Organic electrophosphorescent light-emitting material and application thereof

A phosphorescent light-emitting material, electrophosphorescence technology, applied in the direction of light-emitting materials, organic chemistry, indium organic compounds, etc., can solve the problems of low phosphorescence efficiency, hindering commercialization, poor stability and lifespan, etc.

Active Publication Date: 2021-01-05
北京燕化集联光电技术有限公司
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

For example, the U.S. patent of US6687266 discloses a class of Ir complexes containing benzimidazole ligands. Due to the low phosphorescence efficiency, poor stability and lifespan of these compounds, the possibility of commercialization has been hindered. sex

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Organic electrophosphorescent light-emitting material and application thereof
  • Organic electrophosphorescent light-emitting material and application thereof
  • Organic electrophosphorescent light-emitting material and application thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0062] Example 1: Synthesis of Ligand P1

[0063]

[0064] The synthetic route is as follows:

[0065]

[0066] The specific experimental steps are:

[0067] (1) In a 2L three-necked flask equipped with mechanical stirring, add 2-fluoronitrobenzene (14.1g, 0.1mol), 2-bromoaniline (25.7g, 0.15mol), stir, and heat up to 180 ℃, heat preservation reaction for more than 30 hours, during the reaction process, the color gradually turns red, and finally turns dark red gradually. After the reaction, the organic phase was separated, extracted, dried, column chromatographed, and the solvent was spin-dried to obtain 24.8 g of orange-red solid M1 with a yield of 85%.

[0068] (2) In a 1L three-neck flask equipped with mechanical stirring, add M1 (29.2g, 0.1mol), sodium sulfide nonahydrate (96g, 0.4mol), ethanol (200mL), water (100mL), nitrogen protection, and heat to Reflux, reflux reaction for 3 hours, end the reaction. The organic phase was separated, extracted, dried, column c...

Embodiment 2

[0073] Example 2: Synthesis of Ligand P2

[0074]

[0075] With reference to the synthesis steps of Example 1, just replace o-bromobenzoyl chloride with 2-bromo-4-methylbenzoyl chloride in step (3), and other raw materials and steps are the same as in Example 1 to obtain ligand P2.

[0076] Product MS (m / e): 314; Elemental Analysis (C 20 h 14 N 2 S): theoretical value C: 76.40%, H: 4.49%, N: 8.91%; measured value C: 76.49%, H: 4.56%, N: 8.88%.

Embodiment 3

[0077] Example 3: Synthesis of Ligand P3

[0078]

[0079] Referring to the synthesis steps of Example 1, except that 2-bromo-4-methylaniline is used instead of 2-bromoaniline in step (1), other raw materials and steps are the same as in Example 1 to obtain ligand P3.

[0080] Product MS (m / e): 314; Elemental Analysis (C 20 h 14 N 2 S): theoretical value C: 76.40%, H: 4.49%, N: 8.91%; measured value C: 76.49%, H: 4.56%, N: 8.88%.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention relates to the technical field of organic electroluminescent display, particularly discloses a novel organic electrophosphorescent light-emitting material, and also discloses an application of the novel organic electrophosphorescent light-emitting material in an organic light-emitting device. The organic electrophosphorescent light-emitting material provided by the invention has a structure as shown in a general formula (I) in the specification. The organic electrophosphorescent light-emitting material is applied to the organic light-emitting device, and the prepared light-emitting device shows excellent performances of high purity, high brightness and high efficiency.

Description

technical field [0001] The invention relates to the technical field of organic electroluminescent display, specifically discloses a novel organic electroluminescent material and its application in organic electroluminescent devices. Background technique [0002] Electroluminescent display devices can be divided into inorganic electroluminescent display devices and organic electroluminescent display devices according to the difference in the constituent materials of the light-emitting layer. Compared with inorganic electroluminescent display devices, organic electroluminescent display devices have incomparable advantages, such as full-color emission in the visible spectrum range, extremely high brightness, extremely low driving voltage, fast response time, and simple fabrication. craft etc. [0003] The research on organic electroluminescence started in the 1860s. Pope realized electroluminescence on anthracene single crystal for the first time, but at that time the driving ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C07F15/00C09K11/06H01L51/54H01L51/50
CPCC07F15/0033C09K11/06C09K2211/185C09K2211/1051C09K2211/1007C09K2211/1029C09K2211/1033H10K85/342H10K50/11
Inventor 范洪涛梁现丽段陆萌杭德余曹占广班全志
Owner 北京燕化集联光电技术有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com