A ceramic wine bottle, vanadium yellow technology is applied in the field of vanadium yellow matte decorative glaze formulations for ceramic wine bottles, which can solve the problems of excessive heavy metals, low firing temperature, color fading, etc. Effect

Inactive Publication Date: 2021-04-20
湖南华联君窑艺术瓷有限公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

Similar to the field of the present invention that has been used in life, it can be used as an utensil for us to eat and drink; it is very common and very practical; it has obvious advantages compared with plastic and metal utensils, and it is healthier and safer; today's market On the other hand, the existing ceramic color glazes have some defects, such as low firing temperature, discoloration, heavy metals exceeding the standard, etc., it is necessary to design a formula and method of vanadium yellow matte decorative glaze for ceramic wine bottles

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Formula and method of ceramic wine bottle vanadium yellow matte decorative glaze

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0029]Ceramic wine bottle vanadium yellow matte decorative glaze formulation, formulation including: potassium longite, quartz, square alumina, silica grayite, talc, alumina, zirconium silicate, kaolin, black material, vanadium yellow material, 镨 yellow material and Zirconium iron red, the mass content of each component is: 30 parts of potassium longite, 20 pieces of quartz, 5 serviles, 10 parts of silica amphitone, 15 talc, 5 parts of alumina, 5 parts of zirconium silicate, 10 parts of kaolin, 1 part of black material, 5 parts of vanadium yellow material, 3 pieces of yellow-yellowed materials and 1 zirconia red.

[0030]A method of ceramic wine bottle vanadium yellow matte decorative glaze formulation, including step one, material selection; step two, mix ball mill; step three, screen processing; step four, glaze the kiln; Step 5, storage place;

[0031]In the above steps, in the above steps, the contents of each component are: 30 parts of potassium waith, 20 parts of quartz, 5 parts of ...

Embodiment 2

[0043]Ceramic wine bottle vanadium yellow matte decorative glaze formulation, formulation including: potassium longite, quartz, square alumina, silica grayite, talc, alumina, zirconium silicate, kaolin, black material, vanadium yellow material, 镨 yellow material and Zirconium iron red, the mass content of each component is: 35 pieces of potassium waith, 15 pieces of quartz, 5 square solutions, 10 parts of silica amphitone, 15 talc, 5 parts of alumina, 5 parts of zirconium silicate, 10 parts of kaolin, 1 part of black material, 5 parts of vanadium yellow material, 3 pieces of yellow-yellowed materials and 1 zirconia red.

[0044]A method of ceramic wine bottle vanadium yellow matte decorative glaze formulation, including step one, material selection; step two, mix ball mill; step three, screen processing; step four, glaze the kiln; Step 5, storage place;

[0045]In the above steps, in accordance with the contents of the components, the contents of each component are: 35 parts of potassium ...

Embodiment 3

[0057]Ceramic wine bottle vanadium yellow matte decorative glaze formulation, formulation including: potassium longite, quartz, square alumina, silica grayite, talc, alumina, zirconium silicate, kaolin, black material, vanadium yellow material, 镨 yellow material and Zirconium iron red, the mass content of each component is: 40 parts of potassium longshite, 10 parts of quartz, 5 partial flu solution, 10 parts of silica amphitite, 15 talc, 5 parts of alumina, 5 parts of zirconium silicate, 10 parts of kaolin, 1 part of black material, 5 parts of vanadium yellow material, 3 pieces of yellow-yellowed materials and 1 zirconia red.

[0058]A method of ceramic wine bottle vanadium yellow matte decorative glaze formulation, including step one, material selection; step two, mix ball mill; step three, screen processing; step four, glaze the kiln; Step 5, storage place;

[0059]In the above steps, in accordance with the contents of each component, 40 parts of potassium waith, 10 parts of quartz, 5 p...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses a ceramic wine bottle vanadium yellow matte decorative glaze formula and method. The formula comprises potassium feldspar, quartz, calcite, wollastonite, talc, aluminum oxide, zirconium silicate, kaolin, a black pigment, a vanadium yellow pigment, a praseodymium yellow pigment and zirconium iron red. The glaze is prepared from, by mass, 30-40 parts of potassium feldspar, 10-20 parts of quartz, 5-10 parts of calcite, 10-15 parts of wollastonite, 15-20 parts of talc, 5-10 parts of aluminum oxide, 3-7 parts of zirconium silicate, 10-15 parts of kaolin, 0.5-1 part of black pigment, 5-10 parts of vanadium yellow pigment, 3-6 parts of praseodymium yellow pigment and 1-3 parts of ferrozirconium red. After being fired into porcelain at the high temperature of 1,260-1,280 DEG C, the porcelain is pure in glaze color, smooth in glaze surface, free of fading, free of heavy metal exceeding, resistant to chemical corrosion, resistant to abrasion, good in product quality, high in grade, mild as jade and good in grade, and is practical, safe and guaranteed as a wine container; the glaze is fine and smooth, the glaze surface is smooth like jade, the pressure resistance is high, and the glaze surface hardness is good.

Description

Technical field[0001]The present invention relates to ceramic wine bottles of vanadium yellow matte decorative glaze formulation technology, which is specifically a ceramic wine bottle vanadium yellow matte decorative glaze formulation and method.Background technique[0002]Ceramics are the national quintesses of my Chinese nation, and they have been famous in the whole world since ancient times. In this field of traditional crafts, there are thousands of different forms and raw materials formulations. In Jingde Town, Jiangxi, Guangdong Chaozhou, Fujian Dehua, Shandong Zibo, Hunan Yiling and other places have a variety of different ceramic artworks; Hundred flowers, light and beautiful, highlight my Chinese national wisdom;[0003]The color glaze is a kind of ceramic decorative glaze that has not falundated for thousands of years; the market is very common, and the form of expression and decorative types should have. In the field that has been used in life, it can be used as a piece of ...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C03C8/00C04B41/86
Inventor 屈良奇吴丹
Owner 湖南华联君窑艺术瓷有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com