Marble-imitated reflective heat-insulating inorganic multicolor paint and preparation method thereof

A technique of imitating marble and colorful paint, applied in the field of paint, can solve the problems of inability to form films and gels, and achieve good coloring ability, good fire resistance, water whitening resistance, and performance optimization

Inactive Publication Date: 2021-07-23
四川嘉宝莉涂料有限公司
View PDF3 Cites 2 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

[0005] Aiming at the above-mentioned problems that the existing inorganic paint and reflective heat-insulating paint are directly added to the imitation marble paint, there are no film-forming and gelling problems respectively, the present invention provides a marble-like reflective heat-insulating inorganic colorful paint

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Marble-imitated reflective heat-insulating inorganic multicolor paint and preparation method thereof
  • Marble-imitated reflective heat-insulating inorganic multicolor paint and preparation method thereof

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0032] Preparation of raw materials for base paint: 25kg of water, 0.1kg of cellulose, 0.1kg of defoamer, 0.3kg of dispersant, 12kg of reflective heat-insulating titanium dioxide, 5kg of heavy calcium powder, 5kg of talcum powder, 5kg of barium sulfate, and 12kg of inorganic silicone resin , reflective heat insulation emulsion 5kg, thickener 0.1kg, fungicide 0.1kg;

[0033] Preparation of raw materials for the continuous phase: 10kg of water, 50kg of silicon-acrylic emulsion, 0.5kg of fungicide, 3kg of film-forming aid, 3kg of antifreeze, 0.1kg of pH regulator and 0.1kg of thickener;

[0034] Preparation of raw materials for granulation protective rubber liquid: 90kg of water, 5kg of magnesium aluminum silicate and 0.1kg of fungicide;

[0035] The preparation method of the marble-like reflective heat-insulating inorganic colorful paint is as follows:

[0036] S1: Preparation of base paint

[0037] S1-1: Add water, cellulose, defoamer and dispersant into the mixing tank, and ...

Embodiment 2

[0049] Preparation of raw materials for base paint: 28kg of water, 0.2kg of cellulose, 0.18kg of defoamer, 0.5kg of dispersant, 17kg of reflective heat-insulating titanium dioxide, 8kg of heavy calcium powder, 8kg of talcum powder, 7kg of barium sulfate, and 18kg of inorganic silicone resin , reflective heat insulation emulsion 8kg, thickener 0.4kg, fungicide 0.3kg;

[0050] Preparation of raw materials for the continuous phase: 15kg of water, 55kg of silicon-acrylic emulsion, 0.8kg of fungicide, 3.4kg of film-forming aid, 4kg of antifreeze, 0.12kg of pH regulator and 0.3kg of thickener;

[0051] Preparation of raw materials for granulating protective rubber liquid: 93kg of water, 8kg of magnesium aluminum silicate and 0.17kg of fungicide;

[0052] The preparation method of the marble-like reflective heat-insulating inorganic colorful paint is as follows:

[0053] S1: Preparation of base paint

[0054] S1-1: Add water, cellulose, defoamer and dispersant into the mixing tank, a...

Embodiment 3

[0066] Preparation of raw materials for base paint: 35kg of water, 0.3kg of cellulose, 0.2kg of defoamer, 0.8kg of dispersant, 20kg of reflective heat-insulating titanium dioxide, 10kg of heavy calcium powder, 10kg of talcum powder, 10kg of barium sulfate, and 20kg of inorganic silicone resin , reflective heat insulation emulsion 10kg, thickener 0.5kg, fungicide 0.5kg;

[0067] Preparation of raw materials for the continuous phase: 23kg of water, 67kg of silicon-acrylic emulsion, 1kg of fungicide, 4kg of film-forming aid, 6kg of antifreeze, 0.2kg of pH regulator and 0.5kg of thickener;

[0068] Preparation of raw materials for granulating protective rubber liquid: 95kg of water, 10kg of magnesium aluminum silicate and 0.2kg of fungicide;

[0069] The preparation method of the marble-like reflective heat-insulating inorganic colorful paint is as follows:

[0070] S1: Preparation of base paint

[0071] S1-1: Add water, cellulose, defoamer and dispersant into the mixing tank, a...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

No PUM Login to View More

Abstract

The invention discloses marble-imitated reflective heat-insulating inorganic multi-color paint and a preparation method thereof. The multi-color paint comprises the following components in parts by weight: 20-30 parts of a continuous phase, 20-30 parts of a granulation protection glue liquid and 40-60 parts of base paint, wherein the basic paint is mainly prepared from the following components in parts by weight: 25 to 35 parts of water, 0.1 to 0.3 part of cellulose, 0.1 to 0.2 part of a de-foaming agent, 0.3 to 0.8 part of a dispersing agent, 12 to 20 parts of reflective thermal insulation titanium dioxide, 5 to 10 parts of heavy calcium powder, 5 to 10 parts of talcum powder, 5 to 10 parts of barium sulfate, 12 to 20 parts of inorganic silicon resin, 5 to 10 parts of reflective thermal insulation emulsion, 0.1 to 0.5 part of a thickening agent and 0.1 to 0.5 part of a sterilizing agent. The decoration effect is achieved, and the heat insulation effect is achieved by reflecting light; the inorganic silicon resin and the reflective heat-insulation emulsion are compounded, so that the reflective heat-insulation titanium dioxide does not become white at the initial stage, and the reflective heat-insulation titanium dioxide has good tinting ability.

Description

technical field [0001] The invention belongs to the technical field of paints, and in particular relates to a marble-like reflective heat-insulating inorganic colorful paint and a preparation method thereof. Background technique [0002] At present, the popular imitation marble paints on the market all have realistic imitation stone effects and excellent weather resistance. With the country's ever-increasing energy-saving and environmental protection requirements, colorful paints need to meet decorative functions and have other new properties. Performance of reflective heat-insulating paint: it can block, reflect, and radiate near-infrared heat from sunlight, so that the roof can be insulated and cooled, saving energy and loss. Inorganic paint performance: Made of natural inorganic materials, it has fire resistance, good air permeability, sterility and mildew resistance, long-lasting color retention, and is conducive to protecting the ecological environment. At present, ma...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Applications(China)
IPC IPC(8): C09D183/04C09D133/04C09D5/33C09D5/29C09D5/18C09D5/28
CPCC08K2003/2241C09D5/004C09D5/18C09D5/28C09D5/29C09D183/04C08L43/04C08K3/22
Inventor 汤紫俊周雪瞿伟罗建
Owner 四川嘉宝莉涂料有限公司
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com