Coke high-temperature performance detection device and detection method

A high-temperature performance and detection device technology, applied in the direction of measuring devices, fuel testing, material inspection products, etc., can solve problems such as excess

Pending Publication Date: 2021-10-26
SHOUGANG CORPORATION
View PDF0 Cites 1 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

The experimental gas CO specified in the national standard 2 The flow rate is 5L / min, which is obviously excessive, resulting in some coke reactivity CRI as low as 17%-18% in the actual measurement results, and other coke reactivity CRI even exceeding 40%

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Image

Smart Image Click on the blue labels to locate them in the text.
Viewing Examples
Smart Image
  • Coke high-temperature performance detection device and detection method
  • Coke high-temperature performance detection device and detection method
  • Coke high-temperature performance detection device and detection method

Examples

Experimental program
Comparison scheme
Effect test

Embodiment Construction

[0032] The present invention will be described in detail below in conjunction with specific embodiments and examples, and the advantages and various effects of the present invention will be presented more clearly. Those skilled in the art should understand that these specific implementations and examples are used to illustrate the present invention, not to limit the present invention.

[0033] Throughout the specification, unless otherwise specified, terms used herein should be understood as commonly used in the art. Therefore, unless otherwise defined, all technical and scientific terms used herein have the same meaning as commonly understood by one of ordinary skill in the art to which this invention belongs. In case of conflict, this specification shall take precedence.

[0034] Unless otherwise specified, various raw materials, reagents, instruments and equipment used in the present invention can be purchased from the market or prepared by existing methods.

[0035] The ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

PUM

PropertyMeasurementUnit
particle sizeaaaaaaaaaa
particle sizeaaaaaaaaaa
Login to view more

Abstract

The invention particularly relates to a coke high-temperature performance detection device and a detection method, and belongs to the technical field of coke thermal performance detection. Two cavities are arranged on a conventional coke reactivity testing device, and two reactions of ore reduction and coke solution loss can be completed at the same time. And the loading amount of the ore is obtained through calculation according to the actual load condition of the blast furnace. The reaction gas after ore reduction is directly introduced into the coke reaction tube to participate in the reaction, so that the reaction atmosphere of coke in the blast furnace can be more accurately simulated, and the obtained coke reaction performance index better conforms to the actual state in the blast furnace.

Description

technical field [0001] The invention belongs to the technical field of coke thermal performance detection, and in particular relates to a coke high-temperature performance detection device and detection method. Background technique [0002] Coke is an indispensable raw material in the process of blast furnace ironmaking. On the one hand, it acts as a reducing agent to provide the reducing gas CO required for ore reduction; on the other hand, it acts as a support for the tens of meters of blast furnace material column. Among coke evaluation indicators, reactivity CRI and post-reaction strength CSR have received extensive attention from ironworkers. Among them, CRI corresponds to the ability to provide CO reduction gas, and CSR corresponds to CO 2 After the reaction, it still has the ability to support the blast furnace material column. [0003] At present, the thermal properties of coke are measured in accordance with "GB / T 4000-2017 Coke Reactivity and Post-reaction Strengt...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to view more

Application Information

Patent Timeline
no application Login to view more
Patent Type & Authority Applications(China)
IPC IPC(8): G01N33/22G01N1/44
CPCG01N33/222G01N1/44
Inventor 马超闫立强李东涛孙健李玉清赵鹏徐荣广代鑫刘洋郭德英
Owner SHOUGANG CORPORATION
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Try Eureka
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap