Embossed paper as well as preparation method and application thereof

A technology of embossed paper and embossed layer, applied in the field of composite paper, can solve problems such as poor strength, damage, bulging, etc., and achieve the effects of improving mechanical properties, transparency, and good exhaust effect

Pending Publication Date: 2020-12-11
江苏福泰涂布科技股份有限公司
View PDF11 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

This utility model solves the problems of high manufacturing cost, poor strength and easy damage of embossed paper existing in the prior art
[0006] In the current usual stickers, the problem of bulging caused by long-term use seriously affects people's daily use. How to provide a method to solve the problem of bulging stickers has become an urgent problem to be solved

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Embossed paper as well as preparation method and application thereof
  • Embossed paper as well as preparation method and application thereof
  • Embossed paper as well as preparation method and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0084] This embodiment provides a kind of embossed paper, wherein each layer parameter is as follows:

[0085] composition parameter Resin embossed layer Thickness 30μm paper layer Thickness 100μm resin layer 25μm Depth of air guide groove 15μm The width of the raised part of the air guide groove 0.15mm Air groove width 0.55mm Air groove shape diamond Cross-sectional shape of the air guide groove "V" shape

[0086] The preparation method is as follows:

[0087] (1) 50 parts of low-density polyethylene resin, 25 parts of high-density polyethylene resin and 25 parts of homopolypropylene resin are mixed, and melted in a hopper at 280 ° C to obtain the melted resin;

[0088] (2) Coat the melted resin obtained in step (1) on one side of the kraft paper layer, and cold press at 0.7MPa through an embossing cylinder for 1.2s to obtain a resin embossed layer;

[0089] (3) After mixing 50 parts of low-density polye...

Embodiment 2

[0093] This embodiment provides a kind of embossed paper, wherein each layer parameter is as follows:

[0094] composition parameter Resin embossed layer Thickness 20μm paper layer Thickness 50μm resin layer 12μm Depth of air guide groove 5μm The width of the raised part of the air guide groove 0.1mm Air groove width 0.45mm Air groove shape rectangle Cross-sectional shape of the air guide groove "V" shape

[0095] The preparation method is as follows:

[0096] (1) Mix 37.5 parts of low-density polyethylene resin, 12.5 parts of high-density polyethylene resin and 50 parts of copolymerized polypropylene resin, and melt them in a hopper at 200 ° C to obtain the melted resin;

[0097] (2) Coat the melted resin obtained in step (1) on one side of the glassine paper layer, and cold press at 0.4 MPa through an embossing cylinder for 1.5 seconds to obtain a resin embossed layer;

[0098] (3) After mixing 37.5 par...

Embodiment 3

[0102] This embodiment provides a kind of embossed paper, wherein each layer parameter is as follows:

[0103] composition parameter Resin embossed layer Thickness 40μm paper layer Thickness 150μm resin layer 30μm Depth of air guide groove 40μm The width of the raised part of the air guide groove 0.25mm Air groove width 2.4mm Air groove shape hexagon Cross-sectional shape of the air guide groove "︺"shape

[0104] The preparation method is as follows:

[0105] (1) Mix 60 parts of low-density polyethylene resin and 40 parts of high-density polyethylene resin, melt them in a hopper at 350° C., and obtain the melted resin;

[0106](2) Coating the melted resin obtained in step (1) on one side of the coated paper layer, cold pressing at 1.0 MPa through an embossing cylinder, and cold pressing for 0.4s to obtain a resin embossed layer;

[0107] (3) After mixing 60 parts of low-density polyethylene resin and 20 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides embossed paper and a preparation method and application thereof. The embossed paper comprises a resin embossed layer and a paper layer which are sequentially arranged in a stacked mode. The preparation method comprises the following steps: (1) mixing raw materials of the resin embossed layer, and then conducting melting to obtain molten resin; and (2) coating one side of a paper layer with the molten resin obtained in the step (1), and carrying out cold pressing through an embossing cylinder to obtain a resin embossed layer, thereby obtaining the embossed paper. The embossed paper provided by the invention can solve the problem that the appearance and the practicability are influenced by bubbling caused by long-term use of a sticker, and has a wide application prospect.

Description

technical field [0001] The invention belongs to the field of composite paper, in particular relates to an embossed paper and its preparation method and application, in particular to an embossed paper with exhaust effect and its preparation method and application. Background technique [0002] Embossed paper is a kind of paper for cover decoration. It is called "embossed" because of the inconspicuous depressions on its surface. In the field of stickers, there is a problem that after long-term use, water and other substances in the sticker glue evaporate to produce bulges, which seriously affects the appearance and practical use. [0003] Disclosed in CN108221476A is a kind of color halo pearlescent laser transfer embossed paper and its manufacturing method, wherein the color halo pearlescent laser transfer embossed paper comprises: a base paper layer, a color halo pearlescent coating, coated on the top of the base paper layer; The paint layer is coated on the halo pearlescen...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
IPC IPC(8): D21H27/02D21H27/26D21H19/84D21H19/70D21H19/22B31F1/07C08L23/06C08L23/12C08L23/14C09J7/21
CPCD21H27/02D21H27/26D21H19/84D21H19/70D21H19/22B31F1/07C08L23/06C09J7/21C08L23/14C08L2207/062C08L2207/066C08L2205/025C08L2205/03C09J2400/283
Inventor 顾文斌
Owner 江苏福泰涂布科技股份有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap