A step-voltage-based compact fe 2 o 3 Film Preparation Method

A step voltage, fe2o3 technology, applied in electrodes, electrolysis components, electrolysis process, etc., can solve problems such as cumbersome processes and non-dense films

Inactive Publication Date: 2021-04-06
NAT UNIV OF DEFENSE TECH
View PDF5 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] To solve the traditional Fe 2 o 3 Thin film is not dense, and the technical problem of loaded down with trivial details of procedure, one of purpose of the present invention is to provide a kind of compact Fe based on step voltage 2 o 3 The preparation method of thin film, this preparation method is simple and easy and cost is low, can obtain dense Fe 2 o 3 film

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A step-voltage-based compact fe <sub>2</sub> o <sub>3</sub> Film Preparation Method
  • A step-voltage-based compact fe <sub>2</sub> o <sub>3</sub> Film Preparation Method
  • A step-voltage-based compact fe <sub>2</sub> o <sub>3</sub> Film Preparation Method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0072] Preparation of Fe by step voltage 2 o 3 film

[0073] 1) Use acetone and deionized water to ultrasonically clean the FTO conductive glass, repeat it several times until it is cleaned, and then dry it for later use.

[0074] 2) Weigh a certain amount of boric acid, ascorbic acid, ferrous sulfate heptahydrate and PEG20000, dissolve them in deionized water, and prepare the required electrolyte. Wherein the molar concentration of boric acid is 0.2mol . L -1 ; The molar concentration of ascorbic acid is 0.0006mol . L -1 ; The molar concentration of ferrous sulfate heptahydrate is 0.2mol . L -1 ; The molar concentration of PEG20000 is 0.0012mol . L -1 .

[0075] A three-electrode electrolysis system composed of FTO conductive glass, graphite electrode, Ag / AgCl electrode and the above-mentioned electrolyte is adopted, and a step voltage deposition process is used to generate electricity on the surface of FTO conductive glass by changing the applied voltage between FT...

Embodiment 2

[0116] Preparation of Fe by step voltage 2 o 3 film

[0117] 1) Use acetone and deionized water to ultrasonically clean the FTO conductive glass, repeat it several times until it is cleaned, and then dry it for later use.

[0118] 2) Weigh a certain amount of boric acid, ascorbic acid, ferrous sulfate heptahydrate and PEG20000, dissolve them in deionized water, and prepare the required electrolyte. Wherein the molar concentration of boric acid is 0.2mol . L -1 ; The molar concentration of ascorbic acid is 0.0006mol . L -1 ; The molar concentration of ferrous sulfate heptahydrate is 0.2mol . L -1 ; The molar concentration of PEG20000 is 0.0012mol . L -1 .

[0119] A three-electrode electrolysis system composed of FTO conductive glass, graphite electrode, Ag / AgCl electrode and the above-mentioned electrolyte is adopted, and a step voltage deposition process is used to generate electricity on the surface of FTO conductive glass by changing the applied voltage between FT...

Embodiment 3

[0123] Preparation of Fe by step voltage 2 o 3 film

[0124] 1) Use acetone and deionized water to ultrasonically clean the FTO conductive glass, repeat it several times until it is cleaned, and then dry it for later use.

[0125] 2) Weigh a certain amount of boric acid, ascorbic acid, ferrous sulfate heptahydrate and PEG20000, dissolve them in deionized water, and prepare the required electrolyte. Wherein the molar concentration of boric acid is 0.2mol . L -1 ; The molar concentration of ascorbic acid is 0.0006mol . L -1 ; The molar concentration of ferrous sulfate heptahydrate is 0.2mol . L -1 ; The molar concentration of PEG20000 is 0.0012mol . L -1 .

[0126] A three-electrode electrolysis system composed of FTO conductive glass, graphite electrode, Ag / AgCl electrode and the above-mentioned electrolyte is adopted, and a step voltage deposition process is used to generate electricity on the surface of FTO conductive glass by changing the applied voltage between FT...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
thicknessaaaaaaaaaa
electrical resistanceaaaaaaaaaa
thicknessaaaaaaaaaa
Login to View More

Abstract

The invention discloses a dense Fe based on step voltage 2 o 3 The preparation method of the film includes cleaning the conductive substrate, using organic solvents and deionized water to ultrasonically clean the conductive substrate, repeating it several times until it is cleaned, and then drying it for later use; step voltage electrochemical deposition, using a three-electrode electrolysis system, through The applied voltage is switched between the working electrode and the counter electrode, and a dense Fe film is electrochemically deposited on the surface of the working electrode; oxidation treatment, the prepared dense Fe film is placed in a tube furnace, and calcined in an air atmosphere, get dense Fe 2 o 3 film. The Fe prepared by the method of the present invention 2 o 3 The structure of the thin film is dense and has high photoelectric conversion efficiency, which can be used as the preferred material for photoanodes in catalytic systems.

Description

technical field [0001] The invention belongs to the technical field of metal thin film preparation, in particular to a step voltage-based dense Fe 2 o 3 The method of film preparation. Background technique [0002] Using photoelectrochemical methods to convert solar energy into sustainable clean energy is our goal. In 1972, "Nature" magazine first reported the use of TiO 2 As a photoanode for photoelectrocatalytic water splitting. Anatase TiO 2 Bandgap width of 3.2 eV, rutile TiO 2 The bandgap width is 3.0 eV, and only ultraviolet light can excite its electron-hole separation, which cannot fully utilize sunlight. In many semiconductors, Fe 2 o 3 It has the following advantages and becomes one of the preferred materials for photoanodes to catalyze water oxidation: 1) small band gap, with a band gap of 2.2 eV, and visible light with a wavelength of 560 nm can excite its electron-hole separation; 2) cheap price; 3 ) has good stability and is not easily corroded by ligh...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C25B11/077C25B11/087C25D3/20C25D5/48C23C8/14
CPCC23C8/14C25D3/20C25D5/48
Inventor 李晓霞王晓农张敬岩赵大鹏白秀军吴梦醒顾有林解博
Owner NAT UNIV OF DEFENSE TECH
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com