Water-resistant anticorrosive coating and preparation method thereof

A technology of anti-corrosion coatings and inorganic fillers, applied in the direction of anti-corrosion coatings, coatings, etc., can solve the problems that performance stability needs to be further improved, the preparation process is complicated, and the preparation cost is high, and the preparation cost is low, the source of raw materials is wide, and the curing time is long. Effect

Inactive Publication Date: 2021-03-09
魏建林
View PDF2 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the coating has many components, the preparation process is complicated, the preparation cost is high, and the antagonism between the components is easy to occur, and the performance stability needs to be further improved.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0027] A kind of water-resistant anticorrosion paint, it is characterized in that, is made up of following each component by weight: 10 parts of amino-modified hyperbranched SBS, glycidyl methacrylate / allyl pentafluorobenzene / 3-( 4-fluorophenyl)-2-acrylonitrile / allylphenylsulfone / vinyltriethoxysilane copolymer 40 parts, inorganic filler 15 parts, initiator 0.5 part, dispersant 1 part, film-forming aid 1 part share.

[0028] The film-forming aid is polyethylene glycol; the dispersant is triethylhexyl phosphoric acid; the initiator is azobisisobutyronitrile; the inorganic filler is iron red; the particle diameter of the inorganic filler is It is 1200 mesh.

[0029] The preparation method of the glycidyl methacrylate / allyl pentafluorobenzene / 3-(4-fluorophenyl)-2-acrylonitrile / allyl phenyl sulfone / vinyl triethoxysilane copolymer, Including the following steps: glycidyl methacrylate, allyl pentafluorobenzene, 3-(4-fluorophenyl)-2-acrylonitrile, allyl phenyl sulfone, vinyl trietho...

Embodiment 2

[0035] A kind of water-resistant anticorrosion paint, it is characterized in that, is made up of following each component by weight: 13 parts of amino-modified hyperbranched SBS, glycidyl methacrylate / allyl pentafluorobenzene / 3-( 4-fluorophenyl)-2-acrylonitrile / allylphenylsulfone / vinyltriethoxysilane copolymer 42 parts, inorganic filler 17 parts, initiator 0.7 parts, dispersant 1.5 parts, film-forming aid 1.5 parts share.

[0036] The film-forming aid is ethylene glycol ether; the dispersant is sodium lauryl sulfate; the initiator is azobisisoheptanonitrile; the inorganic filler is titanium dioxide; The diameter is 1300 mesh.

[0037] The preparation method of the glycidyl methacrylate / allyl pentafluorobenzene / 3-(4-fluorophenyl)-2-acrylonitrile / allyl phenyl sulfone / vinyl triethoxysilane copolymer, Including the following steps: glycidyl methacrylate, allyl pentafluorobenzene, 3-(4-fluorophenyl)-2-acrylonitrile, allyl phenyl sulfone, vinyl triethoxysilane, azo Diisobutyronit...

Embodiment 3

[0043] A kind of water-resistant anticorrosion coating, it is characterized in that, is made up of each component by weight as follows: Amino-modified hyperbranched SBS 15 parts, glycidyl methacrylate / allyl pentafluorobenzene / 3-( 45 parts of 4-fluorophenyl)-2-acrylonitrile / allylphenylsulfone / vinyltriethoxysilane copolymer, 20 parts of inorganic filler, 1 part of initiator, 2 parts of dispersant, 2 parts of film-forming aid share.

[0044] The film-forming aid is propylene glycol phenyl ether; the dispersant is methyl amyl alcohol; the initiator is azobisisobutyronitrile; the inorganic filler is talcum powder; the particle diameter of the inorganic filler is 1350 head.

[0045] The preparation method of the glycidyl methacrylate / allyl pentafluorobenzene / 3-(4-fluorophenyl)-2-acrylonitrile / allyl phenyl sulfone / vinyl triethoxysilane copolymer, Including the following steps: glycidyl methacrylate, allyl pentafluorobenzene, 3-(4-fluorophenyl)-2-acrylonitrile, allyl phenyl sulfone,...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
particle size (mesh)aaaaaaaaaa
Login to view more

Abstract

The invention discloses a water-resistant anticorrosive coating which is characterized by being prepared from the following components in parts by weight: 10-20 parts of amino modified hyperbranched SBS, 40-50 parts of glycidyl methacrylate/allyl pentafluorobenzene/3- (4-fluorophenyl) -2-acrylonitrile/allyl phenyl sulfone/vinyl triethoxysilane copolymer, 15-25 parts of an inorganic filler, 0.5-1.5parts of an initiator, 1-3 parts of a dispersant and 1-3 parts of a film-forming assistant. The invention also discloses a preparation method of the water-resistant anticorrosive coating. The waterproof anticorrosive coating disclosed by the invention has the advantages of excellent comprehensive performance, obvious waterproof anticorrosive effect, good performance stability, weather resistance,workability, adaptability and durability, and strong adhesion with a base material.

Description

technical field [0001] The invention relates to the technical field of coatings, in particular to a water-resistant and anti-corrosion coating and a preparation method thereof. Background technique [0002] In recent years, with the rapid development of world science and technology and social production, the use of metal materials has increased significantly, and they are known as the "skeleton of industry". Metal materials are widely used in large-scale steel equipment, components, pipelines and other steel structure facilities due to their excellent mechanical properties. They are the guarantee of the safety and quality of national key projects and large-scale projects. However, metal materials are easy to corrode, especially in coastal and inland hot and humid environments, because the environment contains harmful corrosive media such as chlorides and sulfides, the problem of metal material corrosion is particularly prominent, which in turn affects its service life, and t...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C09D125/18C09D153/02C09D5/08C09D7/61C08F212/14C08F220/32C08F220/50C08F228/02C08F230/08
CPCC08K2003/2241C08K2003/2272C08K2003/3045C09D5/08C09D143/04C09D7/61C08F212/20C08L53/025C08K3/22C08K3/34C08K3/30C08K13/02C08F220/325C08F220/50C08F228/02C08F230/085
Inventor 魏建林
Owner 魏建林
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap