Rapid solid solution and rapid heating aging heat treatment method

An aging heat treatment and solution heat treatment technology, applied in the field of material heat treatment, can solve the problems of poor heating reliability of heat treatment equipment, long heating time, low qualified product rate, etc., to achieve maximum furnace loading and mass production requirements, reduce The total time of solution and aging holding time and the effect of improving heat treatment efficiency

Pending Publication Date: 2021-04-30
山西柴油机工业有限责任公司
View PDF0 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

It can solve the problem of poor quality stability, low qualified product rate, low hardness (or low mechanical properties) and poor consistency of austenitic stainless steel solution and aging heat treatment, long heating time, low efficiency, poor heating reliability of heat treatment equipment and the use of high temperature components Theoretical and practical problems of "one long, one high, three different and five low" unique heat treatment technology such as low life and high cost

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Rapid solid solution and rapid heating aging heat treatment method
  • Rapid solid solution and rapid heating aging heat treatment method
  • Rapid solid solution and rapid heating aging heat treatment method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0050] Exemplary embodiments of the present disclosure will be described in more detail below with reference to the accompanying drawings. Although exemplary embodiments of the present disclosure are shown in the drawings, it should be understood that the present disclosure may be embodied in various forms and should not be limited by the embodiments set forth herein. Rather, these embodiments are provided for more thorough understanding of the present disclosure and to fully convey the scope of the present disclosure to those skilled in the art.

[0051] Such as figure 2 As shown, the embodiment of the present invention proposes a sufficient solid solution and high temperature alternating aging heat treatment method, including: step 21, a rapid solution heat treatment process; and step 22, a rapid temperature-rising aging heat treatment process.

[0052] The process of the method is as follows: the first part of rapid solution heat treatment is firstly carried out, and fina...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

No PUM Login to view more

Abstract

The invention provides a rapid solid solution and rapid heating aging heat treatment method. The rapid solid solution and rapid heating aging heat treatment method comprises the steps of a rapid solid solution heat treatment process and a rapid heating aging heat treatment process. According to the scheme, the specific heat treatment technology theory and practice problems of poor quality stability, low qualified rate, low hardness, low mechanical property, poor consistency, long heating time, low efficiency, poor heating reliability of heating equipment, short service life of high-temperature components and high cost and the like of austenitic stainless steel heat treatment are solved.

Description

technical field [0001] The invention relates to the technical field of material heat treatment, in particular to a rapid solid solution and rapid temperature rise aging heat treatment method. Background technique [0002] The heat treatment principles of austenitic stainless steel and alloy structural steel are completely different: alloy structural steel can undergo high-temperature austenite transformation under high temperature conditions. Therefore, alloy structural steel can easily increase the hardness of the material through quenching and tempering heat treatment methods ( or mechanical properties); and austenitic stainless steel cannot undergo high-temperature austenite structural transformation under high temperature conditions (only the strengthening phase of alloying elements can be dissolved and precipitated), so it is extremely difficult for austenitic stainless steel to undergo solid solution and aging heat treatment. Amplitude increases material hardness (or m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): C21D1/78C21D6/00
CPCC21D1/78C21D6/00C21D2211/001
Inventor 李志广张建颖孔冰李全平陈森刘继林
Owner 山西柴油机工业有限责任公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap