Durable wear-resistant souvenir medal and preparation method thereof
A kind of commemorative medal, durable technology, applied in the field of medal, can solve the problems of wear and smoothing, damage to the medal, affecting the appearance, etc., to achieve the effect of strong wear resistance, high glass transition stability
- Summary
- Abstract
- Description
- Claims
- Application Information
AI Technical Summary
Problems solved by technology
Method used
Image
Examples
Embodiment 1
[0044] A durable and wear-resistant medal, comprising a medal body and a protective layer arranged on the surface of the medal body; the material of the medal body is metal; the material of the protective layer is modified polyetheretherketone, and the preparation method of the modified polyetheretherketone for:
[0045] S1. Weigh polyether ether ketone and mix it into dimethyl sulfoxide, raise the temperature to 115°C, stir until it is completely dissolved, then add sodium borohydride, stir again, keep stirring and react for 9 hours, after the reaction is completed and cooled to room temperature , filtered out the solid, washed three times with absolute ethanol and purified water successively, and dried under reduced pressure or vacuum to obtain hydroxylated polyether ether ketone; the mass ratio of polyether ether ketone, sodium borohydride and dimethyl sulfoxide is 1:0.18:30;
[0046] S2. Weigh 4-sulfonic acid pyrimidine-2-carboxylic acid and add it to deionized water, mix...
Embodiment 2
[0053] A durable and wear-resistant medal, comprising a medal body and a protective layer arranged on the surface of the medal body; the material of the medal body is metal; the material of the protective layer is modified polyetheretherketone, and the preparation method of the modified polyetheretherketone for:
[0054] S1. Weigh polyether ether ketone and mix it into dimethyl sulfoxide, raise the temperature to 110°C, stir until it is completely dissolved, then add potassium borohydride, stir again, keep stirring and react for 8 hours, after the reaction is completed and cooled to room temperature , filtered out the solid, washed three times with absolute ethanol and purified water successively, and dried under reduced pressure or vacuum to obtain hydroxylated polyether ether ketone; the mass ratio of polyetheretherketone, potassium borohydride and dimethyl sulfoxide is 1:0.15:20;
[0055] S2. Weigh 4-sulfonic acid pyrimidine-2-carboxylic acid and add it to deionized water,...
Embodiment 3
[0062] A durable and wear-resistant medal, comprising a medal body and a protective layer arranged on the surface of the medal body; the material of the medal body is metal; the material of the protective layer is modified polyetheretherketone, and the preparation method of the modified polyetheretherketone for:
[0063] S1. Weigh polyether ether ketone and mix it into dimethyl sulfoxide, raise the temperature to 120°C, stir until it is completely dissolved, then add sodium borohydride, stir again, keep stirring and react for 10 hours, after the reaction is completed and cooled to room temperature , filtered out the solid, washed three times with absolute ethanol and purified water successively, and dried under reduced pressure or vacuum to obtain hydroxylated polyether ether ketone; the mass ratio of polyether ether ketone, sodium borohydride and dimethyl sulfoxide is 1:0.2:40;
[0064] S2. Weigh 4-sulfonic acid pyrimidine-2-carboxylic acid and add it to deionized water, mix...
PUM
Property | Measurement | Unit |
---|---|---|
thickness | aaaaa | aaaaa |
Abstract
Description
Claims
Application Information
- R&D Engineer
- R&D Manager
- IP Professional
- Industry Leading Data Capabilities
- Powerful AI technology
- Patent DNA Extraction
Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic.
© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap