Method for preparing reusable masks by using antibacterial meltblown non-woven fabrics

A kind of melt-blown non-woven fabric and repeatable technology, which is applied in the field of hygiene products, can solve the problems of polluting the environment and difficulty in separating masks, and achieve the effects of preventing droplet infiltration, improving wearing comfort, and good protection effect

Active Publication Date: 2022-07-12
TAIHE KERUNGE GARMENT CO LTD
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

At present, disposable masks are widely used, with the characteristics of convenient use, high hygiene and safety, and low cost. However, the problem of garbage disposal caused by discarded disposable masks is very serious, and people usually do not Disposable masks are placed in medical waste for unified treatment. Disposable masks are mixed into domestic waste and difficult to separate during disposal, thus posing a hidden danger of polluting the environment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Method for preparing reusable masks by using antibacterial meltblown non-woven fabrics
  • Method for preparing reusable masks by using antibacterial meltblown non-woven fabrics

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0024] Preparation of antibacterial melt-blown non-woven fabric: first, 4g of silver nitrate, 12g of N-methylol acrylamide, 0.5g of potassium persulfate were dissolved in water to make a saturated aqueous solution at 25°C, and then N-methylol was added to the silver nitrate aqueous solution. Base acrylamide aqueous solution and potassium persulfate aqueous solution, heated to 80 °C for 5 h under stirring, and the reaction was completed to obtain an antibacterial treatment solution; 10kg of melt-blown non-woven fabric was immersed in 100 kg of 45 °C antibacterial treatment solution, after immersion for 30min, take out, 80 drying at ℃ to obtain antibacterial melt-blown non-woven fabrics.

[0025] (1) Mask design: The mask is composed of hydrophilic spunbond non-woven fabric layer, antibacterial melt-blown non-woven fabric layer, activated carbon fiber fabric layer and water-repellent spunbond non-woven fabric layer from inside to outside, as well as nose bridge strips and ears b...

Embodiment 2

[0030] The difference between Example 2 and Example 1 is that the dipping time of the melt-blown non-woven fabric is modified to 15min.

[0031] Preparation of antibacterial melt-blown non-woven fabric: first, 4g of silver nitrate, 12g of N-methylol acrylamide, 0.5g of potassium persulfate were dissolved in water to make a saturated aqueous solution at 25°C, and then N-methylol was added to the silver nitrate aqueous solution. Base acrylamide aqueous solution and potassium persulfate aqueous solution, heated to 80 °C under stirring for 5 hours, and the reaction was completed to obtain an antibacterial treatment solution; 10kg of melt-blown non-woven fabric was immersed in 100kg of 45 °C antibacterial treatment solution, and immersed for 15min. Take out, 80 drying at ℃ to obtain antibacterial melt-blown non-woven fabrics.

[0032] (1) Mask design: The mask is composed of hydrophilic spunbond non-woven fabric layer, antibacterial melt-blown non-woven fabric layer, activated carb...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a method for preparing reusable masks by using antibacterial melt-blown non-woven fabrics, and relates to the technical field of sanitary products. The structure of the spun cloth layer, the activated carbon fiber cloth layer and the water-repellent spunbond non-woven fabric layer makes a reusable mask, wherein the hydrophilic spunbond non-woven fabric layer can absorb the water vapor generated by the human body to improve the wearing comfort of the mask, The antibacterial melt-blown non-woven fabric layer and the activated carbon fiber fabric layer are used to isolate and absorb harmful substances, and the water-repellent spunbond non-woven fabric layer plays a waterproof role to prevent the infiltration of droplets. People's daily wearing needs.

Description

Technical field: [0001] The invention relates to the technical field of sanitary products, in particular to a method for preparing a reusable mask by using an antibacterial melt-blown non-woven fabric. Background technique: [0002] Masks are designed for people's health and are used to block some visible or invisible substances that are harmful to the human body. At present, disposable masks are widely used and have the characteristics of convenient use, high sanitation and safety, and low cost. However, the problem of garbage disposal caused by discarding disposable masks is very serious, and people usually do not use them in daily life. Disposable masks are placed in medical waste for unified treatment. Disposable masks are mixed with domestic waste and are difficult to separate during processing, thus causing potential environmental pollution. [0003] In response to the above problems, the company has developed a reusable mask, which is made of antibacterial meltblown ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): A41D13/11A41D31/02A41D31/30A41D31/10A41D31/04D06M11/65D06M15/29
CPCA41D13/1192A41D31/02A41D31/30A41D31/10A41D31/04D06M11/65D06M15/29D06M16/00A41D2500/30
Inventor 韩晓浩付倩倩韩浩张凯刘凤娟
Owner TAIHE KERUNGE GARMENT CO LTD
Features
  • R&D
  • Intellectual Property
  • Life Sciences
  • Materials
  • Tech Scout
Why Patsnap Eureka
  • Unparalleled Data Quality
  • Higher Quality Content
  • 60% Fewer Hallucinations
Social media
Patsnap Eureka Blog
Learn More

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2025 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com