Self-leveling mortar and preparation method thereof

A self-leveling mortar and quartz sand technology, applied in the field of mortar, can solve the problems of poor water resistance, low strength, and obstacles to the promotion of gypsum-based self-leveling materials, and achieve smooth hand feeling, high flexural strength, strong decorative effect and ornamental Effect

Pending Publication Date: 2020-11-20
XINYANG LINGSHI TECH CO LTD
View PDF8 Cites 3 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, for gypsum-based self-leveling materials, it also has obvious shortcomings, ma

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Self-leveling mortar and preparation method thereof
  • Self-leveling mortar and preparation method thereof
  • Self-leveling mortar and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

preparation example Construction

[0035] The invention also discloses a method for preparing self-leveling mortar, comprising the following steps:

[0036] 1) drying 35-45% by weight of desulfurized gypsum until the moisture content is less than 5%, and then mixing it with 3-11% by weight of cement to obtain a mixture A;

[0037] 2) 1-3% by weight of silica fume, 1-2% by weight of amorphous calcium aluminate cement quick-hardening agent, 2-4% by weight of calcium propionate, 1-2% by weight of carbonic acid Lithium, 2-4% by weight of titanium dioxide, 1-2% by weight of thickener, 1-2% by weight of water reducer, 2-3% by weight of polyethersulfone, 2-4% by weight The polyvinyl chloride thermoplastic elastomer is mixed with 1 to 5% by weight of the additive, and stirred evenly to obtain the mixture B;

[0038] 3) After mixing the mixture A and the mixture B, add 20 to 30% of the filler by weight, and pour 0.5 to 1% of eucalyptol and 0.2 to 0.6% by weight of eucalyptol while stirring evenly. Part of Apisson oil,...

Embodiment 1

[0043] 1) Drying 35% by weight of desulfurized gypsum until the water content is less than 5%, and then mixing it with 3% by weight of cement to obtain Mixture A;

[0044] 2) 1% by weight of silica fume, 1% by weight of amorphous calcium aluminate cement quick-hardening agent, 2% by weight of calcium propionate, 1% by weight of lithium carbonate, 2% by weight of titanium dioxide , 1% by weight of thickener, 1% by weight of water reducer, 2% by weight of polyethersulfone, 2% by weight of polyvinyl chloride thermoplastic elastomer and 1% by weight of additives are mixed, stirred Evenly, mixture B is obtained;

[0045] 3) After mixing the mixture A and the mixture B, add 20% of the filler by weight, and pour 0.5% of eucalyptol and 0.2% of apisson oil into it while stirring well , and then add an appropriate amount of water while stirring, and you can get a self-leveling mortar after preparation.

[0046] The filler includes ceramsite, sand, stone particles, wood fiber and quart...

Embodiment 2

[0051] 1) Dry 45% by weight of desulfurized gypsum until the water content is less than 5%, and then mix it with 11% by weight of cement to obtain admixture A;

[0052]2) 3% by weight of silica fume, 2% by weight of amorphous calcium aluminate cement quick-hardening agent, 4% by weight of calcium propionate, 2% by weight of lithium carbonate, 4% by weight of titanium dioxide , 2% by weight of thickener, 2% by weight of water reducer, 3% by weight of polyethersulfone, 4% by weight of polyvinyl chloride thermoplastic elastomer and 5% by weight of additives are mixed, stirred Evenly, mixture B is obtained;

[0053] 3) After mixing the mixture A and the mixture B, add 30% of the filler by weight, and pour 1% of eucalyptol and 0.6% of apisson oil into it while stirring evenly , and then add an appropriate amount of water while stirring, and you can get a self-leveling mortar after preparation.

[0054] The filler includes ceramsite, sand, stone particles, wood fiber and quartz sa...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Diameteraaaaaaaaaa
Login to view more

Abstract

The invention discloses a self-leveling mortar and a preparation method thereof. The self-leveling mortar comprises the following raw materials in parts by weight: 3-11% of cement; 35%-45% of desulfurized gypsum; 20%-30% of a filler; 1-3% of silica fume; 1%-2% of an amorphous calcium aluminate cement rapid hardening agent; 0.5 to 1% of eucalyptol; 0.2%-0.6% of apiezon grease; 2-4% of calcium propionate; 1-2% of lithium carbonate; 2-4% of titanium dioxide; 1-2% of a thickening agent; 1-2% of a water reducing agent; 2-3% of polyether sulfone; 2-4% of a polyvinyl chloride thermoplastic elastomer;and 1-5% of an additive. The self-leveling mortar is high in breaking strength, high in compressive strength, high in fluidity and high in ground bonding force, and the overall comprehensive performance is greatly improved.

Description

technical field [0001] The invention relates to the technical field of mortar, in particular to a self-leveling mortar and a preparation method thereof. Background technique [0002] For the existing self-leveling materials, they are mainly used on uneven substrates, so as to make the substrate smoother and smoother, which is conducive to the subsequent construction work. Usually, the application of self-leveling materials is to erect various floor materials, such as wooden floors, tile floors, PVC, etc., for leveling operations. However, for gypsum-based self-leveling materials, it also has obvious shortcomings, mainly reflected in poor water resistance and low strength. also suffered certain obstacles. [0003] Therefore, these shortcomings of gypsum-based self-leveling materials must be continuously improved, so as to make the application space of this material wider. At present, in order to improve the performance of desulfurized gypsum-based self-leveling materials, ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): C04B28/14C04B111/62
CPCC04B28/144C04B2111/62C04B2201/50C04B7/00C04B14/06C04B14/02C04B18/26C04B18/025C04B18/146C04B2103/14C04B24/02C04B24/08C04B24/04C04B22/10C04B14/305C04B2103/44C04B2103/302C04B24/28C04B24/2682C04B22/002C04B2103/54C04B2103/0057C04B24/383C04B2103/50C04B2103/0068C04B2103/22C04B2103/12C04B2103/65C04B24/36
Inventor 孟旭燕王明明肖学党赵小艳黄强
Owner XINYANG LINGSHI TECH CO LTD
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap