A kind of aluminum-based composite material welding wire for arc additive manufacturing and preparation method thereof

An aluminum-based composite material and additive manufacturing technology, which is applied in the fields of additive manufacturing materials, material preparation, and metal materials, and can solve the problems of limiting the application of arc additive manufacturing technology, poor mechanical properties of printed parts, and difficult heat treatment of large components. To achieve the effect of inhibiting the growth of grains, improving strength and plasticity, and inhibiting the formation of dendrites

Active Publication Date: 2021-11-12
迈特李新材料(深圳)有限公司
View PDF9 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0003] However, the types of aluminum alloy welding wires that can be used for arc additive manufacturing are currently limited. After the existing aluminum alloy welding wires are made into products through arc additive manufacturing, the mechanical properties of the printed parts are poor (such as 5xxx series aluminum alloy welding wires) or after printing Heat treatment is required to improve the mechanical properties of parts (such as 2xxx series aluminum alloy welding wire)
This severely limits the application of arc additive manufacturing technology in the manufacture of large aluminum alloy components, because large components are often difficult to carry out overall heat treatment

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of aluminum-based composite material welding wire for arc additive manufacturing and preparation method thereof
  • A kind of aluminum-based composite material welding wire for arc additive manufacturing and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0031] An aluminum-based composite material welding wire for arc additive manufacturing, the composite material welding wire includes a matrix alloy and a nano-reinforcement phase distributed in the matrix alloy, and the matrix alloy contains the following components in mass percentage: Mg6. 5%, Cu 1.4%, Mn 0.8%, the balance is Al; the nano-enhanced phase is TiB 2 The particle size is 50-150nm, and its mass fraction in the composite material is 1.5%.

[0032] The preparation method of the aluminum-based composite material welding wire in this embodiment is: according to the composition of the matrix alloy and the TiB 2 Pure Al, pure Mg, pure Cu, Al-Mn master alloy and TiB required for particle mass fraction calculation 2 the quality of the particles. Melt pure Al at a temperature of 800°C, then add TiB 2 A mixture of granules and salt, where the salt consists of MgF 2 27wt.%, CaF 2 21wt.% and BaF 2 52 wt.%. After the salt is melted, the melt is mechanically stirred at...

Embodiment 2

[0034] An aluminum-based composite material welding wire for arc additive manufacturing, the composite material welding wire includes a matrix alloy and a nano-reinforcement phase distributed in the matrix alloy, and the matrix alloy contains the following components in mass percentage: Mg7. 5%, Cu 1.8%, Mn 0.8%, and the balance is Al; the nano reinforcement phase is TiC particles with a size of 40-200nm, and its mass fraction in the composite material is 1.0%.

[0035] The preparation method of the aluminum-based composite welding wire in this example is as follows: calculate the required mass of pure Al, pure Mg, pure Cu, Al-Mn master alloy and TiC particles according to the composition of the matrix alloy and the mass fraction of TiC particles. Melt pure Al at a temperature of 700°C, then add a mixture of TiC particles and salt, where the composition of the salt is KCl 54wt.%, NaCl 12wt.%, and NaF 4wt.%, CaCl 2 30 wt.%. After the salt is melted, the melt is mechanically s...

Embodiment 3

[0037] An aluminum-based composite material welding wire for arc additive manufacturing, the composite material welding wire includes a matrix alloy and a nano-reinforcement phase distributed in the matrix alloy, and the matrix alloy contains the following components in mass percentage: Mg9. 0%, Cu 2.5%, Mn 1.0%, and the balance is Al; the nano reinforcement phase is TiC particles with a size of 40-200nm, and its mass fraction in the composite material is 1.0%.

[0038] The preparation method of the aluminum-based composite welding wire in this example is as follows: calculate the required mass of pure Al, pure Mg, pure Cu, Al-Mn master alloy and TiC particles according to the composition of the matrix alloy and the mass fraction of TiC particles. Melt pure Al at a temperature of 720°C, then add a mixture of TiC particles and salt, where the composition of the salt is KCl 54wt.%, NaCl 12wt.%, and NaF 4wt.%, CaCl 2 30 wt.%. After the salt is melted, the melt is mechanically s...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
sizeaaaaaaaaaa
diameteraaaaaaaaaa
yield strengthaaaaaaaaaa
Login to View More

Abstract

The invention relates to an aluminum-based composite welding wire for arc additive manufacturing. The composite welding wire includes a base alloy and a nano-reinforced phase distributed in the base alloy, and the base alloy contains the following components by mass percentage : Mg 5.0%-15.0%, Cu 0.2%-3.0%, Mn 0.1%-1.0%, the balance is Al; the nano-reinforced phase is nano-particles, nano-wires, nano-tubes or nano-fibers, the nano-reinforced phase The material is ceramic, intermetallic or metal. By rationally designing the composition of the aluminum alloy welding wire, and introducing nanoparticles, the present invention is used for arc additive manufacturing. The printed parts can obtain better mechanical properties without heat treatment, thereby expanding the arc additive manufacturing. Application of technology in the field of aluminum alloy.

Description

technical field [0001] The invention relates to an aluminum-based composite material welding wire for arc additive manufacturing and a preparation method thereof, belonging to the technical fields of metal materials, additive manufacturing materials, and material preparation. Background technique [0002] Aluminum alloy has the advantages of high specific strength, specific stiffness, fatigue strength and excellent corrosion resistance. It is the material of choice for realizing lightweight structures and has broad applications in aerospace, automotive transportation and other fields. Additive manufacturing, also known as 3D printing, is a new manufacturing technology that uses software to segment digital models of parts, and stacks materials layer by layer from two-dimensional outlines according to the segmentation information to produce three-dimensional solid parts. This technology has broad application prospects in the manufacture of aluminum alloy parts and has received...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): B23K35/02B23K35/28B23K35/40C22C1/02C22C1/03C22C1/06C22C1/10C22C21/06C22C47/08C22C49/06C22C49/14C22F1/047
CPCB23K35/286B23K35/40B23K35/0261C22C21/06C22C49/06C22C49/14C22F1/047C22C1/03C22C1/026C22C1/06C22C1/1036C22C47/08C22C1/1047
Inventor 池元清刘伟清
Owner 迈特李新材料(深圳)有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com