A kind of preparation method and application of highly stable zinc-iodine battery and electrode material

A technology of electrode material and battery positive electrode, which is applied in the direction of battery electrodes, positive electrodes, secondary batteries, etc., can solve problems such as hindering development and application, capacity and coulombic efficiency reduction, etc., to improve poor cycle performance, slow down the shuttle effect, and reduce solubility Effect

Active Publication Date: 2022-02-11
SHANDONG UNIV
View PDF7 Cites 0 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, the redox reaction and shuttling effect of I3- / I- ions in the positive electrode of zinc-iodine batteries usually lead to a gradual decrease in capacity and coulombic efficiency during cycling, which seriously hinders its further development and application.

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • A kind of preparation method and application of highly stable zinc-iodine battery and electrode material
  • A kind of preparation method and application of highly stable zinc-iodine battery and electrode material

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0040] A highly stable zinc-iodine battery and its preparation method and application, comprising the following steps:

[0041] (1) Preparation of covalent organic framework compound: the covalent organic framework compound of the composite material is polyimide covalent organic framework compound COF-LZU1.

[0042] 0.30 mmol of 1,3,5-triformylbenzene and 0.45 mmol of 1,4-diaminobenzene were dissolved in 3 mL of 1,4-dioxane, and then 0.6 mL of 3 mol L-1 dilute acetic acid was added to the mixture , stirred on a magnetic stirrer for 5 days, then the obtained product was centrifuged and washed 3 times in a centrifuge at 2000r / min with dimethylformamide and tetrahydrofuran, and then the powder was kept in a vacuum oven at 80 degrees Celsius for 12 hours, and dried , to obtain COF-LZU1 powder.

[0043] The active material was mixed with conductive carbon black and PVDF binder at a ratio of 6:2:2 for 12 hours, then coated on carbon paper, kept in a vacuum oven at 40 degrees Celsiu...

Embodiment 2

[0048] A highly stable zinc-iodine battery and its preparation method and application, comprising the following steps:

[0049] (1) Preparation of covalent organic framework compound: the covalent organic framework compound of the composite material is polyimide covalent organic framework compound COF-LZU1, and the steps are as described in Example 1.

[0050] (2) After grinding the elemental iodine with a mortar, weigh 0.1g elemental iodine powder, grind it evenly with 0.1g COF-LZU1 powder, then put it into a tube furnace, and raise the temperature at a constant heating rate of 2°C / min to 80 degrees Celsius, under the protection of argon for 12 hours, the COF-LZU1 zinc-iodine battery positive electrode loaded with iodine is obtained.

[0051] The active material and MXene colloidal solution are mixed evenly in a ratio of 1:1, filtered, and kept in a vacuum oven at 40 degrees Celsius for 24 hours, and dried to obtain a positive electrode sheet, in which MXene acts as a conduct...

Embodiment 3

[0054] A highly stable zinc-iodine battery and its preparation method and application, comprising the following steps:

[0055] (1) Preparation of covalent organic framework compound: the covalent organic framework compound of the composite material is polyimide covalent organic framework compound COF-LZU1, and the steps are as described in Example 1.

[0056] (2) After grinding the iodine element with a mortar, weigh 0.1g of zinc iodide powder, grind it with 0.1g of COF-LZU1 powder evenly, then put it into a tube furnace, and raise the temperature at a constant heating rate of 2°C / min To 80 degrees Celsius, under the protection of argon for 12 hours, the COF-LZU1 zinc iodide loaded zinc iodide battery cathode active material is obtained.

[0057] (3) The active material and the MXene colloidal solution are mixed evenly in a ratio of 1:1, filtered, and kept in a vacuum oven at 40 degrees Celsius for 24 hours, and dried to obtain a positive electrode sheet, in which MXene acts ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
particle diameteraaaaaaaaaa
Login to View More

Abstract

The invention relates to a highly stable zinc-iodine battery and a preparation method and application of an electrode material. The electrode materials include covalent organic framework compounds and active iodine, and the active iodine is supported in the pore structure formed by the covalent organic framework compounds. The preparation method is as follows: after mixing the covalent organic framework compound and active iodine, heat treatment is carried out in a tube furnace to obtain a composite material. The iodine cathode is effectively stabilized, and the electrochemical performance of the zinc-iodine battery is improved. It has good electrochemical performance, and has good capacity and coulombic efficiency retention characteristics during the cycle process.

Description

technical field [0001] The invention belongs to the technical field of battery cathode material iodine, and in particular relates to a preparation method and application of a highly stable zinc-iodine battery and electrode material. Background technique [0002] The information disclosed in this background section is only intended to increase the understanding of the general background of the present invention, and is not necessarily taken as an acknowledgment or any form of suggestion that the information constitutes the prior art already known to those skilled in the art. [0003] With the rapid development of microelectronic information technology, the demand for digital electronic products, electric tools, electric vehicles, and large-scale energy storage is increasing. Based on the current urgent demand for green, efficient, and practical energy storage materials, high-performance and large-capacity The development of rechargeable and dischargeable batteries for seconda...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): H01M4/62H01M4/38H01M4/02H01M10/36
CPCH01M4/388H01M4/628H01M4/02H01M10/365H01M2004/028H01M2004/021Y02E60/10
Inventor 冯金奎田园安永灵
Owner SHANDONG UNIV
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Patsnap Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Patsnap Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com