Preparation method of polyamide polyamine-polyether amine cylinder adhesive

A technology of polyamide polyamine and polyether amine, which is applied in the field of papermaking aids, can solve the problems of unsatisfactory durability, broken holes in paper sheets, and increased molecular weight of polymers, and achieves good initial adhesion, long duration, The effect of good uniformity

Active Publication Date: 2020-07-24
ZHEJIANG TRANSFAR WHYYON CHEM
View PDF11 Cites 5 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The national standard GB / T 36420-2018 stipulates the limited content of absorbable halides in tissue paper and paper products, including epichlorohydrin, DCP, MCPD, but does not provide detection methods
[0005] In addition, the irreversible cross-linking reaction makes the PAE cylinder sticking agent have good cohesive force, but also leads to its unsatisfactory durability.
PAE cylinder sticking agent will tend to accumulate on the surface of the dryer, and the continuous crosslinking will make the molecular weight of the polymer increase infinitely. After a period of time, the coating will harden, causing the scraper to rattle, and the partial coating will crack and fall off, causing Holes in pages or even paper breaks, the coating has to be rebuilt

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation method of polyamide polyamine-polyether amine cylinder adhesive
  • Preparation method of polyamide polyamine-polyether amine cylinder adhesive
  • Preparation method of polyamide polyamine-polyether amine cylinder adhesive

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0030]In a stainless steel reaction kettle with conditions such as weighing, jacket heating, cooling, nitrogen protection, stirring, temperature, pressure indication, and feeding, add 17.9g of tallow, replace with nitrogen, start stirring, heat up to 140°C, and vacuumize To 5kPa and keep for 15 minutes, the constant weight in the kettle is 17.1g (about 0.02mol). Add 214.8g (1.47mol) of adipic acid, fill with nitrogen to slightly positive pressure, add 155g (1.5mol) of diethylenetriamine dropwise, raise the temperature to 140°C and stir and mix for 2 hours, then raise the temperature by 10°C per hour until 180°C, keep warm 2 hours. Start the vacuum system, gradually evacuate to an absolute pressure of 100Pa, and keep warm for 2 hours. Stop heating, fill with nitrogen to slightly positive pressure, add 670 g of hot deionized water to dilute the reaction material to a solid content of 33%, which is the aqueous solution of polyamide polyamine intermediate.

[0031] The aqueous s...

Embodiment 2

[0041] Add 16.2g of palm oil to a stainless steel reactor with conditions such as weighing, jacket heating, cooling, nitrogen protection, stirring, temperature, pressure indication, and feeding, replace with nitrogen, start stirring, heat up to 140°C, and vacuumize To 5kPa and keep for 15 minutes, the constant weight in the kettle is 16.0g (about 0.01mol). Add 214.8g (1.47mol) of adipic acid, fill with nitrogen to slightly positive pressure, dropwise add 103.2g (1mol) of diethylenetriamine and 73.1g (0.5mol) of triethylenetetramine, raise the temperature to 140°C and stir and mix for 2 hours. Then the temperature was increased by 10°C per hour until 180°C, and kept for 2 hours. Start the vacuum system, gradually evacuate to an absolute pressure of 100Pa, and keep warm for 2 hours. Stop heating, fill with nitrogen to slightly positive pressure, add 650 g of hot deionized water to dilute the reaction material to a solid content of 35%, which is the aqueous solution of polyamide...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation method of a polyamide polyamine-polyether amine cylinder adhesive. The method comprises the following steps: under the protection of introduced nitrogen, firstlycarrying out condensation polymerization on an alkenyl amine derivative, grease and dibasic acid or corresponding dibasic ester under normal pressure, then continuously carrying out condensation polymerization under a vacuum condition until the molecular weight is not increased any more, and adding water to form an aqueous solution of a polyamide polyamine intermediate; and adding branched polyether amine into the aqueous solution, carrying out a closed reaction, heating to carry out a cross-linking reaction, finally adding an organic acid to terminate the reaction, and adding water to diluteto obtain the polyamide polyamine-polyether amine cylinder adhesive. The cylinder adhesive prepared by the invention has good adhesion, flexibility, water solubility, uniformity, durability and the like, and the use of epoxy chloropropane is avoided.

Description

technical field [0001] The invention belongs to the technical field of papermaking additives, and relates to a sticky agent that is sprayed on a drying cylinder to help paper wrinkle when producing crepe paper, in particular to a preparation method of a polyamide polyamine-polyetheramine sticky agent . Background technique [0002] In the production of crepe paper, the paper is dried by a drying cylinder, and it needs to have a strong impact with a scraper to produce wrinkles, so as to improve the paper's softness, water absorption, bulk and other properties, and obtain a good hand feeling. The creping process requires proper cohesion between the paper sheet and the dryer cylinder. For paper machines with high speeds, the natural cohesion between the paper sheet and the dryer cylinder is not enough to form ideal wrinkles. A dryer must be used. Cylinder coating additives (including cylinder sticking agent, stripping agent and modifier) ​​are adjusted to achieve flexible cont...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C08G81/00C08G69/28C08G69/26C08G69/40C09D187/00C09D177/00
CPCC08G81/00C08G69/28C08G69/26C08G69/40C09D187/00C09D177/00
Inventor 钱进梁福根谢占豪方黎锋姚胜来雷赵世英陈文杰
Owner ZHEJIANG TRANSFAR WHYYON CHEM
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap