A kind of ultra-thick material layer sintering material and sintering method, sintered ore

A sintering method and technology for sintering ore, applied in the field of sintering, can solve the problems affecting the output and quality of sintering ore, limiting the thickness of the material layer, low sintering speed, etc., and achieving the effects of good air permeability, improved quality and low ore return rate

Active Publication Date: 2022-03-22
SHOUGANG CORPORATION
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0006] The invention provides an ultra-thick material layer sintering material, a sintering method and a sintered ore, in order to solve the problem that in the prior art, fine-grain fine powder is used as a raw material, and the sintering speed is low when the ultra-thick material layer is sintered, or even flameout affects the sintered ore. The output and quality limit the technical problem of further increasing the thickness of the material layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of ultra-thick material layer sintering material and sintering method, sintered ore
  • A kind of ultra-thick material layer sintering material and sintering method, sintered ore
  • A kind of ultra-thick material layer sintering material and sintering method, sintered ore

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1 to Embodiment 7

[0056] Embodiments 1 to 7 of the present invention provide an ultra-thick material layer sintering material and a sintering method thereof, which are carried out on a 360 flat-belt sintering machine, figure 2 It is a step diagram of a sintering method for an ultra-thick material layer sintered material according to an embodiment of the present invention, combined with figure 2 , during production, firstly carry out the distribution of bottom material, which is composed of sintered ore with a particle size of 10-20 mm; 4. Use sintered ore with a particle size of 5-15mm; then spread the sandwich layer 6, spread the sintered ore with a particle size of 5-15mm on the lower mixture layer, and finally carry out the upper mixture layer 7 cloth, the upper mixture layer 7 is the secondary mixture. The schematic diagram of the longitudinal section of the sintered material after cloth is as follows: figure 1 As shown, the thickness of each layer is shown in Table 1 and Table 2. The ...

Embodiment 8

[0058] Embodiment 8 takes Embodiment 7 as a reference, and is different from Embodiment 7 in that no sandwich layer cloth is carried out, and the rest is the same as Embodiment 7.

Embodiment 9

[0060] Embodiment 9 takes Embodiment 3 as a reference, and differs from Embodiment 3 in that the thickness of the sandwich layer 6 is 40 mm, and the rest is the same as Embodiment 3.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
widthaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to View More

Abstract

The invention discloses an ultra-thick material layer sintering material, a sintering method thereof, and a sintered ore. The sintering material is a bottom material layer, a lower mixed material layer and an upper mixed material layer in sequence from bottom to top; the lower mixed material layer Including N spacer strips and the mixture to be sintered, the N spacer strips are arranged vertically and at intervals to separate the mixture to be sintered, and the N spacer strips are composed of the first sintered ore, The thickness of the N spacer strips is 500-800mm, the width of the N spacer strips is 40-60mm, and the distance between any two adjacent spacer strips is 300-1000mm, wherein N is positive integer. The method disclosed in this application achieves a relatively high sintering speed of 26.1 mm / min under a thick material layer of more than 1000 mm, and a high yield of up to 85%, low fuel consumption, and the drum index of the obtained sintered ore is 82 ~87%.

Description

technical field [0001] The invention relates to the technical field of sintering, in particular to an ultra-thick material layer sintering material, a sintering method and a sintered ore. Background technique [0002] Sintering is a variety of powdery iron-containing raw materials, mixed with an appropriate amount of fuel and flux, added an appropriate amount of water, mixed and granulated, and then distributed, ignited and sintered on the sintering equipment to cause a series of physical and chemical changes in the material. The process in which ore powder particles are bonded into agglomerates to form sintered ore. In iron ore sintering production, thick material layer cloth is generally used for sintering in the cloth stage to improve the quality of sinter and reduce fuel consumption. For example, Ma'anshan Iron and Steel Group Corporation's Santie General Plant has achieved a sintering layer thickness of 900mm, and individual small sintering machines below 300 square me...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22B1/16
CPCC22B1/16
Inventor 马怀营陈斌龚坚吴建海赵志星张勇欧书海刘磊高新洲张志东潘文赵满祥张亚鹏辛越郑敬先
Owner SHOUGANG CORPORATION