Preparation process and device for hot melt adhesive film bonded with PP material

A technology of hot melt adhesive film and preparation process, applied in the direction of adhesive type, heat activated film/sheet, graft polymer adhesive, etc. Handling and other problems to achieve the effect of improving viscosity

Inactive Publication Date: 2021-01-12
江苏惠沣环保科技有限公司
View PDF2 Cites 4 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0004] For this reason, the embodiment of the present invention provides a hot melt adhesive film preparation process and device for bonding PP material, which solves the problem that the way of physically changing the stickiness of PP material cannot fundamentally solve the problem of its stickiness, while using other materials Activating the surface of the PP material will affect the properties of the hot melt adhesive film itself, and there will be problems of structural denaturation and difficult processing in the later stage

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Preparation process and device for hot melt adhesive film bonded with PP material
  • Preparation process and device for hot melt adhesive film bonded with PP material
  • Preparation process and device for hot melt adhesive film bonded with PP material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0031] The implementation mode of the present invention is illustrated by specific specific examples below, and those who are familiar with this technology can easily understand other advantages and effects of the present invention from the contents disclosed in this description. Obviously, the described embodiments are a part of the present invention. , but not all examples. Based on the embodiments of the present invention, all other embodiments obtained by persons of ordinary skill in the art without making creative efforts belong to the protection scope of the present invention.

[0032] Such as figure 1 As shown, the invention provides a hot melt adhesive film preparation process for bonding PP material, which is characterized in that, comprising steps,

[0033] S100, mix epoxy SBS, terpene resin, rosin resin, calcium stearate and catalyst, regulator, surfactant and nucleating agent at high temperature, and add sodium bisulfite continuously with stirring in the process o...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention discloses a preparation process of a hot melt adhesive film for bonding a PP material, which comprises the following steps: mixing terpene resin, rosin ester, calcium stearate, a catalyst, a regulator, a surfactant and a nucleating agent at high temperature, adding sodium hydrogen sulfite to obtain a viscous matrix, then fully stirring and mixing the modified polypropylene, epoxy SBS, metallocene polyolefin, a grafting material, paraffin and an antioxidant for reaction, then performing high-temperature polymerization to obtain a hot melt adhesive raw material, carrying out high-temperature contact gasification operation on the hot melt adhesive raw material, and synchronously coating the hot melt adhesive raw material with a viscous matrix in the high-temperature contact gasification process to obtain a preformed intermediate raw material, spraying the preformed intermediate raw material onto a Teflon mesh belt in a gap spraying manner, cooling and forming to obtain a hotmelt adhesive film, performing separate reaction on a tackifying material and a copolymerization raw material of the hot melt adhesive film, and finally finishing copolymerization mixing of the tackifying material and the copolymerization raw material during high-temperature extrusion, so that a viscous matrix is positioned on the surface of the hot melt adhesive film, and the hot melt adhesive film is obtained. The viscosity with a PP material is effectively improved.

Description

technical field [0001] The embodiments of the present invention relate to the technical field of hot-melt adhesive film preparation, and in particular to a preparation process and device for a hot-melt adhesive film bonded with PP material. Background technique [0002] Hot-melt adhesive film is a film product that is easy to industrialize by preparing hot-melt adhesive through calendering, casting, blown film, etc. Usually, hot melt adhesive films are prepared from highly saturated polyolefin materials. In order to increase the adhesive performance of hot melt adhesive films, additives that are conducive to adhesion are usually added, and PP materials are difficult-to-adhesive materials. Existing Most of the sticky PP materials are used to physically change the surface of the PP material or use other materials to activate the surface of the PP material. [0003] In the existing hot-melt adhesive film preparation process, the raw materials are mostly used to granulate after...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09J7/35C09J7/24C09J123/02C09J11/08C09J123/26C09J153/02C09J151/00B29C48/08B29C48/21B29C48/00
CPCC09J7/35C09J7/245C09J123/02C09J11/08B29C48/08B29C48/21B29C48/0021C08L23/26C08L53/025C08L91/06C08L51/006C08L45/00C08L93/04C08K5/098
Inventor 刘卫峰
Owner 江苏惠沣环保科技有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products