A kind of pure cobalt hydrotalcite compound and preparation method thereof

A hydrotalcite compound, hydrothermal aging technology, applied in cobalt compounds, chemical instruments and methods, inorganic chemistry, etc., can solve the problems of residual cobalt ions, not being fully utilized, etc., and achieve high purity and crystallinity, good layer The effect of crystalline structure regularity and lamellar morphology

Active Publication Date: 2021-11-26
FUZHOU UNIV
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, because ammonia easily forms complexes with cobalt ions, some cobalt ions remain in the solution and cannot be fully utilized.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of pure cobalt hydrotalcite compound and preparation method thereof
  • A kind of pure cobalt hydrotalcite compound and preparation method thereof
  • A kind of pure cobalt hydrotalcite compound and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A preparation method of pure cobalt-like hydrotalcite compound, comprising the steps of: weighing 11.1895 g Co(NO 3 ) 2 ·6H 2 O was dissolved in 256mL methanol-water mixed solvent, and the volume ratio of methanol and water was 1:1 to obtain cobalt nitrate solution. Weigh 0.5096g anhydrous Na 2 CO 3 Dissolve in 464mL methanol-water mixed solvent to get Na 2 CO 3 solution. Weigh 6.4000g NaOH and dissolve in 80 mL methanol-water mixed solvent to obtain NaOH solution. Under room temperature and vigorous stirring, the cobalt nitrate solution was slowly dropped into Na 2 CO 3 solution, while adjusting the reaction system pH=10 with NaOH solution. After the cobalt nitrate solution was added dropwise, the obtained precipitate was filtered and washed with a methanol-water mixed solution, and the obtained solid was dried in an oven at 60 °C for 12 hours to obtain a pure cobalt-like hydrotalcite compound.

[0041] The crystal phase structure of the above samples was cha...

Embodiment 2

[0043] A preparation method of pure cobalt-like hydrotalcite compound, comprising the steps of: weighing 11.1895g Co(NO 3 ) 2 ·6H 2 O was dissolved in 256mL methanol-water mixed solvent, the volume ratio of methanol and water was 4:1 to obtain cobalt nitrate solution. Weigh 0.5096 g anhydrous Na 2 CO 3 Dissolved in 464 mL of methanol-water mixed solvent to obtain Na 2 CO 3 solution. Weigh 6.4000 g of NaOH and dissolve it in 80 mL of methanol-water mixed solvent to obtain NaOH solution. Under room temperature and vigorous stirring, the cobalt nitrate solution was slowly dropped into Na 2 CO 3 solution, while adjusting the reaction system pH=10 with NaOH solution. After the cobalt nitrate solution was added dropwise, the obtained precipitate was filtered and washed with a methanol-water mixed solution, and the obtained solid was dried in an oven at 60 °C for 12 hours to obtain a pure cobalt-like hydrotalcite compound.

[0044] The crystal phase structure of the above s...

Embodiment 3

[0046] A preparation method of pure cobalt-like hydrotalcite compound, comprising the steps of: weighing 11.1895g Co(NO 3 ) 2 ·6H 2 O was dissolved in 256mL methanol-water mixed solvent, the volume ratio of methanol and water was 8:1 to obtain cobalt nitrate solution. Weigh 0.5096 g anhydrous Na 2 CO 3 Dissolved in 464 mL of methanol-water mixed solvent to obtain Na 2 CO 3 solution. Weigh 6.4000 g NaOH and dissolve in 80 mL methanol-water mixed solvent to obtain NaOH solution. Under room temperature and vigorous stirring, the cobalt nitrate solution was slowly dropped into Na 2 CO 3 solution, while adjusting the reaction system pH=10 with NaOH solution. After the cobalt nitrate solution was added dropwise, the obtained precipitate was filtered and washed with a methanol-water mixed solution, and the obtained solid was dried in an oven at 60 °C for 12 hours to obtain a pure cobalt-like hydrotalcite compound.

[0047] The crystal phase structure of the above samples wa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
thicknessaaaaaaaaaa
Login to view more

Abstract

The invention relates to the technical field of preparation of hydrotalcite-like compounds, and discloses a pure cobalt-like hydrotalcite compound and a preparation method thereof. Using the constant pH precipitation method, using cobalt nitrate as the cobalt source, methanol-water (volume ratio 1:1–8:1) mixed solution as the solvent, slowly add the cobalt nitrate solution to the sodium carbonate solution at room temperature and adjust the pH of the solution =8–12, after hydrothermal aging, suction filtration, washing, drying and other steps, pure cobalt-based hydrotalcites can be obtained. The hydrotalcite-like crystal phase is single, the structure is regular, and it presents a good layered structure and sheet morphology. The average thickness of the nanosheets is 5.9-12.8 nm, and it has a high degree of crystallinity. The preparation process of the invention is simple and easy to operate, the raw materials are cheap and easy to obtain, the preparation conditions are mild, the cycle is short, the purity and yield of the hydrotalcite-like stone are high, and the quantitative synthesis can be realized.

Description

technical field [0001] The invention belongs to the technical field of hydrotalcite-like preparation, and in particular relates to a pure cobalt-like hydrotalcite compound and a preparation method thereof. Background technique [0002] Hydrotalcite-like compounds are a class of layered compounds formed by electrostatic interactions between positively charged brucite-like laminates and interlayer anions, and their structural formula can be expressed as [M2+1− x M3+ x (OH) 2 ][A n− ] x / n · z h 2 O, where M 2+ for Mg 2 + 、Ni 2+ 、Co 2+ 、Cu 2+ , Zn 2+ Wait, M 3+ for Al 3+ , Fe 3+ , Mn 3+ , Ga 3+ Wait, A n− for CO 3 2– , NO 3 – , Cl – and organic anions. Hydrotalcite-like compounds exhibit unique physical and chemical properties due to the particularity of their structure, such as the tunability of layered cations and interlayer anions, the exchangeability of interlayer anions, and the "memory effect", etc., and are widely used in anion exchange. materials...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Patents(China)
IPC IPC(8): C01G51/00B82Y30/00B82Y40/00
CPCB82Y30/00B82Y40/00C01G51/00C01P2002/72C01P2004/03C01P2004/64
Inventor 李达林宛春生江莉龙
Owner FUZHOU UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap