain the nickel-titanium alloy medium thick wire;

[0045] Step 3) performing high-temperature annealing and water quenching on the thick wire in the nickel-titanium alloy in step 2);

[0046] Step 4) performing cold drawing and on-line annealing treatment on the nickel-titanium alloy medium-thick wire after high-temperature annealing and water quenching in step 3), to obtain the nickel-titanium alloy thin wire;

[0047] Step 5) performing on-line aging treatment and peeling treatment on the nickel-titanium alloy fine wire in step 4), to obtain high-strength nickel-titanium shape memory alloy wire.

[0048] Preferably, the peeling treatment ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
tensile strengthaaaaaaaaaa
yield strengthaaaaaaaaaa
tensile strengthaaaaaaaaaa
Login to View More

Abstract

The invention discloses a method for processing a nickel-titanium shape memory alloy high-strength wire, which comprises the following steps: step 1) peeling a nickel-titanium alloy wire billet to obtain a nickel-titanium alloy thick wire; The nickel-titanium alloy thick wire material is hot-drawn, obtains the nickel-titanium alloy medium thick wire material; Step 3) the nickel-titanium alloy medium thick wire material in step 2) is carried out high-temperature annealing and water quenching; Step 4) step 3 ) through high-temperature annealing and water quenching in nickel-titanium alloy medium thick wire material is carried out cold drawing and on-line annealing treatment, obtains nickel-titanium alloy thin wire material; step 5) carries out the nickel-titanium alloy thin wire material in step 4) On-line aging treatment and peeling treatment can obtain nickel-titanium shape memory alloy high-strength wire.

Description

technical field [0001] The invention belongs to the technical field of alloy wire processing, in particular to a method for processing nickel-titanium shape memory alloy high-strength wire. Background technique [0002] Nickel-titanium shape memory alloy is an intermetallic compound with nearly equal atomic ratio. The alloy has different crystal structures at different temperatures. The high-temperature phase is a body-centered cubic structure with high hardness and rigidity; the low-temperature martensite is monoclinic Structure, low hardness, and the alloy undergoes martensite and austenite phase transformation with temperature changes. The high-temperature phase of nickel-titanium alloy has excellent wear resistance and corrosion resistance, and the low-temperature phase has excellent damping properties. It has a unique shape memory effect and superelasticity in the phase transition region, and also has excellent biocompatibility. It is a kind of Ideal medical biomateria...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B21C37/04B21C1/04B21C43/04C22F1/10
CPCB21C1/04B21C37/045B21C37/047B21C43/04C22F1/002C22F1/006C22F1/10
Inventor 牛中杰梁振伟梁园园
Owner 西安华创新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com