ZSM-5 structure zeolite, preparation and use thereof

A technology of ZSM-5 and zeolite, which is applied in the field of ZSM-5 structure zeolite, can solve problems such as difficulty in filtration/separation, difficulty in industrial production and application, etc., so as to solve difficulty in filtration, solve difficulty in separation of catalyst and liquid phase, and achieve good conversion rate effect

Inactive Publication Date: 2006-05-31
CHINA PETROLEUM & CHEM CORP +1
View PDF5 Cites 20 Cited by
  • Summary
  • Abstract
  • Description
  • Claims
  • Application Information

AI Technical Summary

Problems solved by technology

However, in actual operation, no matter in the synthesis process or in the separation of cyclohexene hydration reaction, the fine-grained zeolite is difficult to filter / separate due to the fine grain of zeolite, which is an increase for industrial production and application. Difficulty

Method used

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
View more

Examples

Experimental program
Comparison scheme
Effect test

Embodiment 1

[0021] This example illustrates the preparation of the zeolites provided by the invention.

[0022] Get 50 grams of commercially available ZSM-5 zeolite (commercial brand is ZRP-5, SiO 2 / Al 2 o 3 =60, primary particle diameter is 3μm, mesopore surface area is 8m 2 / g), put into 2 liters of concentration and be in the sodium hydroxide aqueous solution of 0.5 mole (record pH=11). Stir at a constant temperature of 80°C for 3 hours under reflux, filter, rinse with 100 ml of deionized water, exchange with 500 ml of 1 molar ammonium nitrate solution at a constant temperature of 90°C for 1 hour, filter, repeat the ammonium exchange once, filter, and The filter cake was dried at 110°C for 5 hours and calcined at 500°C for 3 hours.

[0023] The resulting zeolite product is designated as T1. Its SiO 2 / Al 2 o 3 = 41, the primary particle diameter measured by the electron microscope is 2.7 μm, and the mesopore surface area measured by the BET low-temperature nitrogen adsorption ...

Embodiment 2

[0032] This example illustrates the preparation of the zeolites provided by the invention.

[0033] Get 40 grams of commercially available ZSM-5 zeolite (commercial brand is ZRP-5, SiO 2 / Al 2 o 3 =60, primary particle diameter is 3μm, mesopore surface area is 8m 2 / g), put into 2 liters of concentration and be 0.5 mole sodium hydroxide aqueous solution (recording PH=11), under reflux at 85 ℃ of constant temperature stirring 2 hours, filter, rinse with 100 milliliters of deionized water, then use 500 ml of 1 molar ammonium nitrate solution was exchanged at 90°C for 1 hour at a constant temperature, filtered, repeated ammonium exchange once, filtered, and the filter cake was dried at 110°C for 5 hours and then roasted at 500°C for 3 hours.

[0034] The resulting zeolite product is designated as T2. Its SiO 2 / Al 2 o 3 =37, the primary particle diameter measured by the electron microscope is 2.5 μm, and the mesopore surface area measured by the BET low-temperature nitroge...

Embodiment 3

[0036] This example illustrates the preparation of the zeolites provided by the invention.

[0037] Get 20 grams of commercially available ZSM-5 zeolite (commercial brand is ZRP-5, SiO 2 / Al 2 o 3 =60, primary particle diameter is 3μm, mesopore surface area is 8m 2 / g), put into 3 liters of concentration and be 0.8 moles of sodium hydroxide aqueous solution (record pH=11.8), under reflux at 80 ℃ of constant temperature and stir for 1.5 hours, filter, rinse with 100 milliliters of deionized water, then use 500 ml of 1 molar ammonium nitrate solution was exchanged at 90°C for 1 hour at a constant temperature, filtered, repeated ammonium exchange once, filtered, and the filter cake was dried at 110°C for 5 hours and then roasted at 500°C for 3 hours.

[0038] The resulting zeolite product is designated as T3. Its SiO2 / Al 2 o 3 =30, the primary particle diameter measured by the electron microscope is 2.1 μm, and the mesopore surface area measured by the BET low-temperature ...

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

PUM

PropertyMeasurementUnit
diameteraaaaaaaaaa
diameteraaaaaaaaaa
diameteraaaaaaaaaa
Login to View More

Abstract

A ZSM-5 structured zeolite, the molar ratio of silicon oxide to aluminum oxide is 15-200, the primary particle diameter is 0.5-10 μm, and the mesopore surface area with a pore diameter of 2-50 nm measured by BET low-temperature nitrogen adsorption method is 25- 250m 2 / g. The zeolite is prepared from conventionally produced zeolite with larger crystal grains as raw material, treated with alkaline aqueous solution, ammonium ion exchange, dried and roasted. When the zeolite is used as a catalyst for the hydration of cyclohexene to prepare cyclohexanol, a good conversion rate of cyclohexene can be obtained, and it solves the difficulty in separating the catalyst from the liquid phase after the hydration reaction in the prior art and the fine crystal grains during the zeolite synthesis. resulting in difficult filtering problems.

Description

technical field [0001] The invention relates to a ZSM-5 structure zeolite, its preparation and application. More specifically, the present invention relates to a ZSM-5 zeolite with a specific physicochemical structure, its preparation method, and its application in the reaction of cyclohexene hydration to prepare cyclohexanol. Background technique [0002] Cyclohexanol is an important chemical product and chemical raw material, which is currently produced by the hydration method of cyclohexene. The catalyst used in it was an inorganic acid such as sulfuric acid in the early stage, but the product and the catalyst were mixed together and it was difficult to separate and recover; there were a large number of side reactions in the reaction, which made it difficult to purify the product; once the catalyst was deactivated, it was difficult to regenerate. For this reason, it is proposed to use solid catalysts, such as ion exchange resins. However, ion exchange resins have poor m...

Claims

the structure of the environmentally friendly knitted fabric provided by the present invention; figure 2 Flow chart of the yarn wrapping machine for environmentally friendly knitted fabrics and storage devices; image 3 Is the parameter map of the yarn covering machine
Login to View More

Application Information

Patent Timeline
no application Login to View More
Patent Type & Authority Patents(China)
IPC IPC(8): C01B39/38B01J29/40
Inventor 王殿中舒兴田何鸣元
Owner CHINA PETROLEUM & CHEM CORP
Who we serve
  • R&D Engineer
  • R&D Manager
  • IP Professional
Why Eureka
  • Industry Leading Data Capabilities
  • Powerful AI technology
  • Patent DNA Extraction
Social media
Eureka Blog
Learn More
PatSnap group products

Browse by: Latest US Patents, China's latest patents, Technical Efficacy Thesaurus, Application Domain, Technology Topic, Popular Technical Reports.

© 2024 PatSnap. All rights reserved.Legal|Privacy policy|Modern Slavery Act Transparency Statement|Sitemap|About US| Contact US: help@patsnap.com