Formula of novel logistics tray
A pallet and logistics technology, which is applied in the formulation field of new logistics pallets, can solve the problem of low surface energy, achieve the effects of improving surface energy, avoiding poor cementation effect, and facilitating automatic implementation
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Examples
Example Embodiment
[0021] Example one;
[0022] A formula for a new type of logistics tray, the logistics tray is composed of the following ingredients, 88.2% PP (polypropylene), 2.0% HDPE (hot melt resin), 0.10% defoamer, 5.0% POE (thermoplastic elastic Body), 1.8% color masterbatch, 2.46% 30% sodium hydroxide solution and 0.10% degreasing mixed solution.
[0023] Among them, the specific process is as follows:
[0024] Step 1, sieving and proportioning. Firstly, each component is sieved, and then the sieved components are proportioned and weighed.
[0025] Step 2, mixing and stirring, put the weighed raw materials into the deceleration mixer for mixing, and during the stirring process, heat the interior of the high-speed mixer. After heating to 300 degrees, the sodium hydroxide solution and chromium A mixed solution composed of 10% acid; 60% water; 30% concentrated sulfuric acid, and under the action of the corresponding rotation speed, makes the ingredients mixed evenly and fully to obtain the mixtu...
Example Embodiment
[0033] Example two;
[0034] 88.2% PP (polypropylene), 5.0% HDPE (hot melt resin), 0.30% defoamer, 0.1% POE (thermoplastic elastomer), 1.8% color masterbatch and 3.0% 30% sodium hydroxide Solution and 1.6% degreasing mixed solution.
[0035] Among them, the specific process is as follows:
[0036] Step 1, sieving and proportioning. Firstly, each component is sieved, and then the sieved components are proportioned and weighed.
[0037] Step 2, mixing and stirring, put the weighed raw materials into the deceleration mixer for mixing, and during the stirring process, heat the inside of the high-speed mixer. After heating to 300 degrees, the sodium hydroxide solution and chromium A mixed solution composed of 10% acid; 60% water; 30% concentrated sulfuric acid, and under the action of the corresponding rotation speed, makes the ingredients mixed evenly and fully to obtain the mixture;
[0038] Step 3. The mixture is allowed to stand, and the mixture is allowed to stand for 3 hours, and the...
Example Embodiment
[0045] Example three;
[0046] 88.2% PP (polypropylene), 4.0% HDPE (hot melt resin), 0.30% defoamer, 0.1% POE (thermoplastic elastomer), 1.8% color masterbatch and 2.0% 30% sodium hydroxide Solution and 3.6% degreasing mixed solution.
[0047] Among them, the specific process is as follows:
[0048] Step 1, sieving and proportioning. Firstly, each component is sieved, and then the sieved components are proportioned and weighed.
[0049] Step 2, mixing and stirring, put the weighed raw materials into the deceleration mixer for mixing, and during the stirring process, heat the inside of the high-speed mixer. After heating to 300 degrees, the sodium hydroxide solution and chromium A mixed solution composed of 10% acid; 60% water; 30% concentrated sulfuric acid, and under the action of the corresponding rotation speed, makes the ingredients mixed evenly and fully to obtain the mixture;
[0050] Step 3. The mixture is allowed to stand, and the mixture is allowed to stand for 3 hours, and t...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap