A kind of preparation method of copper/graphite/tin oxide electrical contact material

An electrical contact material, tin oxide technology, applied in tin oxide, contacts, circuits, etc., can solve the problems of short life and poor material reliability, and achieve the effects of low contact resistance, good high temperature lubrication performance of graphite, and high electrical conductivity

Active Publication Date: 2022-04-22
XI'AN POLYTECHNIC UNIVERSITY
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] The purpose of the present invention is to provide a preparation method of copper / graphite / tin oxide electrical contact material, which solves the problems of poor material reliability and short service life of existing copper-based electrical contact materials due to oxidation of the surface working layer

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0046] A kind of preparation method of copper / graphite / tin oxide electrical contact material, specifically implement according to the following steps:

[0047] Step 1, preparing tin oxide particles;

[0048] The specific process of step 1 is:

[0049] Step 1.1, fully dissolving tin chloride hydrate in formaldehyde solution, and obtaining tin chloride solution after fully stirring;

[0050] The concentration of tin chloride solution is 0.05mol / L.

[0051] Step 1.2, adding polyethylene glycol and sodium hydroxide solution to the tin chloride solution prepared in step 1.1, and stirring evenly to obtain a white turbid solution;

[0052] Step 1.3, quickly transfer the white turbid liquid to a sealed reaction kettle, and put it into an electric blast drying box for heat preservation;

[0053] The concentration of sodium hydroxide solution is 0.01mol / L, the molecular weight of polyethylene glycol is 600, and the addition amount of polyethylene glycol is 0.3g.

[0054] Step 1.3 Pu...

Embodiment 2

[0063] A kind of preparation method of copper / graphite / tin oxide electrical contact material, specifically implement according to the following steps:

[0064] Step 1, preparing tin oxide particles;

[0065] The specific process of step 1 is:

[0066] Step 1.1, fully dissolving tin chloride hydrate in formaldehyde solution, and obtaining tin chloride solution after fully stirring;

[0067] The concentration of tin chloride solution is 0.07mol / L.

[0068] Step 1.2, adding polyethylene glycol and sodium hydroxide solution to the tin chloride solution prepared in step 1.1, and stirring evenly to obtain a white turbid solution;

[0069] Step 1.3, quickly transfer the white turbid liquid to a sealed reaction kettle, and put it into an electric blast drying box for heat preservation;

[0070] The concentration of sodium hydroxide solution is 0.013mol / L, the molecular weight of polyethylene glycol is 600, and the addition amount of polyethylene glycol is 0.35g.

[0071] Step 1.3 ...

Embodiment 3

[0080] A kind of preparation method of copper / graphite / tin oxide electrical contact material, specifically implement according to the following steps:

[0081] Step 1, preparing tin oxide particles;

[0082] The specific process of step 1 is:

[0083] Step 1.1, fully dissolving tin chloride hydrate in formaldehyde solution, and obtaining tin chloride solution after fully stirring;

[0084] The concentration of tin chloride solution is 0.1mol / L.

[0085] Step 1.2, adding polyethylene glycol and sodium hydroxide solution to the tin chloride solution prepared in step 1.1, and stirring evenly to obtain a white turbid solution;

[0086] Step 1.3, quickly transfer the white turbid liquid to a sealed reaction kettle, and put it into an electric blast drying box for heat preservation;

[0087] The concentration of sodium hydroxide solution is 0.015mol / L, the molecular weight of polyethylene glycol is 600, and the addition amount of polyethylene glycol is 0.4g.

[0088] Step 1.3 Pu...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a preparation method of a copper / graphite / tin oxide electrical contact material, which is specifically implemented according to the following steps: step 1, preparing tin oxide particles; step 2, placing copper powder, graphite powder and tin oxide particles in a horizontal The planetary ball mill is fully mixed to obtain a uniformly mixed copper / graphite / tin oxide composite powder; step 3, the copper / graphite / tin oxide composite powder is pressed, sintered and annealed to obtain a copper / graphite / tin oxide electrical contact material ; It can solve the problems of high price and low silver recovery rate of existing silver-based electrical contact composite materials; it can also solve the problems of poor material reliability and short service life of existing copper-based electrical contact materials due to the oxidation of the surface working layer, and provide a kind of Silver-free electrical contact material with low contact resistance, high conductivity, anti-welding and arc extinguishing ability of the second phase current network path.

Description

technical field [0001] The invention belongs to the technical field of material preparation technology, and in particular relates to a preparation method of a copper / graphite / tin oxide electrical contact material. Background technique [0002] Electrical contact materials play a vital role in the use of electrical energy, distribution of electrical energy, and current conversion. They are widely used in various electrical contact systems, and their performance directly affects the service life and stability of low-voltage electrical appliances. [0003] In the research of electrical contact materials, the research on silver-based contact materials is the most in-depth, and silver-based electrical contact materials are also most widely used in low-voltage electrical appliances. So far, hundreds of silver-based electrical contact materials have been developed. However, the output of silver is limited, and nearly a quarter of silver output is used to manufacture electrical con...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C22C9/00C22C32/00C22C1/05C01G19/02H01H1/025H01H1/027
CPCC22C9/00C22C32/0084C22C1/05C01G19/02H01H1/025H01H1/027
Inventor 付翀王金龙侯锦丽闫贞常延丽梁苗苗刘德华孙扬帆
Owner XI'AN POLYTECHNIC UNIVERSITY
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com