Spreading type iron-carbon composite filler powder for concrete and preparation method of spreading type iron-carbon composite filler powder

A composite filler and concrete technology, applied in chemical instruments and methods, water/sludge/sewage treatment, water pollutants, etc., can solve the problems of large manpower, material resources and financial resources, complex and harsh preparation process, and cost of filling laying, etc., and achieve the effect. Strong, high processing efficiency, low price effect

Active Publication Date: 2021-03-23
安徽瑞和新材料有限公司 +1
View PDF6 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The purpose of the present invention is to solve the problem of complicated and harsh filler preparation process, huge manpower, material and financial resources for filler laying, and the concrete poured in artificial wetland and other structures can not only meet the requirements of high anti-seepage and crack resistance, but also purify water quality, Removing harmful substances such as nitrogen and phosphorus in sewage, etc., proposes the application of a spreadable iron-carbon composite filler powder for concrete, which can be applied as long as the concrete area where sewage passes through

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Spreading type iron-carbon composite filler powder for concrete and preparation method of spreading type iron-carbon composite filler powder

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0022] A spreadable iron-carbon composite filler powder for concrete is composed of the following raw materials in parts by weight: 30 parts of iron-carbon, 30 parts of zeolite, 20 parts of ceramsite, 10 parts of anthracite and 10 parts of volcanic rock. Put each component into a crusher for crushing, then into a pulverizer, pass through a 1mm sieve, and finally add each component into a compounding tank, stir evenly to obtain the filler powder. After the concrete has just been poured and put into the mold, the prepared iron-carbon composite filler powder is evenly sprinkled on the upstream surface of the concrete, with a thickness of 5mm, and then wait for the concrete to harden, and the powder is firmly bonded to the concrete surface.

Embodiment 2

[0024] A spreadable iron-carbon composite filler powder for concrete is composed of the following raw materials in parts by weight: 30 parts of iron-carbon, 40 parts of zeolite, 10 parts of ceramsite, 10 parts of anthracite and 10 parts of volcanic rock. Put each component into a crusher for crushing, then into a pulverizer, pass through a 1mm sieve, and finally add each component into a compounding tank, stir evenly to obtain the filler powder. After the concrete has just been poured and put into the mold, the prepared iron-carbon composite filler powder is evenly sprinkled on the upstream surface of the concrete, with a thickness of 5mm, and then wait for the concrete to harden, and the powder is firmly bonded to the concrete surface.

Embodiment 3

[0026] A spreadable iron-carbon composite filler powder for concrete is composed of the following raw materials in parts by weight: 32 parts of iron-carbon, 30 parts of zeolite, 12 parts of ceramsite, 10 parts of anthracite, and 16 parts of volcanic rock. Put each component into a crusher for crushing, then into a pulverizer, pass through a 1mm sieve, and finally add each component into a compounding tank, stir evenly to obtain the filler powder. After the concrete has just been poured and put into the mold, the prepared iron-carbon composite filler powder is evenly sprinkled on the upstream surface of the concrete, with a thickness of 5mm, and then wait for the concrete to harden, and the powder is firmly bonded to the concrete surface.

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention discloses spreading type iron-carbon composite filler powder for concrete. The spreading type iron-carbon composite filler powder is prepared from 30-40 parts of iron carbon, 30-40 partsof zeolite, 10-20 parts of ceramsite, 10-20 parts of anthracite and 10-20 parts of volcanic rock. The preparation method comprises the following steps: sequentially putting the components into a crusher and a pulverizer for treatment, sieving with a 1mm sieve, adding the components into a compounding tank, and uniformly stirring to obtain the filler powder. The method is wider in application range, and can be applied to all concrete areas where sewage passes through; concrete poured into structures such as the constructed wetland can meet the high requirements for seepage prevention, crack resistance and the like, meanwhile, the capabilities of purifying water, removing harmful substances such as nitrogen and phosphorus in sewage and the like are achieved, and multiple purposes can be achieved.

Description

technical field [0001] The invention belongs to the field of sewage treatment technology, composite filler and concrete engineering, and in particular relates to the application of a spread-type iron-carbon composite filler powder for concrete. Background technique [0002] After the nitrogen and phosphorus nutrients in the sewage enter relatively closed waters, they can easily lead to eutrophication of water bodies under sunlight. Throughout the world, almost all lakes and other recreational water bodies have varying degrees of eutrophication, and most areas are quite serious. As an emerging sewage treatment process, constructed wetland has the characteristics of simple maintenance, good effect, and wide application. It is a wetland treatment system that has been widely studied and applied in the world. Constructed wetlands remove pollutants in water through various methods. For example, fillers remove pollutants in sewage through physical and chemical actions such as adso...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C04B18/02C02F1/00C02F1/58C02F101/10C02F101/16
CPCC04B40/0039C02F1/00C02F1/58C02F2101/16C02F2101/105C04B14/022C04B14/34C04B14/047C04B18/027C04B14/14
Inventor 崔征王达道徐志峰祝烨然唐修生李建彭涛
Owner 安徽瑞和新材料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com