High-oxygen-permeability corneal contact lens and preparation method thereof
A corneal contact lens and oxygen transmission rate technology, which are applied in the preparation of polysiloxane macromonomer cross-linking agent materials, the preparation of high oxygen transmission rate corneal contact lenses, and the surface hydrophilic modification of corneal contact lenses. , can solve the problems of low oxygen permeability, low water content of lenses, development and application limitations, etc., to achieve the effect of comfortable wearing and good wetting performance
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Example Embodiment
[0036] Example 1
[0037] This example discloses a hydrophilic segment modification, a double-bonded polydimethylsiloxane large monomer crosslinking agent, which includes the following steps:
[0038] 1. Add KF-6001 (7.5 g) into a 100 ml bump, insert mechanical stirring, cock coating vacuum, grouped with vacuum line, 55 ° C water bath, vacuum drying for 2 h.
[0039] 2. At the same time, KF-6002 (30g) is added to the single-mouth flask, the drying method is the same.
[0040]3300rpm under mechanical stirring, is added IPDI (1.67g), stirred at 55 ℃ until complete dissolution, with the injector suction micro 100ul of DBTDL (100ul) was added dropwise in the reactor (> 10min), the reaction 2h.
[0041] 4, using a syringe KF-6002 (24.8g) into the reactor, injector suction micro 100ul amount of DBTDL (100ul) was added dropwise in a reactor, reacted at 55 ℃ overnight.
[0042] 5, the pressure to atmospheric pressure balance 30min, weighing IEM (1.165g) by the amount of difference method,...
Example Embodiment
[0044] Example 2
[0045] In the present embodiment, on the basis of Example 1 discloses a method for preparing a silicone hydrogel material, comprising the steps of:
[0046] Amount of 41.7% in mass percentage in Example 1 polydimethylsiloxane macromer crosslinking agent, 22.6% by mass percentage of N'N- dimethylacrylamide (DMA), 15.9% of the mass percentage A yl acryloxy propyl tris (trimethylsiloxy) silane (Tris), 1.0% by mass percentage of Darocur 1173, was dissolved in n-propanol of 18.8% by mass percentage of diluent is magnetically stirred for 20 min, ultrasonic extinction soak for 10 minutes to the polymerization solution for use. With a pipette to draw the polymerization solution was added dropwise with 5ml 5 * 5 * 0.2cm groove Teflon mold, covered with a glass plate after dropwise over a 6 * 6 * 0.2cm on the mold, the whole is placed ultraviolet under light, a polymerization 40min. After the opened glass, good solid polymeric gel is washed off 10 ~ 20min with ethanol fro...
Example Embodiment
[0047] Example 3
[0048] In the present embodiment, on the basis of the embodiment 2 discloses a method for preparing a silicone hydrogel contact lens, comprising the steps of:
[0049] Amount of 41.7% in mass percentage in Example 1 polydimethylsiloxane macromer crosslinking agent, 22.6% by mass percentage of N'N- dimethylacrylamide (DMA), 15.9% of the mass percentage A yl acryloxy propyl tris (trimethylsiloxy) silane (Tris), 1.0% by mass percentage of Darocur 1173, was dissolved in n-propanol of 18.8% by mass percentage of diluent is magnetically stirred for 20 min, ultrasonic extinction soak for 10 minutes to the polymerization solution for use. 20μL suction pipette with the polymerization solution was added dropwise a polypropylene contact lens molds in a female mold, the male mold cover dropwise over in the mold, the whole is placed under UV light, polymerization 30min. After the reaction, the mold is opened, the lens is bonded to the surface of the mold, the mold was remove...
PUM
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap